US4558200A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Electrical lead termination
Assignee: Ranco Inc of Delaware
•
Filing: 1983-08-12
•
Granted: 1985-12-10
•
Expires: 2003-08-12
Abstract
Abstract A method of attaching fine coil wire ends 22, 24 to terminal connectors 16, 18 wherein the terminals are rapidly heated into the red zone by common current flow therethrough from contact electrodes 26, 28 in the presence of a gaseous purge comprising a mixture of hydrogen balance argon, nitrogen, or helium while low melting temperature solder 84 is flowed onto the heated terminal for wire attachment. The gaseous purge from a nozzle 80 is maintained until the terminal has cooled sufficiently to prevent rapid atmosphere oxidation thereof.
Inventors
- 👤 Charles H. Weigand, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 01:28
CPC Classifications
B; B23; B23K; B23K3/00; B23K3/08; B23K3/02; B23K3/03; B23K3/0307; B23K2101/00; B23K2101/36; B23K2101/38
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
91 words
A method of making circuit terminations comprising of steps of: (a) providing a metal connecting terminal for electrical lead connection thereto; (b) heating said terminal to a temperature above 450° C.; (c) flowing a gaseous mixture comprising 5-15% hydrogen, balance selected from the group consisting of argon, nitrogen or helium over said heated terminal; and, (d) applying a solder having a melting point not greater than 350° C. to said terminal in the region of said lead connection and permitting said solder to melt in the atmosphere of said gaseous mixture.
Claim 2
Independent Claim
91 words
A method of making circuit terminations comprising of steps of: (a) providing a metal connecting terminal for electrical lead connection thereto; (b) heating said terminal to a temperature above 450° C.; (c) flowing a gaseous mixture comprising 5-15% hydrogen, balance selected from the group consisting of argon, nitrogen or helium over said heated terminal; and, (d) applying a solder having a melting point not greater than 350° C. to said terminal in the region of said lead connection and permitting said solder to melt in the atmosphere of said gaseous mixture.
Claim 3
Dependent Claim
28 words
The method defined in claim 1 where in the step of heating comprises contacting said terminal with a pair of electrodes and flowing a current through said terminal;
Claim 4
Dependent Claim
21 words
The method defined in claim 1 wherein said step of applying solder comprises progressively advancing a continuous wire strip of solder.
Claim 5
Dependent Claim
31 words
The method defined in claim 1 further comprising the step of maintaining said flow of gaseous mixture until said solder cools to a temperature below the oxidation point of the terminal;
Claim 6
Dependent Claim
23 words
The method defined in claim 1 where in said step of applying solder includes feeding a connection wire of solder against said connections
Claim 7
Independent Claim
96 words
A method of making coil lead terminations comprising the steps of: (a) providing a pair of spaced connecting terminals for connection thereto; (b) wrapping a coil lead about portions of each terminal; (c) flowing a common electrical current through said terminals for heating said terminals to an elevated temperature in the range sufficient to cause rapid oxidation; and (d) applying solder to said pair of heated terminals while at said elevated temperature; and, (e) flowing a gaseous mixture comprising 5-15% hydrogen, balance selected from the group consisting of argon, nitrogen or helium over said heated terminals.
Claim 8
Independent Claim
96 words
A method of making coil lead terminations comprising the steps of: (a) providing a pair of spaced connecting terminals for connection thereto; (b) wrapping a coil lead about portions of each terminal; (c) flowing a common electrical current through said terminals for heating said terminals to an elevated temperature in the range sufficient to cause rapid oxidation; and (d) applying solder to said pair of heated terminals while at said elevated temperature; and, (e) flowing a gaseous mixture comprising 5-15% hydrogen, balance selected from the group consisting of argon, nitrogen or helium over said heated terminals.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-12-09 | 1989-06-10 | 1989-12-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-12-09 | 1993-06-10 | 1993-12-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-12-09 | 1997-06-10 | 1997-12-10 | $7700.00 | Window Closed / Lapsed |