Method for forming structural parts
Assignee: Boeing North American Inc
•
Filing: 1985-07-17
•
Granted: 1985-12-24
•
Expires: 2005-07-17
Abstract
Abstract Method for producing structures from metal workpieces which may or may not be capable of superplastic forming, such as titanium alloy and steel, using a forming die having a predetermined contour or shape and a cooperating pressure diaphragm formed of a metal capable of superplastic forming. Fluid pressure is applied to one side of the pressure diaphragm to cause stretching or expansion thereof by superplastic forming, and forcing the diaphragm against the workpiece, which in turn is caused to move or expand into contact with the forming die, to produce a structural component of predetermined shape. With the proper application of pressure, temperature and time, metal parts, e.g. 8 to 12 inches thick, can be formed in addition to parts formed from comparatively thin sheet metal.
Inventors
- 👤 Roger S. Raymond
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 23:50
CPC Classifications
B; B21; B21D; B21D26/00; B21D26/02; B21D26/053; B21D26/055
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
110 words
A method for producing a metallic structure of predetermined shape from a metal workpiece which comprises: providing an apparatus containing a forming die having a contoured surface of predetermined shape; positioning a formable metal workpiece adjacent to said forming die; providing a pressure diaphragm of a metal sheet capable of superplastic forming adjacent to said workpiece; bringing said diaphragm to within an elevated temperature range suitable for superplastic forming of said diaphragm; and applying pressure to one side of said diaphragm to plastically deform said diaphragm by superplastic forming against said workpiece and in turn deforming said workpiece against said forming die to produce a structural component of predetermined shape.
Claim 2
Independent Claim
110 words
A method for producing a metallic structure of predetermined shape from a metal workpiece which comprises: providing an apparatus containing a forming die having a contoured surface of predetermined shape; positioning a formable metal workpiece adjacent to said forming die; providing a pressure diaphragm of a metal sheet capable of superplastic forming adjacent to said workpiece; bringing said diaphragm to within an elevated temperature range suitable for superplastic forming of said diaphragm; and applying pressure to one side of said diaphragm to plastically deform said diaphragm by superplastic forming against said workpiece and in turn deforming said workpiece against said forming die to produce a structural component of predetermined shape.
Claim 3
Dependent Claim
21 words
The method of claim 1, wherein said pressure diaphragm is a sealed diaphragm and wherein said applied pressure is fluid pressure.
Claim 4
Dependent Claim
17 words
The method of claim 1, wherein said metal workpiece is of a metal capable of superplastic forming.
Claim 5
Dependent Claim
11 words
The method of claim 1, wherein said metal workpiece is steel.
Claim 6
Dependent Claim
18 words
The method of claim 1, wherein said pressure diaphragm and said workpiece are comprised of a titanium alloy.
Claim 7
Dependent Claim
20 words
The method of claim 1, wherein said pressure diaphragm and said workpiece are comprised of aluminum or an aluminum alloy.
Claim 8
Dependent Claim
26 words
The method of claim 1 wherein said step of applying pressure is such that said diaphragm conforms to the surface of said workpiece which it contacts.
Claim 9
Dependent Claim
40 words
The method of claim 7 wherein during said step of applying pressure, said diaphragm also deforms against a portion of said forming die and said diaphragm conforms to the surface of said forming die where it contacts said forming die.
Claim 10
Independent Claim
129 words
A method for producing a metallic structure of predetermined shape from a workpiece capable of superplastic forming which comprises: providing an apparatus containing a forming die having a contoured surface of predetermined shape; positioning a workpiece of a metal capable of superplastic forming adjacent to said forming die; positioning a pressure diaphragm of a metal sheet capable of superlastic forming adjacent to said workpiece on the opposite side thereof from said forming die; heating said pressure diaphragm and said workpiece to superplastic forming temperature; and applying pressure to one side of said diaphragm opposite to said workpiece to plastically deform said diaphragm by superplastic forming against said workpiece and in turn deforming said workpiece by superplastic forming against said forming die to produce a structural component of predetermined shape.
Claim 11
Independent Claim
129 words
A method for producing a metallic structure of predetermined shape from a workpiece capable of superplastic forming which comprises: providing an apparatus containing a forming die having a contoured surface of predetermined shape; positioning a workpiece of a metal capable of superplastic forming adjacent to said forming die; positioning a pressure diaphragm of a metal sheet capable of superlastic forming adjacent to said workpiece on the opposite side thereof from said forming die; heating said pressure diaphragm and said workpiece to superplastic forming temperature; and applying pressure to one side of said diaphragm opposite to said workpiece to plastically deform said diaphragm by superplastic forming against said workpiece and in turn deforming said workpiece by superplastic forming against said forming die to produce a structural component of predetermined shape.
Claim 12
Dependent Claim
47 words
The method of claim 9, including positioning an upper die adjacent to said pressure diaphragm on the opposite said thereof from said workpiece and providing a seal between said pressure diaphragm and said workpiece to form a pressure chamber therebetween, and applying pressure fluid to said chamber.
Claim 13
Dependent Claim
18 words
The method of claim 9, wherein said pressure diaphragm and said workpiece are comprised of a titanium alloy.
References Cited (Backward Citations)
US3934441A
Cited
US4087037A
Cited
US4117970A
Cited
US4188811A
Cited
US4269053A
Cited
US4409809A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-12-23 | 1989-06-24 | 1989-12-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-12-23 | 1993-06-24 | 1993-12-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-12-23 | 1997-06-24 | 1997-12-24 | $7700.00 | Window Closed / Lapsed |