Method of manufacturing a positive temperature coefficient resistive heating element

Claim 2

A process for producing a positive temperature coefficient resistance element comprising the steps of: A. blending a polymer having at least about 20% crystallinity as determined by X-ray diffraction and having a melt flow index of at least one with an effective amount of up to about 20% by weight of carbon black to attain a suitable volume resistivity when voltage is applied to the resulting composition; B. placing the composition of step A in contact with a pair of spaced-apart conductive electrodes; C. maintaining the product of step B at a temperature above the melting point of the polymer component of the blend of step A for no more than about one hour and then cooling to produce an approximately constant room temperature volume resistivity of the composition of less than about 100,000 ohm-cm and thereby obtain a temperature self-regulating resistance element.

Claim 3

The process of claim 1 wherein the polymer fraction of the blend of step A has a melt flow index greater than 1.2.

Claim 4

The process of claim 1 wherein the polymer fraction of the blend of step A has a melt flow index between 1.5 and 10.

Claim 5

The process of claim 1 wherein the melt flow index of a polymer blended in step A is between about 10 and 100.

Claim 6

The process of claim 1 wherein said crystalline polymer is selected from a group consisting of polyolefins, fluoropolymers, copolymers, terpolymers containing non-conjugated dienes, and mixtures thereof.

Claim 7

The process of claim 1 wherein in step C the product of step B is maintained at said temperature for less than about 5 minutes.

Claim 8

The process of claim 1 wherein the carbon black blended in step A is a low structure carbon black having a dibutyl phthalate absorption of less than about 100 ml/100 g of carbon black.

Claim 9

The process of claim 1 wherein the carbon black blended in step A is present at a level less than about 15% by weight.

Claim 10

The process of claim 1 comprising a continuous process wherein step B is effected by extruding said composition about elongate electrodes, and step C is effected by exposing the resulting extrudate to said temperature as said extrudate passes through a heated zone.

Claim 11

The process of claim 1 comprising the additional step of cross-linking said composition after step c.

Claim 12

A process for producing a positive temperature coefficient resistance element comprising the steps of: extruding a positive temperature coefficient composition over a pair of spaced-apart elongate conductive electrodes, said positive temperature coefficient composition comprising a blend of a polymer having at least about 20% crystallinity as determined by X-ray diffraction and having a melt flow index of at least one and an effective amount of up to 20% by weight of carbon black to attain a suitable volume resistivity when voltage is applied to the resulting composition; and maintaining the positive temperature coefficient composition at a temperature above the melting point of the polymer in the blend for a sufficient amount of time less than one hour, and then cooling, to produce an approximately constant volume resistivity in said positive temperature coefficient composition to convert said composition and electrodes into a useful positive temperature coefficient resistance heating element.

Claim 13

A process for producing a positive temperature coefficient resistance element comprising the steps of: extruding a positive temperature coefficient composition over a pair of spaced-apart elongate conductive electrodes, said positive temperature coefficient composition comprising a blend of a polymer having at least about 20% crystallinity as determined by X-ray diffraction and having a melt flow index of at least one and an effective amount of up to 20% by weight of carbon black to attain a suitable volume resistivity when voltage is applied to the resulting composition; and maintaining the positive temperature coefficient composition at a temperature above the melting point of the polymer in the blend for a sufficient amount of time less than one hour, and then cooling, to produce an approximately constant volume resistivity in said positive temperature coefficient composition to convert said composition and electrodes into a useful positive temperature coefficient resistance heating element.