Method of making carbon/carbon composites
Assignee: VOUGHT Corp A CORP OF DE
•
Filing: 1980-08-29
•
Granted: 1986-01-28
•
Expires: 2000-08-29
Abstract
Abstract Disclosed is a method of making carbon/carbon composites by pyrolytic conversion of a carbonizable liquid in a pre-formed graphite body to form an amorphous carbon reinforcing matrix. Graphite fabric saturated with a carbonizable liquid is formed into the shape of the desired end product body and placed in a flexible bag. The bag is evacuated to compress the formed body and the bagged body subjected to external pressure and heated. When the carbonizable liquid is heated to the curing temperature, the external pressure is reduced, causing volatile materials in the liquid to expand and form an interconnected pore structure. The formed body is thereafter heated to a temperature in excess of the curing temperature to further remove volatile materials therefrom. The cured rigid body is then transferred to a pyrolyzing furnace and rapidly heated in an inert gaseous environment directly to about 1500° F. to pyrolyze the carbonizable material and form an amorphous carbon matrix.
Inventors
- 👤 Isaac E. Harder
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 22:49
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/71; C04B35/78; C04B35/80; C04B35/83
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
154 words
The method of making a carbon/carbon composite structure, comprising the steps of: (a) fabricating a pre-form body of the desired configuration from a graphite fabric impregnated with a carbonizable fluid comprising a phenolic resin; (b) enclosing the pre-form body in a flexible bag; (c) reducing the pressure within said flexible bag to a pressure less than atmospheric; (d) enclosing said flexible bag in an enclosed containers (e) forming a pressure within said enclosed container of about 45 psia; (f) venting said flexible bag to atmosphere; (g) heating said pre-form body to a first temperature at which said carbonizable fluid is liquid and begins to cure while maintaining said pressure within said enclosed container at about 45 psia; and (h) thereafter reducing the pressure within said enclosed container to a pressure of at least about 30 psia and heating said pre-form body to a second temperature greater than the curing temperature of said carbonizable fluid.
Claim 2
Independent Claim
154 words
The method of making a carbon/carbon composite structure, comprising the steps of: (a) fabricating a pre-form body of the desired configuration from a graphite fabric impregnated with a carbonizable fluid comprising a phenolic resin; (b) enclosing the pre-form body in a flexible bag; (c) reducing the pressure within said flexible bag to a pressure less than atmospheric; (d) enclosing said flexible bag in an enclosed containers (e) forming a pressure within said enclosed container of about 45 psia; (f) venting said flexible bag to atmosphere; (g) heating said pre-form body to a first temperature at which said carbonizable fluid is liquid and begins to cure while maintaining said pressure within said enclosed container at about 45 psia; and (h) thereafter reducing the pressure within said enclosed container to a pressure of at least about 30 psia and heating said pre-form body to a second temperature greater than the curing temperature of said carbonizable fluid.
Claim 3
Dependent Claim
23 words
The method set forth in claim 1 wherein said first temperature is about 150° F. and said second temperature is about 325° F.
Claim 4
Dependent Claim
24 words
The method set forth in claim 1 including the additional step of rapidly heating said body to a third temperature of about 1500° F.
Claim 5
Dependent Claim
26 words
The method set forth in claim 3 wherein said pre-form body is heated to said third temperature in an inert gaseous environment at substantially atmospheric pressure.
Claim 6
Dependent Claim
47 words
The method set forth in claim 3 including the additional step of immersing said body in a carbonizable fluid under pressure to impregnate the pores of said body with said carbonizable fluid and thereafter directly reheating said body impregnated with said carbonizable fluid to said second temperature.
Claim 7
Dependent Claim
28 words
The method set forth in claim 5 wherein said body is re-heated to said second temperature in an inert gas environment under a pressure of about 80 psig.
Claim 8
Dependent Claim
106 words
In the method of forming a carbon-reinforced composite structure wherein a porous carbon body containing carbonizable fluid, comprising a phenolic resin, is heated to pyrolyze said carbonizable fluid and form amorphous carbon, the improvement comprising the steps of: (a) heating said porous carbon body containing carbonizable fluid to the curing temperature of said carbonizable fluid in an inert environment under a first substantial pressure; (b) reducing said pressure to a second pressure still greater than atmospheric while said carbonizable fluid is still liquid; and (c) heating said porous body to a second temperature in excess of said curing temperature while maintaining said pressure greater than atmospheric.
