Method of sealing open ends of ceramic honeycomb structural body
Assignee: NGK Insulators Ltd
•
Filing: 1983-04-06
•
Granted: 1986-02-04
•
Expires: 2003-04-06
Abstract
Abstract The disclosed method seals preselected open ends of channels of a ceramic honeycomb structural body with cordierite-forming sealing material batch, and fires the honeycomb structural body with the thus sealed ends, so as to convert the sealing material batch into cordierite.
Inventors
- 👤 Yutaka Ogawa
- 👤 Shunichi Yamada
- 👤 Toshiyuki Hamanaka
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 14:15
CPC Classifications
F; F01; F01N; F01N3/00; F01N3/08; F01N3/10; F01N3/24; F01N3/28; F01N3/2803; F01N3/2825; F01N3/2828; C; C03; C03B; C03B23/00; C03B23/20; C04; C04B; C04B35/00; C04B35/01; C04B35/16; C04B35/18; C04B35/195; C04B38/00; C04B38/0006; F01N3/02; F01N3/021; F01N3/022; F01N3/0222; B; B01; B01J; B01J35/00; B01J35/50; B01J35/56; F01N2330/00; F01N2330/06; Y; Y02; Y02T; Y02T10/00; Y02T10/10; Y02T10/12
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
190 words
A method of sealing open ends of channels of a ceramic honeycomb structural body, comprising the steps of applying a cordierite-forming sealing material batch to selected open ends of channels of a ceramic honeycomb structural body, ingredients of said sealing material batch containing a combination of materials selected from the group of combinations consisting of a combination of 10-16% by weight of α-alumina, 10-38.2% by weight of calcined talc and 80-45.8% by weight of oxides which form cordierite, a combination of 15-30.2% by weight of α-alumina, 5.5-18.1% by weight of quartz and 79.5-51.7% by weight of oxides which form cordierite, and a combination of 15% by weight of α-alumina, 10% by weight of amorphous silica and 75% by weight of oxides which form cordierite, and firing the ceramic honeycomb structural body with the sealing material batch thus applied thereto at a temperature not lower than 1,300° C. so as to convert the cordierite-forming sealing material batch into cordierite having a coefficient of thermal expansion of less than 2.0×10 -6 /°C. through a temperature range of room temperature to 800° C., said sealing material not shrinking, or actually expanding upon firing.
Claim 2
Independent Claim
190 words
A method of sealing open ends of channels of a ceramic honeycomb structural body, comprising the steps of applying a cordierite-forming sealing material batch to selected open ends of channels of a ceramic honeycomb structural body, ingredients of said sealing material batch containing a combination of materials selected from the group of combinations consisting of a combination of 10-16% by weight of α-alumina, 10-38.2% by weight of calcined talc and 80-45.8% by weight of oxides which form cordierite, a combination of 15-30.2% by weight of α-alumina, 5.5-18.1% by weight of quartz and 79.5-51.7% by weight of oxides which form cordierite, and a combination of 15% by weight of α-alumina, 10% by weight of amorphous silica and 75% by weight of oxides which form cordierite, and firing the ceramic honeycomb structural body with the sealing material batch thus applied thereto at a temperature not lower than 1,300° C. so as to convert the cordierite-forming sealing material batch into cordierite having a coefficient of thermal expansion of less than 2.0×10 -6 /°C. through a temperature range of room temperature to 800° C., said sealing material not shrinking, or actually expanding upon firing.
Claim 3
Independent Claim
124 words
A method of sealing open ends of channels of a ceramic honeycomb structural body, comprising the steps of applying a cordierite-forming sealing material batch to selected open ends of channels of a ceramic honeycomb structural body, ingredients of said sealing material batch consisting of 7-20% by weight of mullite and 93-80% by weight of oxides which form cordierite, and firing the ceramic honeycomb structural body with the sealing material batch thus applied thereto at a temperature not lower than 1,300° C. so as to convert the cordierite-forming sealing material batch into cordierite having a coefficient of thermal expansion of less than 2.0×10 -6 /°C. through a temperature range of room temperature to 800° C., said sealing material not shrinking, or actually expanding upon firing.
Claim 4
Independent Claim
124 words
A method of sealing open ends of channels of a ceramic honeycomb structural body, comprising the steps of applying a cordierite-forming sealing material batch to selected open ends of channels of a ceramic honeycomb structural body, ingredients of said sealing material batch consisting of 7-20% by weight of mullite and 93-80% by weight of oxides which form cordierite, and firing the ceramic honeycomb structural body with the sealing material batch thus applied thereto at a temperature not lower than 1,300° C. so as to convert the cordierite-forming sealing material batch into cordierite having a coefficient of thermal expansion of less than 2.0×10 -6 /°C. through a temperature range of room temperature to 800° C., said sealing material not shrinking, or actually expanding upon firing.
