Method of making ferroboron and ferroborosilicon alloys and the alloys made by this method
Assignee: GfE Gesellschaft fuer Elektrometallurgie mbH
•
Filing: 1985-03-12
•
Granted: 1986-02-11
•
Expires: 2005-03-12
Abstract
Abstract A method of making ferroboron or ferroborosilicon alloys in a low-shaft electrical furnace wherein the burden or charge has at least as a major portion of its carbon carrier, wood chips or particles which are carbonized to wood charcoal during the process and thus the charge has a porosity which permits adsorption action to prevent loss of volatile boron compounds. The charge also contains iron oxide and boron oxide, the electrodes of the furnace effecting a reduction of the boron oxide at a reduction zone just above the floor of the furnace.
Inventors
- 👤 Rudolf Fichte
- 👤 Friedrich Breuer
- 👤 Reinhard Hahn
- 👤 Hans-Joachim Retelsdorf
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 02:11
CPC Classifications
C; C22; C22C; C22C33/00; C22C33/003; C22C35/00; C22C35/005
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
193 words
A method of producing an iron and boron-containing alloy which comprises the steps of: (a) maintaining a porous charge consisting essentially of reducible alloying components including oxidic boron compounds and iron oxide, and a carbon carrier consisting at least in major part of wood and wood charcoal above a reduction zone of a low-shaft electrical furnace, said molten alloy collecting on a floor of said furnace; (b) electrically heating said reduction zone by passing an electric current between a plurality of electrodes extending into said reduction zone just above the floor of said furnace to effect a reduction reaction therein, thereby forming said alloy and producing carbon monoxide to reduce iron oxide at an upper portion of said charge; and (c) maintaining the thickness of said charge in said furnace during the formation of the alloy and dry carbonizing said pieces of wood in said charge to wood charcoal, said pieces of wood representing 35 to 65% of the total carbon carrier and being of a particle size of substantially 5 to 250 mm; said dry carbonization and said reductions of oxidic boron and iron oxide all being conducted within said electrical furnace.
Claim 2
Independent Claim
193 words
A method of producing an iron and boron-containing alloy which comprises the steps of: (a) maintaining a porous charge consisting essentially of reducible alloying components including oxidic boron compounds and iron oxide, and a carbon carrier consisting at least in major part of wood and wood charcoal above a reduction zone of a low-shaft electrical furnace, said molten alloy collecting on a floor of said furnace; (b) electrically heating said reduction zone by passing an electric current between a plurality of electrodes extending into said reduction zone just above the floor of said furnace to effect a reduction reaction therein, thereby forming said alloy and producing carbon monoxide to reduce iron oxide at an upper portion of said charge; and (c) maintaining the thickness of said charge in said furnace during the formation of the alloy and dry carbonizing said pieces of wood in said charge to wood charcoal, said pieces of wood representing 35 to 65% of the total carbon carrier and being of a particle size of substantially 5 to 250 mm; said dry carbonization and said reductions of oxidic boron and iron oxide all being conducted within said electrical furnace.
Claim 3
Dependent Claim
14 words
The method defined in claim 1 wherein said thickness is at least 500 mm.
Claim 4
Dependent Claim
28 words
The method defined in claim 2 wherein said thickness is substantially 800 to 1200 mm for a furnace with an energy consumption of 500 kVA to 1500 kVA.
Claim 5
Dependent Claim
13 words
The method defined in claim 3 wherein said thickness is about 1000 mm.
Claim 6
Dependent Claim
25 words
The method defined in claim 1 wherein said wood charcoal is in the form of grains having a particle size of at most 3 mm.
Claim 7
Dependent Claim
16 words
The method defined in claim 1 wherein said charge consists of agglomerates of the components thereof.
Claim 8
Dependent Claim
25 words
A ferroboron alloy made by the method of claim 1, containing less than 0.2% by weight aluminum and suitable for the production of metallic glasses.
Claim 9
Dependent Claim
44 words
The alloy defined in claim 7 which has a boron content of 15 to 25% by weight, the balance iron and a total of not more than 0.2% by weight of impurities selected from the Group II of the Periodic Table or mixtures thereof.
Claim 10
Dependent Claim
15 words
The alloy defined in claim 8 having a boron content of about 19% by weight.
Claim 11
Dependent Claim
19 words
The alloy defined in claim 7 in the form of a ferroborosilicon alloy for the production of metallic glasses.
Claim 12
Dependent Claim
41 words
The ferroborosilicon alloy of claim 10 which consists of 3 to 15% by weight boron, 40 to 10% by weight silicon and the balance iron with not more than 0.2% by weight of impurities of Group II of the Periodic Table.
Claim 13
Dependent Claim
25 words
The ferroborosilicon alloy defined in claim 11 having a boron content of about 10% by weight and a silicon content of about 24% by weight.
References Cited (Backward Citations)
US4486226A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-02-10 | 1989-08-12 | 1990-02-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-02-10 | 1993-08-12 | 1994-02-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-02-10 | 1997-08-12 | 1998-02-11 | $7700.00 | Window Closed / Lapsed |