Polymerization and catalysts
Assignee: Phillips Petroleum Co
•
Filing: 1979-12-07
•
Granted: 1986-01-21
•
Expires: 1999-12-07
Abstract
Abstract Polymerization of olefins in the presence of a catalyst system comprising a titanium-containing component A associated with a chemically treated silica-containing composition and a dihydrocarbylmagnesium compound and a cocatalyst component B comprising metal hydride or organometal compound derived from an element of Groups IA-IIIA of the Periodic Table.
Inventors
- 👤 James N. Short
- 👤 Max P. McDaniel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 02:12
CPC Classifications
C; C08; C08F; C08F10/00
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
192 words
A catalyst useful for polymerization which comprises: (1) a solid complex titanium-containing catalyst A obtained by mixing; (a) a pretreated particulate silica-containing support containing at least 80 wt. % silica formed by reacting said support with at least one of a chlorinating compound, a lower alkanol, a silating compound, a carboxylic acid chloride and an organoboron compound under conditions such that at least a portion of the OH groups on the surface of the silica-containing support are reacted with the treating agent with; (b) an organomagnesium compound of the formula MgR 2 wherein R is a hydrocarbon radical having from 1 to 12, inclusive, carbon atoms and; (c) a halogenated tetravalent titanium compound of the formula TiX n (OR') 4-n in which X is a bromine, chlorine, or iodine, R' is a hydrocarbon radical selected from saturated aliphatic, saturated cycloaliphatic and aromatic groups containing from 1 to about 12, inclusive, carbon atoms, and n is an integer of 3 or 4 and; (2) a cocatalyst component B comprising a metallic hydride or organometal compound wherein said metal is selected from a metal of Groups IA, IIA and IIIA of the Periodic Table.
Claim 2
Dependent Claim
192 words
A catalyst useful for polymerization which comprises: (1) a solid complex titanium-containing catalyst A obtained by mixing; (a) a pretreated particulate silica-containing support containing at least 80 wt. % silica formed by reacting said support with at least one of a chlorinating compound, a lower alkanol, a silating compound, a carboxylic acid chloride and an organoboron compound under conditions such that at least a portion of the OH groups on the surface of the silica-containing support are reacted with the treating agent with; (b) an organomagnesium compound of the formula MgR 2 wherein R is a hydrocarbon radical having from 1 to 12, inclusive, carbon atoms and; (c) a halogenated tetravalent titanium compound of the formula TiX n (OR') 4-n in which X is a bromine, chlorine, or iodine, R' is a hydrocarbon radical selected from saturated aliphatic, saturated cycloaliphatic and aromatic groups containing from 1 to about 12, inclusive, carbon atoms, and n is an integer of 3 or 4 and; (2) a cocatalyst component B comprising a metallic hydride or organometal compound wherein said metal is selected from a metal of Groups IA, IIA and IIIA of the Periodic Table.
Claim 3
Dependent Claim
176 words
A catalyst according to claim 1 wherein; said chlorinating compound is selected from the group consisting of CCl 4 , COCl 2 , SOCl 2 , SO 2 Cl 2 and S 2 Cl 2 ; said alkanol is a lower 1-alkanol containing from 1 to about 5 carbon atoms; said silating compound is a chlorosilane which can be expressed as SiR 2 c Cl 4-c in which R 2 is phenyl or alkyl group of 1 to about 6 carbon atoms, and c is an integer of 1, 2, or 3; said carboxylic acid chloride can be expressed as ##STR2## in which each G is selected from chlorine, alkyl of 1 to about 3 carbon atoms, hydrogen, and phenyl, with at least one G being chlorine; said organoboron compound is a trihydrocarbyl boron compound having the formula B(R 3 ) 3 in which R 3 can be selected from among hydrogen, alkyl, aryl and cycloalkyl, at least one R 3 in each compound being a hydrocarbon radical containing from 1 to about 6 carbon atoms.
Claim 4
Dependent Claim
18 words
A catalyst according to claim 1 wherein (b) is dibutylmagnesium, (c) is titanium tetrachloride and (2) is triisobutylaluminum.
Claim 5
Dependent Claim
29 words
A catalyst according to claim 1 wherein said particulate silica-containing support in (a) is reacted with at least one of carbon tetrachloride, methanol, trimethyl chlorosilane, dichloroacetyl chloride and triethylborane.
Claim 6
Dependent Claim
35 words
A catalyst according to claim 1 wherein (a) is reacted with at least one of carbon tetrachloride, methanol, trimethyl chlorosilane, dichloroacetyl chloride and triethylborane; (b) is dibutylmagnesium, (c) is titanium tetrachloride and (2) is triisobutylaluminum.
Claim 7
Dependent Claim
36 words
A catalyst according to claim 1 wherein the mole ratio of (a) to (c) ranges from about 1:1 to about 1000:1 and the mole ratio of (c) to (b) ranges from about 0.1:1 to about 20:1.
Claim 8
Independent Claim
216 words
A method of producing a polymerization catalyst which comprises; (1) pretreating a particulate silica-containing support containing at least 80 wt. % silica by reacting same with at least one of a chlorinating compound, a lower alkanol, a silating compound, a carboxylic acid chloride and an organoboron compound under conditions such that at least a portion of the OH groups on the support are reacted with the treating agent and thereby provide an activating amount of treating agent into the support, (2) contacting the pretreated silica of (1) with an organomagnesium compound of the formula MgR 2 wherein R is a hydrocarbon radical having from 1 to about 12, inclusive, carbon atoms, (3) treating the product obtained in (2) with a halogenated tetravalent titanium compound of the formula TiX n (OR') 4-n in which X is bromine, chlorine, or iodine, R' is a hydrocarbon radical selected from saturated aliphatic, saturated cycloaliphatic and aromatic groups containing from 1 to about 12, inclusive, carbon atoms, and n is an integer of 3 or 4, (4) isolating and purifying the product obtained in (3), and (5) combining the purified product of (4) with a cocatalyst comprising a metallic hydride or organometal compound wherein said metal is selected from a metal of Groups IA, IIA and IIIA of the Periodic Table.
