Process for producing a bubble pressure barrier

Claim 2

A process for producing a porous bubble pressure barrier of predetermined pore size by forming metal oxide within its pores, said bubble pressure barrier having at least one face free of any significant amount of said metal oxide, said bubble pressure barrier being useful in a molten carbonate fuel cell, which consists essentially of providing a porous sintered blank in the form of a plaque consisting essentially of a metal selected from the group consisting of nickel, copper, an alloy of nickel and copper, and an alloy of nickel and up to about 10 weight % chromium, said blank having a median pore size ranging from about 1 micron to about 10 microns, and a pore volume ranging from about 40% to about 75% by volume of the total volume of said blank, immersing said blank in an aqueous salt solution of a precursor for a metal oxide selected from the group consisting of aluminum oxide, titanium oxide, iron oxide, zinc oxide and cerium oxide, subjecting the aqueous salt solution to a vacuum sufficient to at least substantially evacuate the pores of said immersed blank and at least significantly fill said evacuated pores with said salt solution, retrieving the resulting filled blank, immersing said filled blank in an aqueous hydroxide solution, subjecting said aqueous hydroxide solution to a vacuum sufficient to drive it into contact with the salt solution within said pores of said blank effecting reaction therewith producing metal hydroxide, retrieving the resulting metal hydroxide-containing blank, removing the metal hydroxide from at least one face of said blank leaving no significant amount thereof, first firing the resulting metal hydroxide-containing blank to convert said metal hydroxide to metal oxide leaving no significant amount of said hydroxide therein at a temperature ranging from the temperature at which said hydroxide converts to the oxide to less than about 600° C., and second firing the resulting metal oxide-containing blank to remove any water which may be present therein at a temperature ranging from about 600° C. to about 700° C., said first and second firings being carried out at or about atmospheric pressure in a reducing atmosphere, said first and second firings having no significant deleterious effect on said bubble pressure barrier.

Claim 3

The process according to claim 1 wherein said metal oxide is aluminum oxide.

Claim 4

The process according to claim 1 wherein said aqueous hydroxide solution is aqueous ammonium hydroxide.

Claim 5

A process for producing an integrally bonded electrode composite useful as an electrode in a molten carbonate fuel cell which consists essentially of the following steps: (a) producing a porous bubble pressure barrier of predetermined pore size by forming metal oxide within its pores, said bubble pressure barrier having at least one face free of any significant amount of said metal oxide, which consists essentially of providing a porous sintered blank in the form of a plaque consisting essentially of a metal selected from the group consisting of nickel, copper, an alloy of nickel and copper, and an alloy of nickel and up to about 10 weight % chronium, said blank having a median pore size ranging from about 1 micron to about 10 microns, and a pore volume ranging from about 40% to about 75% by volume of the total volume of said blank, immersing said blank in an aqueous salt solution of a precursor for a metal oxide selected from the group consisting of aluminum oxide, titanium oxide, iron oxide, zinc oxide and cerium oxide, subjecting the aqueous salt solution to a vacuum sufficient to at least substantially evacuate the pores of said blank and at least significantly fill said evacuated pores with said salt solution, retrieving the resulting filled blank, immersing said filled blank in an aqueous hydroxide solution, subjecting said aqueous hydroxide solution to a vacuum sufficient to drive it into contact with the salt solution within said pores of said blank effecting reaction therewith producing metal hydroxide, retrieving the resulting metal hydroxide-containing blank, removing the metal hydroxide from at least one face of said blank leaving no significant amount thereof, first firing the resulting metal hydroxide-containing blank to convert said metal hydroxide to metal oxide leaving no significant amount of said hydroxide therein at a temperature ranging from the temperature at which said hydroxide converts to the oxide to less than about 600° C., and second firing the resulting metal oxide-containing blank to remove any water which may be present therein at a temperature ranging from about 600° C. to about 700° C., said first and second firings being carried out at or about atmospheric pressure in a reducing atmosphere, said first and second firings having no significant deleterious effect on said bubble pressure barrier; and (b) depositing a layer of an electrode-forming powder on said metal oxide-free-face of said bubble pressure barrier, said electrode-forming powder covering said face and being coextensive therewith, said electrode-forming powder being selected from the group consisting of nickel, copper, an alloy of nickel and copper, and an alloy of nickel and up to about 10 weight % chromium, firing the resulting composite structure in a reducing atmosphere at or about atmospheric pressure, said electrode-forming powder sintering to form an electrode and simultaneously sintering to said barrier forming an integral bond therewith producing said integrally bonded electrode composite, said barrier having a median pore size significantly smaller than the median pore size of said electrode, said firing to form said electrode composite not exceeding the melting point of said composite.