Claim 9
Dependent Claim
106 words
In the method of forming a carbon-reinforced composite structure wherein a porous carbon body containing carbonizable fluid, comprising a phenolic resin, is heated to pyrolyze said carbonizable fluid and form amorphous carbon, the improvement comprising the steps of: (a) heating said porous carbon body containing carbonizable fluid to the curing temperature of said carbonizable fluid in an inert environment under a first substantial pressure; (b) reducing said pressure to a second pressure still greater than atmospheric while said carbonizable fluid is still liquid; and (c) heating said porous body to a second temperature in excess of said curing temperature while maintaining said pressure greater than atmospheric.
Claim 10
Dependent Claim
24 words
The improvement set forth in claim 7 wherein said first substantial pressure is about 45 psia and said second pressure is about 30 psia.
Claim 11
Dependent Claim
23 words
The improvement set forth in claim 7 wherein said curing temperature is about 150° F. and said second temperature is about 325° F.
Claim 12
Independent Claim
82 words
The method of forming a substantially interconnected pore structure in a body of amorphous carbon comprising the steps of: (a) heating a carbonizable precursor, comprising a phenolic resin, under a first substantial pressure to a first temperature approximating the curing reaction temperature of said carbonizable precursor; (b) reducing said pressure to a second pressure greater than atmospheric while said carbonizable precursor is still substantially liquid; and (c) heating said carbonizable precursor to a second temperature in excess of said curing reaction temperature.
Claim 13
Independent Claim
82 words
The method of forming a substantially interconnected pore structure in a body of amorphous carbon comprising the steps of: (a) heating a carbonizable precursor, comprising a phenolic resin, under a first substantial pressure to a first temperature approximating the curing reaction temperature of said carbonizable precursor; (b) reducing said pressure to a second pressure greater than atmospheric while said carbonizable precursor is still substantially liquid; and (c) heating said carbonizable precursor to a second temperature in excess of said curing reaction temperature.
Claim 14
Independent Claim
175 words
The method of making a carbon/carbon composite structure comprising the steps of: (a) fabricating a pre-form body of the desired configuration from a graphite fabric impregnated with a carbonizable fluid, the carbonizable fluid comprising an organic resin, derived from a low volatility hydrocarbon which passes, successively, through liquid, gelatinous, and solid states during heat curing; (b) enclosing the pre-form body in a flexible bag; (c) reducing the pressure within said flexible bag to a pressure less than atmospheric; (d) enclosing said flexible bag in an enclosed container; (e) forming a pressure within said enclosed container of about 45 psia; (f) venting said flexible bag to atmosphere; (g) heating said pre-form body to a first temperature at which said carbonizable fluid is liquid and begins to cure while maintaining said pressure within said enclosed container at about 45 psia; and (h) thereafter reducing the pressure within said enclosed container to a pressure of at least about 30 psia and heating said pre-form body to a second temperature greater than the curing temperature of said carbonizable fluid.
Claim 15
Independent Claim
175 words
The method of making a carbon/carbon composite structure comprising the steps of: (a) fabricating a pre-form body of the desired configuration from a graphite fabric impregnated with a carbonizable fluid, the carbonizable fluid comprising an organic resin, derived from a low volatility hydrocarbon which passes, successively, through liquid, gelatinous, and solid states during heat curing; (b) enclosing the pre-form body in a flexible bag; (c) reducing the pressure within said flexible bag to a pressure less than atmospheric; (d) enclosing said flexible bag in an enclosed container; (e) forming a pressure within said enclosed container of about 45 psia; (f) venting said flexible bag to atmosphere; (g) heating said pre-form body to a first temperature at which said carbonizable fluid is liquid and begins to cure while maintaining said pressure within said enclosed container at about 45 psia; and (h) thereafter reducing the pressure within said enclosed container to a pressure of at least about 30 psia and heating said pre-form body to a second temperature greater than the curing temperature of said carbonizable fluid.
Claim 16
Dependent Claim
15 words
The method set forth in claim 11 wherein said carbonizable fluid is a phenolic resin.
