US4562238A Expired / Lapsed US ⏱️ 0.0 years remaining

Room temperature curable silicone rubber composition

Assignee: Shin-Etsu Chemical Co Ltd
•
Filing: 1984-06-18
•
Granted: 1985-12-31
•
Expires: 2004-06-18
📄 Original PDF 🌐 Google Patents 🔄 Sync Now

Abstract

Abstract The invention provides an improvement of a room temperature-curable silicone rubber composition cured by the mechanism of the condensation reaction between terminal silanolic hydroxy groups of a diorganopolysiloxane and an organosilicon compound having at least three alkoxy groups per molecule in the presence of an organotin compound as a catalyst to form crosslinks in respect of the remarkably small permanent compression set as well as excellent heat resistance of the cured rubbery elastomer thereof. Different from conventional compositions of the above mentioned type containing some organotin compound as the curing catalyst, the inventive composition preferably contains very specific organotin compound as the curing catalyst, which is represented by the general formula R2R1Sn-O-SnR1R2 or R2SnR21, in which R is a monovalent hydrocarbon group and R1 is an acid residue of a monoalkyl ester of a dibasic carboxylic acid such as MeOCOCH=CHCOO- and the like, in a limited amount. The composition may further contain an inorganic filler, of which the neutral surface condition is important in order that the composition may have good curability to give a cured rubbery elastomer exhibiting a small permanent compression set. A limited content of silicon-bonded vinyl group in the diorganopolysiloxane, the balance being methyl groups, is effective to improve the heat resistance of the cured rubber.

Inventors

  • 👤 Kiyohiro Kondo
  • 👤 Hiroshi Sugawara
  • 👤 Nobuyuki Hasebe

Bibliographic Details

Application Number —
Jurisdiction US
Data Source google_patents
Last Synchronized 2026-10-30 18:40
CPC Classifications
C; C08; C08K; C08K5/00; C08K5/56; C08K5/57; C08K5/54

Claims Analysis

Total Claims: 6
Claim 1
Independent Claim 162 words
A room temperature-curable silicone rubber composition which comprises: (a) 100 parts by weight of a diorganopolysiloxane of a substantially linear molecular structure terminated at both molecular chain ends each with a hydroxy group directly bonded to the silicon atom and having a viscosity in the range from 500 to 1,000,000 centistokes at 25° C.; (b) from 1 to 30 parts by weight of an organosilicon compound having at least three alkoxy groups directly bonded to the silicon atom or atoms; (c) up to 300 parts by weight of an inorganic filler having a surface property not excessively acidic or alkaline; and (d) an organotin compound represented by the general formula R.sub.2 R.sup.1 Sn--O--SnR.sup.1 R.sub.2 or R.sub.2 SnR.sup.1.sub.2, in which R is a monovalent hydrocarbon group and R 1 is an acid residue of a monoalkyl ester of a dibasic carboxylic acid, in an amount from 0.01 to 5% by weight based on the total amount of the components (a), (b), and (c).
Claim 2
Dependent Claim 162 words
A room temperature-curable silicone rubber composition which comprises: (a) 100 parts by weight of a diorganopolysiloxane of a substantially linear molecular structure terminated at both molecular chain ends each with a hydroxy group directly bonded to the silicon atom and having a viscosity in the range from 500 to 1,000,000 centistokes at 25° C.; (b) from 1 to 30 parts by weight of an organosilicon compound having at least three alkoxy groups directly bonded to the silicon atom or atoms; (c) up to 300 parts by weight of an inorganic filler having a surface property not excessively acidic or alkaline; and (d) an organotin compound represented by the general formula R.sub.2 R.sup.1 Sn--O--SnR.sup.1 R.sub.2 or R.sub.2 SnR.sup.1.sub.2, in which R is a monovalent hydrocarbon group and R 1 is an acid residue of a monoalkyl ester of a dibasic carboxylic acid, in an amount from 0.01 to 5% by weight based on the total amount of the components (a), (b), and (c).
Claim 3
Dependent Claim 42 words
The room temperature-curable silicone rubber composition as claimed in claim 1 wherein the organotin compound as the component (d) is selected from the class consisting of bis(methoxymaleoyloxy dibutyltin) oxide, bis(ethoxymaleoyloxy dibutyltin) oxide, bis(isopropoxymaleoyloxy dibutyltin) oxide, dibutyltin di(hexylmaleate), dibutyltin di(benzylmaleate) and dibutyltin di(octylphthalate).
Claim 4
Dependent Claim 41 words
The room temperature-curable silicone rubber composition as claimed in claim 1 wherein the inorganic filler as the component (c) has such a surface property that the aqueous suspension thereof has a value of pH in the range from 3 to 10.
Claim 5
Dependent Claim 46 words
The room temperature-curable silicone rubber composition as claimed in claim 1 wherein the organosilicon compound as the component (b) is selected from the class consisting of methyl trimethoxysilane, methyl triethoxysilane, phenyl trimethoxysilane, phenyl triethoxysilane, vinyl trimethoxysilane, vinyl triethoxysilane, tetraethoxysilane, tetrapropoxysilane and a partial hydrolysis-condensation product thereof.
Claim 6
Dependent Claim 50 words
The room temperature-curable silicone rubber composition as claimed in claim 1 wherein the diorganopolysiloxane as the component (a) contains from 0.01 to 0.1 mole of vinyl groups bonded to the silicon atoms per 100 g of the component, the balance of the organic groups in the component being methyl groups.

References Cited (Backward Citations)

US3664997A Cited
US3661887A Cited

USPTO Annuity & Maintenance Windows

Annuity Stage Window Opens Payment Deadline Surcharge Period Until Estimated Fee Status
3.5 Years (Year 4) 1988-12-30 1989-07-01 1989-12-31 $2000.00 Window Closed / Lapsed
7.5 Years (Year 8) 1992-12-30 1993-07-01 1993-12-31 $3760.00 Window Closed / Lapsed
11.5 Years (Year 12) 1996-12-30 1997-07-01 1997-12-31 $7700.00 Window Closed / Lapsed

Assigned Categories & Tags

No categories assigned to this patent yet.

Assign Category Tag