Modified polyolefin composition and process for producing the same
Assignee: Ube Corp
•
Filing: 1983-11-10
•
Granted: 1985-12-31
•
Expires: 2003-11-10
Abstract
Abstract A modified polyolefin composition useful for producing a shaped article having an excellent bonding property and an enhanced impact resistance comprises a modified olefin polymer material prepared by melting a mixture of an olefin polymer material comprising at least one crystalline ethylene-propylene random copolymer containing from 0.5 to 5% by weight of copolymerized ethylene and having a melt flow index of from 0.2 to 5 with a modifying agent consisting of at least one unsaturated dicarboxylic anhydride and a radical reaction initiator at a temperature of from 170 DEG C. to 270 DEG C. at which the mixture is melted; and a polyolefin rubber having a Mooney viscosity ML1+4 (100 DEG C.) of 10 to 100 and mixed in an amount of from 5% to 40% based on the sum of the weight of the modified olefin polymer material and the polyolefin rubber with the modified olefin polymer material at a temperature at which the mixture is melted.
Inventors
- 👤 Osamu Fukui
- 👤 Yoshihiro Inuizawa
- 👤 Saburo Hinenoya
- 👤 Yasufumi Takasaki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 06:01
CPC Classifications
C; C08; C08L; C08L51/00; C08L51/06
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
196 words
A modified polyolefin composition, consisting essentially of (A) a modified olefin polymer material which is a reaction product of 100 parts by weight of at least one crystalline ethylene-propylene random copolymer containing from 0.5% to 5% by weight of copolymerized ethylene and having a melt flow index of from 0.2 to 5, with from 0.02 to 0.3 parts by weight of a modifying agent consisting of at least one unsaturated dicarboxylic anhydride in the presence of from 0.01 to 0.2 parts by weight of a radical reaction initiator at a temperature of from 170° C. to 270° C. at which the reaction mixture is molten; and (B) an ethylene-propylene copolymer rubber in an amount of from 35% to 40% based on the sum of the weight of said modified olefin polymer material and said ethylene-propylene copolymer rubber, which copolymer rubber material has been mixed with said modified olefin polymer material at a temperature at which the resultant mixture is molten, said composition having a melt flow index of from 1 to 20 g/10 min determined in accordance with ASTM D 1238 at a temperature of 230° C., and a brittleness temperature not higher than -20° C.
Claim 2
Dependent Claim
196 words
A modified polyolefin composition, consisting essentially of (A) a modified olefin polymer material which is a reaction product of 100 parts by weight of at least one crystalline ethylene-propylene random copolymer containing from 0.5% to 5% by weight of copolymerized ethylene and having a melt flow index of from 0.2 to 5, with from 0.02 to 0.3 parts by weight of a modifying agent consisting of at least one unsaturated dicarboxylic anhydride in the presence of from 0.01 to 0.2 parts by weight of a radical reaction initiator at a temperature of from 170° C. to 270° C. at which the reaction mixture is molten; and (B) an ethylene-propylene copolymer rubber in an amount of from 35% to 40% based on the sum of the weight of said modified olefin polymer material and said ethylene-propylene copolymer rubber, which copolymer rubber material has been mixed with said modified olefin polymer material at a temperature at which the resultant mixture is molten, said composition having a melt flow index of from 1 to 20 g/10 min determined in accordance with ASTM D 1238 at a temperature of 230° C., and a brittleness temperature not higher than -20° C.
Claim 3
Dependent Claim
30 words
The composition as claimed in claim 1, wherein said radical reaction initiator (RI) and said modifying agent (MA) are used in a weight ratio (RI/MA) of from 0.1:1 to 5:1.
Claim 4
Dependent Claim
34 words
The composition as claimed in claim 1, wherein said unsaturated dicarboxylic anhydride is selected from the group consisting of anhydrides of maleic acid, fumaric acid, mesaconic acid, citraconic acid, 5-norbornene-2,3-dicarboxylic acid, and 1,2,3,6-tetrahydrophthalic acid.
Claim 5
Dependent Claim
44 words
The composition as claimed in claim 1, wherein said radical reaction initiator consists essentially of at least one member selected from the group consisting of azobis compounds and organic peroxide compounds which exhibit a one-minute half-life temperature of approximately 160° C. to 270° C.
Claim 6
Dependent Claim
29 words
The composition as claimed in claim 1, wherein said copolymer rubber is selected from the group consisting of ethylene-propylene copolymer rubbers, ethylene-propylene-non-conjugated diene terpolymer rubbers, and ethylene-propylene-butene-1 terpolymer rubbers.
Claim 7
Dependent Claim
201 words
A process for producing a modified polyolefin composition having a melt flow index of from 1 to 20 g/10 min determined in accordance with ASTM D 1238 at a temperature of 230° C., comprising the steps of: melting a reaction mixture of an olefin polymer material comprising 100 parts by weight of at least one crystalline ethylene-propylene random copolymer containing from 0.5% to 5% by weight of copolymerized ethylene and having a melt flow index of from 0.2 to 5 with from 0.02 to 0.3 parts by weight of a modifying agent consisting of at least one unsaturated dicarboxylic anhydride in the presence of from 0.01 to 0.2 parts by weight of a radical reaction initiator at temperature of from 170° C. to 270° C. at which the reaction mixture is melted so as to modify said olefin polymer material; and mixing the resultant modified olefin polymer material with ethylene-propylene copolymer rubber having a Mooney viscosity ML 1+4 (100° C.) of from 10 to 100 in an amount of from 35% to 40% based on the sum of the weights of said modified olefin polymer material and said ethylene-propylene copolymer rubber at a temperature at which the resultant mixture is melted.
Claim 8
Dependent Claim
201 words
A process for producing a modified polyolefin composition having a melt flow index of from 1 to 20 g/10 min determined in accordance with ASTM D 1238 at a temperature of 230° C., comprising the steps of: melting a reaction mixture of an olefin polymer material comprising 100 parts by weight of at least one crystalline ethylene-propylene random copolymer containing from 0.5% to 5% by weight of copolymerized ethylene and having a melt flow index of from 0.2 to 5 with from 0.02 to 0.3 parts by weight of a modifying agent consisting of at least one unsaturated dicarboxylic anhydride in the presence of from 0.01 to 0.2 parts by weight of a radical reaction initiator at temperature of from 170° C. to 270° C. at which the reaction mixture is melted so as to modify said olefin polymer material; and mixing the resultant modified olefin polymer material with ethylene-propylene copolymer rubber having a Mooney viscosity ML 1+4 (100° C.) of from 10 to 100 in an amount of from 35% to 40% based on the sum of the weights of said modified olefin polymer material and said ethylene-propylene copolymer rubber at a temperature at which the resultant mixture is melted.
Claim 9
Dependent Claim
24 words
The process as claimed in claim 6, wherein said mixing operation is carried out at a temperature of from 160° C. to 270° C.
Claim 10
Dependent Claim
25 words
A shaped composite article wherein shaped articles made of a metallic material are bonded to each other with the modified polyolefin composition of claim 1.
References Cited (Backward Citations)
US3868433A
Cited
US3987122A
Cited
US4198327A
Cited
US4198327B1
Cited
US4230830A
Cited
US4230830B1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-12-30 | 1989-07-01 | 1989-12-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-12-30 | 1993-07-01 | 1993-12-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-12-30 | 1997-07-01 | 1997-12-31 | $7700.00 | Window Closed / Lapsed |