Composite foam-textile cleaning pad

Claim 2

A process for preparing a composite cleaning pad incorporating opposed foam and textile surfaces comprising: (a) forming an aqueous reactant phase comprising about 45-75% by weight of solid abrasive particles, about 0.1-5% of the weight of the abrasive particles of a silane coupling agent, about 1-10% of a nonionic surfactant, about 1-10% of a gelling agent, and about 15-35% water; (b) mixing and foaming said aqueous reactant phase with a water-foamable prepolymer resin which contains about 1.3-1.5 mEg of free isocyanate groups per gram of resin so that the final mole ratio of water to total free isocyanate groups is within the range of about 20-80:1; and (c) curing said foaming mixture in contact with a highly reticulated textile sheet to provide a hydrophillic, oil and water absorbent foam sheet, one surface of which is integrally bonded to said textile sheet.

Claim 3

The process of claim 1 wherein said foam sheet has a density of about 0.2-0.4 g/cc and a breaking strength of about 300-400 g.

Claim 4

The process of claim 1 wherein the aqueous reactant phase further comprises about 2-10% of a silicone fluid.

Claim 5

The process of claim 1 wherein the aqueous phase further comprises about 0.5-5% of an anionic surfactant.

Claim 6

The process of claim 1 wherein said aqueous reactant phase is formed by slurrying the solid abrasive particles with about 50-70% of the total water, adding the silane coupling agent, stirring and heating the water phase to about 21°-32° C. and adding the remainder of the water, the surfactants, and the gelling agent.

Claim 7

The process of claim 5 wherein the solid particles comprise silaceous mineral particles and said silane coupling agent is an aminoalkyl(tris-alkoxy)silane.

Claim 8

A process for preparing a composite cleaning pad incorporating opposed foam and textile surfaces comprising: (a) forming a slurry comprising water and about 300-400% weight excess of solid abrasive particles; (b) treating said slurry with an amount of a silane coupling agent equal to about 0.1-5% by weight of the amount of abrasive particles; (c) adding to said slurry an amount of water-comprising an anionic surfactant, a nonionic surfactant comprising a poly(lower)alkylenoxy moiety, and an inorganic gelling agent to form an aqueous reactant phase comprising about 45-75% abrasive solids and about 1-10% gelling agent; (d) mixing and foaming said aqueous reactant phase with a water-foamable, self cross-linking prepolymer resin in a weight ratio of aqueous phase to prepolymer of about 4-2:1, said prepolymer resin comprising a polyisocyanate-capped polyalkylenoxy polyol, said polyol having a molecular weight of about 900-1100 and said resin comprising about 1.3-1.5 mEq/g of free isocyanate groups; and (e) curing said foaming mixture in contact with a textile sheet to provide an oil and water absorbent, open-celled, highly reticulated foam sheet, one surface of which is integrally bonded to said textile sheet.

Claim 9

A process for preparing a composite cleaning pad incorporating opposed foam and textile surfaces comprising: (a) forming a slurry comprising water and about 300-400% weight excess of solid abrasive particles; (b) treating said slurry with an amount of a silane coupling agent equal to about 0.1-5% by weight of the amount of abrasive particles; (c) adding to said slurry an amount of water-comprising an anionic surfactant, a nonionic surfactant comprising a poly(lower)alkylenoxy moiety, and an inorganic gelling agent to form an aqueous reactant phase comprising about 45-75% abrasive solids and about 1-10% gelling agent; (d) mixing and foaming said aqueous reactant phase with a water-foamable, self cross-linking prepolymer resin in a weight ratio of aqueous phase to prepolymer of about 4-2:1, said prepolymer resin comprising a polyisocyanate-capped polyalkylenoxy polyol, said polyol having a molecular weight of about 900-1100 and said resin comprising about 1.3-1.5 mEq/g of free isocyanate groups; and (e) curing said foaming mixture in contact with a textile sheet to provide an oil and water absorbent, open-celled, highly reticulated foam sheet, one surface of which is integrally bonded to said textile sheet.

Claim 10

The process of claim 7 wherein step (c) further comprises treating the aqueous reactant phase with a silicone fluid.

Claim 11

The process of claim 8 wherein the aqueous reactant phase comprises about 4-8% nonionic surfactant, about 1.5-2.5% by weight of anionic surfactant, and about 2-10% of silicone fluid.

Claim 12

The process of claim 7 wherein the aqueous reactant phase is cooled to about 8°-15° C. and the resin is warmed to about 35°-45° C. prior to mixing.

Claim 13

The process of claim 7 wherein the inorganic gelling agent comprises a smectite clay, an inosilicate mineral or mixtures thereof.

Claim 14

The process of claim 7 wherein the foam sheet exhibits a density of about 0.25-0.35 g/cc and a breaking strength of about 300-400 g.

Claim 15

The process of claim 7 wherein the textile sheet comprises a nonwoven blend of about 70-80% polyester and about 20-30% rayon.