Claim 6

A process for producing an integrally bonded electrode composite useful as an electrode in a molten carbonate fuel cell which consists essentially of the following steps: (a) producing a porous bubble pressure barrier of predetermined pore size by forming metal oxide within its pores, said bubble pressure barrier having at least one face free of any significant amount of said metal oxide, which consists essentially of providing a porous sintered blank in the form of a plaque consisting essentially of a metal selected from the group consisting of nickel, copper, an alloy of nickel and copper, and an alloy of nickel and up to about 10 weight % chronium, said blank having a median pore size ranging from about 1 micron to about 10 microns, and a pore volume ranging from about 40% to about 75% by volume of the total volume of said blank, immersing said blank in an aqueous salt solution of a precursor for a metal oxide selected from the group consisting of aluminum oxide, titanium oxide, iron oxide, zinc oxide and cerium oxide, subjecting the aqueous salt solution to a vacuum sufficient to at least substantially evacuate the pores of said blank and at least significantly fill said evacuated pores with said salt solution, retrieving the resulting filled blank, immersing said filled blank in an aqueous hydroxide solution, subjecting said aqueous hydroxide solution to a vacuum sufficient to drive it into contact with the salt solution within said pores of said blank effecting reaction therewith producing metal hydroxide, retrieving the resulting metal hydroxide-containing blank, removing the metal hydroxide from at least one face of said blank leaving no significant amount thereof, first firing the resulting metal hydroxide-containing blank to convert said metal hydroxide to metal oxide leaving no significant amount of said hydroxide therein at a temperature ranging from the temperature at which said hydroxide converts to the oxide to less than about 600° C., and second firing the resulting metal oxide-containing blank to remove any water which may be present therein at a temperature ranging from about 600° C. to about 700° C., said first and second firings being carried out at or about atmospheric pressure in a reducing atmosphere, said first and second firings having no significant deleterious effect on said bubble pressure barrier; and (b) depositing a layer of an electrode-forming powder on said metal oxide-free-face of said bubble pressure barrier, said electrode-forming powder covering said face and being coextensive therewith, said electrode-forming powder being selected from the group consisting of nickel, copper, an alloy of nickel and copper, and an alloy of nickel and up to about 10 weight % chromium, firing the resulting composite structure in a reducing atmosphere at or about atmospheric pressure, said electrode-forming powder sintering to form an electrode and simultaneously sintering to said barrier forming an integral bond therewith producing said integrally bonded electrode composite, said barrier having a median pore size significantly smaller than the median pore size of said electrode, said firing to form said electrode composite not exceeding the melting point of said composite.

Claim 7

The process according to claim 4 wherein said electrode composite is an anode composite.

Claim 8

The process according to claim 4 wherein said electrode composite is a cathode composite selected from the group consisting of nickel, copper and an alloy of nickel and copper.

