Electrical resistor and method of making the same
Assignee: CTS Corp
•
Filing: 1981-02-09
•
Granted: 1985-12-31
•
Expires: 2001-02-09
Abstract
Abstract Disclosed is a method for making glass bonded metal oxide electric resistors involving including in the mixture a refractory oxide for providing configuration stability during firing.
Inventors
- 👤 Curtis L. Holmes
- 👤 William M. Faber, Sr.
- 👤 Gaylord L. Francis
- 👤 Otis F. Boykin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 16:10
CPC Classifications
H; H01; H01C; H01C17/00; H01C17/06; H01C17/065; H01C17/06506; H01C17/06513; H01C17/06533; H01C17/0654
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
97 words
A resistor composition comprising a mixture of a finely divided glass, at least 0.2 percent by weight of the total composition of a finely divided oxide of a noble metal selected from the group consisting of iridium oxide and ruthenium oxide, and 30 percent to 70 percent by weight of the total composition of a finely divided refractory filler oxide, the ratio of the glass to the refractory filler oxide being such that the composition may be formed into a desired shape and fired at a temperature sufficiently high to fuse the glass without changing the shape.
Claim 2
Dependent Claim
97 words
A resistor composition comprising a mixture of a finely divided glass, at least 0.2 percent by weight of the total composition of a finely divided oxide of a noble metal selected from the group consisting of iridium oxide and ruthenium oxide, and 30 percent to 70 percent by weight of the total composition of a finely divided refractory filler oxide, the ratio of the glass to the refractory filler oxide being such that the composition may be formed into a desired shape and fired at a temperature sufficiently high to fuse the glass without changing the shape.
Claim 3
Dependent Claim
30 words
The resistor composition of claim 1, wherein the refractory filler oxide is selected from the group consisting of alumina, silica, beryllia, feldspar, chromic oxide, kaolin, titania, zinc oxide and zirconia.
Claim 4
Dependent Claim
61 words
A resistor composition comprising a mixture of a finely divided refractory filler oxide, finely divided glass particles, and at least 0.2 percent by weight of the total composition of at least one of the metal oxides selected from the group consisting of iridium oxide and ruthenium oxide, and obtained by the pyrolytic decomposition of an iridium resinate or a ruthenium resinate.
Claim 5
Dependent Claim
61 words
A resistor composition comprising a mixture of a finely divided refractory filler oxide, finely divided glass particles, and at least 0.2 percent by weight of the total composition of at least one of the metal oxides selected from the group consisting of iridium oxide and ruthenium oxide, and obtained by the pyrolytic decomposition of an iridium resinate or a ruthenium resinate.
Claim 6
Dependent Claim
79 words
A resistor composition comprising a mixture of a finely divided refractory filler oxide, finely divided glass particles, and at least 0.2 percent by weight of the total composition of a plurality of a metal and a metal oxide, the metal oxide comprising 50 to 90 percent by weight ruthenium oxide and the metal comprising 10 to 50 percent by weight platinum, both the metal and the metal oxide being obtained by pyrolytic decomposition of ruthenium resinate and platinum resinate.
Claim 7
Dependent Claim
79 words
A resistor composition comprising a mixture of a finely divided refractory filler oxide, finely divided glass particles, and at least 0.2 percent by weight of the total composition of a plurality of a metal and a metal oxide, the metal oxide comprising 50 to 90 percent by weight ruthenium oxide and the metal comprising 10 to 50 percent by weight platinum, both the metal and the metal oxide being obtained by pyrolytic decomposition of ruthenium resinate and platinum resinate.
Claim 8
Dependent Claim
84 words
A resistor composition comprising a mixture of a finely divided refractory filler oxide, at least 30 percent by weight of the total composition of finely divided glass particles, and at least 0.2 percent by weight of the total composition of a plurality of metal oxides, the metal oxides comprising 1 to 99 percent by weight ruthenium oxide and 1 to 99 percent by weight iridium oxide, both metal oxides being obtained by pyrolytic decomposition of resinates containing the metal included in the metal oxides.
Claim 9
Dependent Claim
84 words
A resistor composition comprising a mixture of a finely divided refractory filler oxide, at least 30 percent by weight of the total composition of finely divided glass particles, and at least 0.2 percent by weight of the total composition of a plurality of metal oxides, the metal oxides comprising 1 to 99 percent by weight ruthenium oxide and 1 to 99 percent by weight iridium oxide, both metal oxides being obtained by pyrolytic decomposition of resinates containing the metal included in the metal oxides.
Claim 10
Dependent Claim
86 words
A resistor composition comprising a mixture of a finely divided refractory filler oxide, finely divided glass particles, and at least 0.2 percent by weight of the total composition of a plurality of a metal and a metal oxide, the metal oxide comprising 50 to 90 percent by weight iridium oxide and the metal comprising 10 to 50 percent by weight platinum, both the metal and the metal oxide being obtained by pyrolytic decomposition of resinates containing the metal and the metal included in the metal oxide.