Claim 9
Independent Claim
216 words
A method of producing a polymerization catalyst which comprises; (1) pretreating a particulate silica-containing support containing at least 80 wt. % silica by reacting same with at least one of a chlorinating compound, a lower alkanol, a silating compound, a carboxylic acid chloride and an organoboron compound under conditions such that at least a portion of the OH groups on the support are reacted with the treating agent and thereby provide an activating amount of treating agent into the support, (2) contacting the pretreated silica of (1) with an organomagnesium compound of the formula MgR 2 wherein R is a hydrocarbon radical having from 1 to about 12, inclusive, carbon atoms, (3) treating the product obtained in (2) with a halogenated tetravalent titanium compound of the formula TiX n (OR') 4-n in which X is bromine, chlorine, or iodine, R' is a hydrocarbon radical selected from saturated aliphatic, saturated cycloaliphatic and aromatic groups containing from 1 to about 12, inclusive, carbon atoms, and n is an integer of 3 or 4, (4) isolating and purifying the product obtained in (3), and (5) combining the purified product of (4) with a cocatalyst comprising a metallic hydride or organometal compound wherein said metal is selected from a metal of Groups IA, IIA and IIIA of the Periodic Table.
Claim 10
Dependent Claim
21 words
A process according to claim 7 wherein the mole ratio of (3) to (2) ranges from about 0.1:1 to about 20:1.
Claim 11
Dependent Claim
25 words
A process according to claim 7 wherein the silica-containing support is slurried in a hydrocarbon and contacted under refluxing conditions with the chemical treating agent.
Claim 12
Dependent Claim
35 words
A process according to claim 7 wherein the final product obtained in step (3) is washed with an inert solvent to remove unreacted titanium compounds prior to combining with the cocatalyst component in step (5).
Claim 13
Dependent Claim
46 words
A catalyst according to claim 1 wherein the amount of treating agent selected from chlorinating compound, lower alkanol, silating compound, carboxylic acid chloride, and organoboron compound reacted with said silica-containing support in (a) ranges from about 0.1 to about 1.8 mmoles treating agent per gram silica.
Claim 14
Dependent Claim
29 words
A catalyst according to claim 11 wherein the amount of treating agent reacted with said support ranges from about 0.8 to about 1.7 mmoles treating agent per gram silica.
Claim 15
Dependent Claim
27 words
A process according to claim 7 wherein said silica-containing support in (1) is reacted with from about 0.1 to about 1.8 mmoles treating agent per gram silica.
Claim 16
Dependent Claim
30 words
A process according to claim 7 wherein said silica-containing support in (1) is reacted with the treating agent at a temperature ranging from about 100° C. to about 900° C.
Claim 17
Dependent Claim
25 words
A process according to claim 13 wherein said silica-containing support is reacted with from about 0.8 to about 1.7 mmoles treating agent per gram silica.
Claim 18
Dependent Claim
79 words
A solid polymerization catalyst component prepared by mixing; (a) a support obtained by reacting silica having surface hydroxyl groups with a chlorosilane which is reactive with said surface hydroxyl groups, with; (b) an organomagnesium compound of the formula MgR 2 wherein R is a hydrocarbon radical, and (c) a titanium compound of the formula TiX n (OR 1 ) 4-n wherein X is halogen, R 1 is a hydrocarbon radical, and n is an integer of 3 or 4.
Claim 19
Dependent Claim
79 words
A solid polymerization catalyst component prepared by mixing; (a) a support obtained by reacting silica having surface hydroxyl groups with a chlorosilane which is reactive with said surface hydroxyl groups, with; (b) an organomagnesium compound of the formula MgR 2 wherein R is a hydrocarbon radical, and (c) a titanium compound of the formula TiX n (OR 1 ) 4-n wherein X is halogen, R 1 is a hydrocarbon radical, and n is an integer of 3 or 4.
Claim 20
Dependent Claim
38 words
A catalyst according to claim 16 which additionally contains (d) a cocatalyst component comprising a metallic hydride or organometal compound wherein said metal is selected from a metal of Groups IA, IIA and IIIA of the Periodic Table.
Claim 21
Dependent Claim
52 words
A composition according to claim 16 which additionally contains (d) a cocatalyst component comprising an organoaluminum compound having the formula AIR' b Y 3-b in which R' is a hydrocarbon radical, Y is a monovalent radical selected from among the halogens and hydrogen, and b is an integer of 0 to 3.
Claim 22
Dependent Claim
24 words
A catalyst according to claim 18 wherein said chlorosilane in (a) is trimethylchlorosilane, (b) is dibutylmagnesium, (c) is titanium tetrachloride, and (d) is triisobutylaluminum.
References Cited (Backward Citations)
US2981725A
Cited
US3594330A
Cited
US3855324A
Cited
US3787384A
Cited
US3670043A
Cited
US3833515A
Cited
US3936431A
Cited
US3993588A
Cited
US4301029A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-01-20 | 1989-07-22 | 1990-01-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-01-20 | 1993-07-22 | 1994-01-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-01-20 | 1997-07-22 | 1998-01-21 | $7700.00 | Window Closed / Lapsed |