Abstract A method and system for continuously or semicontinuously casting a composite metal article, such as a structurally composite ingot or the like, wherein one of the principal structural components of the ingot comprises an aluminum-lithium alloy. During such casting by a D.C. (direct chill) conventional tubular mold or electromagnetic process, the aluminum-lithium structural component of a structurally composite ingot is encircled or peripherally encased by a further outer metal cladding component that can be cast simultaneously with the aluminum-lithium component such as another outer aluminous alloy from which lithium is absent as a constituent or impurity, although it may be present and tolerated as a trace element. In this arrangement the aluminum-lithium structural component is prevented during casting from coming into direct contact with the chilling coolant, normally water, with which lithium can react violently. Only the outer aluminous alloy envelope is subjected to the direct contact of a liquid coolant whereby as it solidifies, this outer envelope or peripheral sheath acts as an impervious secondary mold for and protects the inner aluminum-lithium alloy structural component which is then directly controllably chilled and solidified.
Inventors
👤 George J. Binczewski
Bibliographic Details
Application Number—
JurisdictionUS
Data Sourcegoogle_patents
Last Synchronized2026-11-10 02:22
CPC Classifications
B; B22; B22D; B22D11/00; B22D11/007
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
124 words
A method of protecting a lithium-containing aluminum alloy from oxidation and other undesirable reactions during casting and subsequent fabrication and processing operations, said method comprising: (a) forming, in a mold in a continuous or semi-continuous casting apparatus, a hollow, tubular casing of an aluminum alloy containing no more than trace amounts of lithium; (b) solidifying the aluminum alloy in the casing; (c) casting into the interior of the casing a core of molten aluminum-lithium alloy containing more than about 0.25% lithium so that the molten aluminum-lithium alloy contacts the casing only after the metal forming the casing has completely soldified; (d) solidifying the aluminum-lithium alloy core within the casing; and (e) continuously or semi-continuously withdrawing the composite core and casing from the casting apparatus.
Claim 2
Independent Claim
124 words
A method of protecting a lithium-containing aluminum alloy from oxidation and other undesirable reactions during casting and subsequent fabrication and processing operations, said method comprising: (a) forming, in a mold in a continuous or semi-continuous casting apparatus, a hollow, tubular casing of an aluminum alloy containing no more than trace amounts of lithium; (b) solidifying the aluminum alloy in the casing; (c) casting into the interior of the casing a core of molten aluminum-lithium alloy containing more than about 0.25% lithium so that the molten aluminum-lithium alloy contacts the casing only after the metal forming the casing has completely soldified; (d) solidifying the aluminum-lithium alloy core within the casing; and (e) continuously or semi-continuously withdrawing the composite core and casing from the casting apparatus.
Claim 3
Dependent Claim
31 words
A method according to claim 1 wherein the solidifying of step (b) is carried out by spraying coolant water on the exterior of the mold in which the casing is formed.
Claim 4
Dependent Claim
26 words
A method according to claim 1 wherein the solidifying of step (d) is carried out by spraying coolant water on the exterior of the solidified casing.
Claim 5
Dependent Claim
31 words
A method according to claim 3 wherein the solidifying of step (b) is carried out by spraying coolant water on the exterior of the mold in which the casing is formed.
Claim 6
Dependent Claim
53 words
A method according to claim 1 wherein the forming of step (a) and the casting of step (c) are controlled so that the difference between the molten metal level in the casing mold and the molten metal level of the aluminum-lithium alloy within the solidified casing is maintained at a constant, predetermined value.
Claim 7
Dependent Claim
22 words
Method according to claim 1 wherein the lithium-free aluminum casing alloy has a higher solidus temperature than the lithium-containing aluminum core alloy.