Claim 5
Dependent Claim
50 words
The method of claim 1, wherein some of the channels of the ceramic honeycomb structural body are sealed at one end of the honeycomb structural body, while the remainder of the channels of the ceramic honeycomb structural body are sealed at the opposite end of the ceramic honeycomb structural body.
Claim 6
Dependent Claim
37 words
The method of claim 1, wherein a plurality of the channels of the ceramic honeycomb structural body located near an outer peripheral portion thereof are sealed adjacent at least one end of the ceramic honeycomb structural body.
Claim 7
Dependent Claim
15 words
The method of claim 1, wherein said ceramic honeycomb structural body is made of cordierite.
Claim 8
Dependent Claim
15 words
The method of claim 3, wherein said ceramic honeycomb structural body is made of cordierite.
Claim 9
Dependent Claim
15 words
The method of claim 4, wherein said ceramic honeycomb structural body is made of cordierite.
Claim 10
Dependent Claim
48 words
The method of claim 2, wherein a crystal phase of said sealing material batch, after being converted into cordierite, consists essentially of cordierite and contains less than 30% by weight of crystals of at least one compound selected from the group consisting of spinel, sapphirine, mullite, and corundum.
Claim 11
Dependent Claim
48 words
The method of claim 3, wherein a crystal phase of said sealing material batch, after being converted into cordierite, consists essentially of cordierite and contains less than 30% by weight of crystals of at least one compound selected from the group consisting of spinel, sapphirine, mullite, and corundum.
Claim 12
Dependent Claim
48 words
The method of claim 4, wherein a crystal phase of said sealing material batch, after being converted into cordierite, consists essentially of cordierite and contains less than 30% by weight of crystals of at least one compound selected from the group consisting of spinel, sapphirine, mullite, and corundum.
Claim 13
Independent Claim
215 words
A method of sealing open ends of channels of a ceramic honeycomb structural body, comprising the steps of applying a cordierite-forming sealing material batch to selected open ends of channels of a ceramic honeycomb structural body, ingredients of said sealing material batch containing a combination of materials selected from the group of combinations consisting of a combination of 10-16% by weight of α-alumina, 10-38.2% by weight of calcined talc and 80-45.8% by weight of oxides which form cordierite, a combination of 15-30.2% by weight of α-alumina, 5.5-18.1% by weight of quartz and 79.5-51.7% by weight of oxides which form cordierite, and a combination of 15% by weight of α-alumina, 10% by weight of amorphous silica and 75% by weight of oxides which form cordierite, and firing the ceramic honeycomb structural body with the sealing material batch thus applied thereto at a temperature not lower than 1,300° C. so as to convert the cordierite-forming sealing material batch into cordierite having a coefficient of thermal expansion of less than 2.0×10 -6 /°C. through a temperature range of room temperature to 800° C. and containing less than 30% by weight of crystals of at least one compound selected from the group consisting of spinel, sapphirine, mullite and corundum, said sealing material not shrinking, or actually expanding upon firing.
Claim 14
Independent Claim
215 words
A method of sealing open ends of channels of a ceramic honeycomb structural body, comprising the steps of applying a cordierite-forming sealing material batch to selected open ends of channels of a ceramic honeycomb structural body, ingredients of said sealing material batch containing a combination of materials selected from the group of combinations consisting of a combination of 10-16% by weight of α-alumina, 10-38.2% by weight of calcined talc and 80-45.8% by weight of oxides which form cordierite, a combination of 15-30.2% by weight of α-alumina, 5.5-18.1% by weight of quartz and 79.5-51.7% by weight of oxides which form cordierite, and a combination of 15% by weight of α-alumina, 10% by weight of amorphous silica and 75% by weight of oxides which form cordierite, and firing the ceramic honeycomb structural body with the sealing material batch thus applied thereto at a temperature not lower than 1,300° C. so as to convert the cordierite-forming sealing material batch into cordierite having a coefficient of thermal expansion of less than 2.0×10 -6 /°C. through a temperature range of room temperature to 800° C. and containing less than 30% by weight of crystals of at least one compound selected from the group consisting of spinel, sapphirine, mullite and corundum, said sealing material not shrinking, or actually expanding upon firing.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-02-03 | 1989-08-05 | 1990-02-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-02-03 | 1993-08-05 | 1994-02-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-02-03 | 1997-08-05 | 1998-02-04 | $7700.00 | Window Closed / Lapsed |