Claim 11
Dependent Claim
86 words
A resistor composition comprising a mixture of a finely divided refractory filler oxide, finely divided glass particles, and at least 0.2 percent by weight of the total composition of a plurality of a metal and a metal oxide, the metal oxide comprising 50 to 90 percent by weight iridium oxide and the metal comprising 10 to 50 percent by weight platinum, both the metal and the metal oxide being obtained by pyrolytic decomposition of resinates containing the metal and the metal included in the metal oxide.
Claim 12
Dependent Claim
120 words
A resistor composition containing a mixture of at least 30 percent by weight of the total composition of a finely divided glass, at least 30 percent by weight of the total composition of a finely divided refractory filler oxide, and at least 0.2 percent by weight of the total composition of a noble metal oxide selected from the group consisting of iridium oxide and ruthenium oxide deposited on the surface of one of the glass and the refractory filler oxide, the ratio of glass to refractory filler oxide being such that the composition can be formed into a desired configuration, fired at a temperature sufficiently high to fuse the glass, and produce a non-porous, rigid mass of the desired configuration.
Claim 13
Dependent Claim
120 words
A resistor composition containing a mixture of at least 30 percent by weight of the total composition of a finely divided glass, at least 30 percent by weight of the total composition of a finely divided refractory filler oxide, and at least 0.2 percent by weight of the total composition of a noble metal oxide selected from the group consisting of iridium oxide and ruthenium oxide deposited on the surface of one of the glass and the refractory filler oxide, the ratio of glass to refractory filler oxide being such that the composition can be formed into a desired configuration, fired at a temperature sufficiently high to fuse the glass, and produce a non-porous, rigid mass of the desired configuration.
Claim 14
Dependent Claim
103 words
A resistor composition comprising a resistive metal-organometallic compound, at least one metal stabilizer in organometallic form and an anti-agglomerating agent which is inert to the system and which prevents agglomeration of the resistive metal and metal stabilizer during alloying thereof, which alloying is conducted prior to the firing of the composition into a resistor structure, said resistive metal being selected f om the group consisting of palladium, rhodium, iridium, ruthenium and mixtures thereof, said metal stabilizer being selected from the group consisting of silver, gold and platinum and mixtures thereof, and said anti-agglomerating agent being selected from ultrafine silica and an ultrafine refractory.
Claim 15
Dependent Claim
103 words
A resistor composition comprising a resistive metal-organometallic compound, at least one metal stabilizer in organometallic form and an anti-agglomerating agent which is inert to the system and which prevents agglomeration of the resistive metal and metal stabilizer during alloying thereof, which alloying is conducted prior to the firing of the composition into a resistor structure, said resistive metal being selected f om the group consisting of palladium, rhodium, iridium, ruthenium and mixtures thereof, said metal stabilizer being selected from the group consisting of silver, gold and platinum and mixtures thereof, and said anti-agglomerating agent being selected from ultrafine silica and an ultrafine refractory.
Claim 16
Dependent Claim
13 words
A resistor composition according to claim 8, wherein said resistive metal is palladium.
Claim 17
Dependent Claim
94 words
A resistor composition comprising a particulate lead borosilicate glass binder having a firing temperature of about 800° C. and a positive TCR, said glass binder being admixed with a substantially homogenous finely divided, powder comprised of at least one resistive metal selected from the group consisting of palladium, rhodium, iridium, ruthenium and mixtures thereof, at least two stabilizer metals selected from the group consisting of silver, gold and platinum, and about 0.02-0.5 weight percent, related to the weight of the metal powder of particulate MnO 2 to reduce the TCR of said resistor composition.
Claim 18
Dependent Claim
94 words
A resistor composition comprising a particulate lead borosilicate glass binder having a firing temperature of about 800° C. and a positive TCR, said glass binder being admixed with a substantially homogenous finely divided, powder comprised of at least one resistive metal selected from the group consisting of palladium, rhodium, iridium, ruthenium and mixtures thereof, at least two stabilizer metals selected from the group consisting of silver, gold and platinum, and about 0.02-0.5 weight percent, related to the weight of the metal powder of particulate MnO 2 to reduce the TCR of said resistor composition.
Claim 19
Dependent Claim
38 words
A resistor composition according to claim 10, wherein said powder also includes an anti-agglomerating agent substantially homogeneously dispersed throughout the powder, said anti-agglomerating agent being a refractory having a particle size less than about two hundred fifty microns.
Claim 20
Dependent Claim
13 words
A resistor composition according to claim 10, wherein said resistive metal is palladium.
References Cited (Backward Citations)
US1764311A
Cited
US2739901A
Cited
US2718577A
Cited
US2786819A
Cited
US2950995A
Cited
US3149002A
Cited
US2950996A
Cited
US2924540A
Cited
US3154503A
Cited
US3304199A
Cited
US3329526A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-12-30 | 1989-07-01 | 1989-12-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-12-30 | 1993-07-01 | 1993-12-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-12-30 | 1997-07-01 | 1997-12-31 | $7700.00 | Window Closed / Lapsed |