Claim 9

A process for producing an integrally bonded electrode composite useful as an electrode in a molten carbonate fuel cell which consists essentially of the following steps: (a) producing a porous bubble pressure barrier of predetermined pore size by forming metal oxide within its pores, said bubble pressure barrier having at least one face free of any significant amount of said metal oxide, which consists essentially of providing a porous sintered blank in the form of a plaque consisting essentially of a metal selected from the group consisting of nickel, copper, an alloy of nickel and copper, and an alloy of nickel and up to about 10 weight % chromium, said blank having a median pore size ranging from about 1 micron to about 10 microns, and a pore volume ranging from about 40% to about 75% by volume of the total volume of said blank, immersing said blank in an aqueous salt solution of a precursor for a metal oxide selected from the group consisting of aluminum oxide, titanium oxide, iron oxide, zinc oxide and cerium oxide, subjecting the aqueous salt solution to a vacuum sufficient to at least substantially evacuate the pores of said immersed blank and at least significantly fill said evacuated pores with said salt solution, retrieving the resulting filled blank, immersing said filled blank in an aqueous hydroxide solution, subjecting said aqueous hydroxide solution to a vacuum sufficient to drive it into contact with the salt solution within said pores of said blank effecting reaction therewith producing metal hydroxide, retrieving the resulting metal hydroxide-containing blank, removing the metal hydroxide from at least one face of said blank leaving no significant amount thereof, first firing the resulting metal hydroxide-containing blank to convert said metal hydroxide to metal oxide leaving no significant amount of said hydroxide therein at a temperature ranging from the temperature at which said hydroxide converts to the oxide to less than about 600° C., and second firing the resulting metal oxide-containing blank to remove any water which may be present therein at a temperature ranging from about 600° C. to about 700° C., said first and second firings being carried out at or about atmospheric pressure in a reducing atmosphere, said first and second firings having no significant deleterious effect on said bubble pressure barrier; and (b) providing a porous sintered electrode in the form of a plaque, said electrode being selected from the group consisting of nickel, copper, an alloy of nickel and copper, and an alloy of nickel and up to about 10 weight % chromium, contacting one face of said electrode coextensively with said metal oxide-free-face of said bubble pressure barrier forming a composite structure, firing the resulting composite structure in a reducing atmosphere at or about atmospheric pressure sintering said barrier to said electrode forming an integral bond therewith, said bubble pressure barrier having a median pore size significantly smaller than the median pore size of said electrode, said firing to form said electrode composite not exceeding the melting point of said composite.

Claim 10

A process for producing an integrally bonded electrode composite useful as an electrode in a molten carbonate fuel cell which consists essentially of the following steps: (a) producing a porous bubble pressure barrier of predetermined pore size by forming metal oxide within its pores, said bubble pressure barrier having at least one face free of any significant amount of said metal oxide, which consists essentially of providing a porous sintered blank in the form of a plaque consisting essentially of a metal selected from the group consisting of nickel, copper, an alloy of nickel and copper, and an alloy of nickel and up to about 10 weight % chromium, said blank having a median pore size ranging from about 1 micron to about 10 microns, and a pore volume ranging from about 40% to about 75% by volume of the total volume of said blank, immersing said blank in an aqueous salt solution of a precursor for a metal oxide selected from the group consisting of aluminum oxide, titanium oxide, iron oxide, zinc oxide and cerium oxide, subjecting the aqueous salt solution to a vacuum sufficient to at least substantially evacuate the pores of said immersed blank and at least significantly fill said evacuated pores with said salt solution, retrieving the resulting filled blank, immersing said filled blank in an aqueous hydroxide solution, subjecting said aqueous hydroxide solution to a vacuum sufficient to drive it into contact with the salt solution within said pores of said blank effecting reaction therewith producing metal hydroxide, retrieving the resulting metal hydroxide-containing blank, removing the metal hydroxide from at least one face of said blank leaving no significant amount thereof, first firing the resulting metal hydroxide-containing blank to convert said metal hydroxide to metal oxide leaving no significant amount of said hydroxide therein at a temperature ranging from the temperature at which said hydroxide converts to the oxide to less than about 600° C., and second firing the resulting metal oxide-containing blank to remove any water which may be present therein at a temperature ranging from about 600° C. to about 700° C., said first and second firings being carried out at or about atmospheric pressure in a reducing atmosphere, said first and second firings having no significant deleterious effect on said bubble pressure barrier; and (b) providing a porous sintered electrode in the form of a plaque, said electrode being selected from the group consisting of nickel, copper, an alloy of nickel and copper, and an alloy of nickel and up to about 10 weight % chromium, contacting one face of said electrode coextensively with said metal oxide-free-face of said bubble pressure barrier forming a composite structure, firing the resulting composite structure in a reducing atmosphere at or about atmospheric pressure sintering said barrier to said electrode forming an integral bond therewith, said bubble pressure barrier having a median pore size significantly smaller than the median pore size of said electrode, said firing to form said electrode composite not exceeding the melting point of said composite.

Claim 11

The process according to claim 7 wherein said electrode composite is an anode composite.

Claim 12

The process according to claim 7 wherein said electrode composite is a cathode composite selected from the group consisting of nickel, copper and an alloy of nickel and copper.