Claim 17
Dependent Claim
23 words
The method set forth in claim 11 wherein said first temperature is about 150° F. and said second temperature is about 325° F.
Claim 18
Dependent Claim
24 words
The method set forth in claim 11 including the additional step of rapidly heating said body to a third temperature of about 1500° F.
Claim 19
Dependent Claim
26 words
The method set forth in claim 14 wherein said pre-form body is heated to said third temperature in an inert gaseous environment at substantially atmospheric pressure.
Claim 20
Dependent Claim
47 words
The method set forth in claim 14 including the additional step of immersing said body in a carbonizable fluid under pressure to impregnate the pores of said body with said carbonizable fluid and thereafter directly reheating said body impregnated with said carbonizable fluid to said second temperature.
Claim 21
Dependent Claim
28 words
The method set forth in claim 16 wherein said body is re-heated to said second temperature in an inert gas environment under a pressure of about 80 psig.
Claim 22
Dependent Claim
127 words
In the method of forming a carbon-reinforced composite structure wherein a porous carbon body containing carbonizable fluid is heated to pyrolyze said carbonizable fluid and form amorphous carbon, the carbonizable fluid comprising an organic resin, derived from a low volatility hydrocarbon, which passes, successively, through liquid, gelatinous, and solid states during heat curing, the improvement comprising the steps of: (a) heating said porous carbon body containing carbonizable fluid to the curing temperature of said carbonizable fluid in an inert environment under a first substantial pressure; (b) reducing said pressure to a second pressure still greater than atmospheric while said carbonizable fluid is still liquid; and (c) heating said porous body to a seocnd temperature in excess of said curing temperature while maintaining said pressure greater than atmospheric.
Claim 23
Dependent Claim
127 words
In the method of forming a carbon-reinforced composite structure wherein a porous carbon body containing carbonizable fluid is heated to pyrolyze said carbonizable fluid and form amorphous carbon, the carbonizable fluid comprising an organic resin, derived from a low volatility hydrocarbon, which passes, successively, through liquid, gelatinous, and solid states during heat curing, the improvement comprising the steps of: (a) heating said porous carbon body containing carbonizable fluid to the curing temperature of said carbonizable fluid in an inert environment under a first substantial pressure; (b) reducing said pressure to a second pressure still greater than atmospheric while said carbonizable fluid is still liquid; and (c) heating said porous body to a seocnd temperature in excess of said curing temperature while maintaining said pressure greater than atmospheric.
Claim 24
Dependent Claim
24 words
The improvement set forth in claim 18 wherein said first substantial pressure is about 45 psia and said second pressure is about 30 psia.
Claim 25
Dependent Claim
23 words
The improvement set forth in claim 18 wherein said curing temperature is about 150° F. and said second temperature is about 325° F.
Claim 26
Independent Claim
100 words
The method of forming a substantially interconnected pore structure in a body of amorphous carbon comprising the steps of: (a) heating a carbonizable precursor, comprising an organic resin derived from a low volatility hydrocarbon, which passes, successively, through liquid, gelatinous, and solid states during heat curing, under a first substantial pressure to a first temperature approximating the curing reaction temperature of said carbonizable precursor; (b) reducing said pressure to a second pressure greater than atmospheric while said carbonizable precursor is still substantially liquid; and (c) heating said carbonizable precursor to a second temperature in excess of said curing reaction temperature.
Claim 27
Independent Claim
100 words
The method of forming a substantially interconnected pore structure in a body of amorphous carbon comprising the steps of: (a) heating a carbonizable precursor, comprising an organic resin derived from a low volatility hydrocarbon, which passes, successively, through liquid, gelatinous, and solid states during heat curing, under a first substantial pressure to a first temperature approximating the curing reaction temperature of said carbonizable precursor; (b) reducing said pressure to a second pressure greater than atmospheric while said carbonizable precursor is still substantially liquid; and (c) heating said carbonizable precursor to a second temperature in excess of said curing reaction temperature.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-01-27 | 1989-07-29 | 1990-01-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-01-27 | 1993-07-29 | 1994-01-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-01-27 | 1997-07-29 | 1998-01-28 | $7700.00 | Window Closed / Lapsed |