Process for the preparation of alumina
Assignee: Chiyoda Corp
•
Filing: 1984-06-01
•
Granted: 1985-11-26
•
Expires: 2004-06-01
Abstract
Abstract An improved process for the preparation of alumina, including forming an alumina hydrogel from aluminum hydroxide, and processing the alumina hydrogel into alumina. The improvement involves the alumina hydrogel forming step which is connected in the presence of sulfate ion and which comprises providing, in a reaction zone, an aqueous slurry containing seed aluminum hydroxide and having a pH of 6-11, and feeding to the reaction zone an aluminum compound and a pH controlling agent for mixing with the aqueous slurry while maintaining the aqueous slurry at a temperature of at least about 50 DEG C. at feed rates so that the pH of the aqueous slurry is maintained within the range of 6-11 and that 0.2-5 mols/hour of aluminum components, in terms of elemental aluminum, are fed to the reaction zone per mole of the seed aluminum hydroxide originally contained in the aqueous slurry, whereby the seed aluminum hydroxide is caused to grow to the aluminum hydrogel.
Inventors
- 👤 Sachio Asaoka
- 👤 Takashi Sendo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 02:29
CPC Classifications
C; C01; C01F; C01F7/00; C01F7/02; C01F7/34; B; B82; B82Y; B82Y30/00; C01P; C01P2006/00; C01P2006/12; C01P2006/14; C01P2006/16; C01P2006/17; C01P2006/21
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
149 words
In a process for the preparation of alumina, including forming an alumina hydrogel from aluminum hydroxide, and processing the alumina hydrogel into alumina, the improvement comprising the alumina hydrogel forming step which is conducted in the presence of sulfate ion and which comprises feeding an aluminum compound and a pH controlling agent to a reaction zone, in which an aqueous slurry containing seed aluminum hydroxide is contained, for mixing with said aqueous slurry while maintaining said aqueous slurry at a temperature of at least about 50° C. at feed rates so that the pH of said aqueous slurry is maintained within the range of 6-11 and that 0.2-5 mols/hour of aluminum components, in terms of elemental aluminum, are fed to said reaction zone per mole of the seed aluminum hydroxide originally contained in said aqueous slurry, whereby the seed aluminum hydroxide is caused to grow to the alumina hydrogel.
Claim 2
Dependent Claim
149 words
In a process for the preparation of alumina, including forming an alumina hydrogel from aluminum hydroxide, and processing the alumina hydrogel into alumina, the improvement comprising the alumina hydrogel forming step which is conducted in the presence of sulfate ion and which comprises feeding an aluminum compound and a pH controlling agent to a reaction zone, in which an aqueous slurry containing seed aluminum hydroxide is contained, for mixing with said aqueous slurry while maintaining said aqueous slurry at a temperature of at least about 50° C. at feed rates so that the pH of said aqueous slurry is maintained within the range of 6-11 and that 0.2-5 mols/hour of aluminum components, in terms of elemental aluminum, are fed to said reaction zone per mole of the seed aluminum hydroxide originally contained in said aqueous slurry, whereby the seed aluminum hydroxide is caused to grow to the alumina hydrogel.
Claim 3
Dependent Claim
23 words
A process according to claim 1, wherein said feeding of the aluminum compound and the pH controlling agent is conducted continuously and simultaneously.
Claim 4
Dependent Claim
19 words
A process according to claim 1, wherein said aqueous slurry contained in said reaction zone contains the sulfate ion.
Claim 5
Dependent Claim
26 words
A process according to claim 1, wherein at least one of the aluminum compound and the pH controlling agent is capable of generating the sulfate ion.
Claim 6
Dependent Claim
49 words
A process according to claim 1, wherein the aluminum compound and the pH controlling agent are each fed to said reaction zone in the form of an aqueous solution, at least one of the aqueous solutions of aluminum compound and of the pH controlling agent contains the sulfate ion.
Claim 7
Dependent Claim
33 words
A process according to claim 1, wherein the aluminum compound is aluminum sulfate and the pH controlling agent is selected from the group consisting of sodium aluminate, sodium hydroxide, potassium hydroxide and ammonia.
Claim 8
Dependent Claim
14 words
A process according to claim 6, wherein the pH controlling agent is sodium aluminate.
Claim 9
Dependent Claim
14 words
A process according to claim 6, wherein the pH controlling agent is sodium hydroxide.
Claim 10
Dependent Claim
21 words
A process according to claim 1, wherein the aluminum compound is an aluminate and the pH controlling agent is sulfuric acid.
Claim 11
Dependent Claim
13 words
A process according to claim 9, wherein the aluminum compound is sodium aluminate.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-11-25 | 1989-05-27 | 1989-11-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-11-25 | 1993-05-27 | 1993-11-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-11-25 | 1997-05-27 | 1997-11-26 | $7700.00 | Window Closed / Lapsed |