Method of forming a continuous polymeric skin on a cellular foam material
Assignee: United States Department of Energy
•
Filing: 1982-10-21
•
Granted: 1985-11-26
•
Expires: 2002-10-21
Abstract
Abstract Hydrophobic cellular material is coated with a thin hydrophilic polymer skin which stretches tightly over the outer surface of the foam but which does not fill the cells of the foam, thus resulting in a polymer-coated foam structure having a smoothness which was not possible in the prior art. In particular, when the hydrophobic cellular material is a specially chosen hydrophobic polymer foam and is formed into arbitrarily chosen shapes prior to the coating with hydrophilic polymer, inertial confinement fusion (ICF) targets of arbitrary shapes can be produced by subsequently coating the shapes with metal or with any other suitable material. New articles of manufacture are produced, including improved ICF targets, improved integrated circuits, and improved solar reflectors and solar collectors. In the coating method, the cell size of the hydrophobic cellular material, the viscosity of the polymer solution used to coat, and the surface tensin of the polymer solution used to coat are all very important to the coating.
Inventors
- 👤 David V. Duchane
- 👤 Barry L. Barthell
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 09:32
CPC Classifications
B; B05; B05D; B05D7/00; B05D7/02; C; C08; C08J; C08J9/00; C08J9/36; C08J9/365; B05D5/00; B05D5/04; B05D5/06; B05D5/067; Y; Y10; Y10S; Y10S205/00; Y10S205/923
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
149 words
A method of forming a thin, smooth continuous skin of a hydrophilic polymer on the outer surface of a hydrophobic cellular material, said method comprising: (a) coating said outer surface said cellular material, which has an average cell size less than about 500 μm, in a wetting solution of said hydrophilic polymer and water, wherein said wetting solution has a surface tension within the range from about 35 to about 55 dynes/cm and a viscosity within the range from about 100 to about 3000 cP; (b) removing said cellular material from said wetting solution and allowing the excess wetting solution to drain away from said cellular material; and (c) drying the wetted surface of said cellular material to thereby remove by evaporation the water in the wetting solution on said surface, thereby forming a smooth continuous layer of said hydrophilic polymer on the outer surface of said cellular material.
Claim 2
Independent Claim
149 words
A method of forming a thin, smooth continuous skin of a hydrophilic polymer on the outer surface of a hydrophobic cellular material, said method comprising: (a) coating said outer surface said cellular material, which has an average cell size less than about 500 μm, in a wetting solution of said hydrophilic polymer and water, wherein said wetting solution has a surface tension within the range from about 35 to about 55 dynes/cm and a viscosity within the range from about 100 to about 3000 cP; (b) removing said cellular material from said wetting solution and allowing the excess wetting solution to drain away from said cellular material; and (c) drying the wetted surface of said cellular material to thereby remove by evaporation the water in the wetting solution on said surface, thereby forming a smooth continuous layer of said hydrophilic polymer on the outer surface of said cellular material.
Claim 3
Dependent Claim
15 words
A method according to claim 1, wherein said hydrophobic cellular material is a polymer foam.
Claim 4
Dependent Claim
40 words
A method according to claim 2, wherein the surface tension of said wetting solution is within the range from about 40 to about 50 dynes/cm and wherein the cell size of said polymer foam is less than about 200 μm.
Claim 5
Dependent Claim
24 words
A method according to claim 3, wherein the viscosity of said wetting solution is within the range from about 100 to about 1000 cP.
Claim 6
Dependent Claim
12 words
A method according to claim 4 wherein said hydrophobic foam is poly(4-methyl-1-pentene).
Claim 7
Dependent Claim
13 words
A method according to claim 5, wherein said hydrophilic polymer is polyvinyl alcohol.
Claim 8
Dependent Claim
13 words
A method according to claim 5, wherein said hydrophilic polymer is hydroxypropyl cellulose.
Claim 9
Dependent Claim
79 words
A method of producing an arbitrarily shaped structure having a smooth exterior layer of metal and an interior structure comprising a hydrophobic cellular material, said method comprising: (a) forming a hydrophobic foam having a cell size less than about 500 μm into a chosen shape; (b) coating said chosen shape with a hydrophilic polymer according to the method of claim 2, so as to form a polymer-coated shape; (c) applying a coating of metal to said polymer coated shape.
Claim 10
Dependent Claim
21 words
A method according to claim 8, wherein the formed structure of foam is removed by dissolving the foam after step (c).
Claim 11
Dependent Claim
37 words
A method of forming an inertial confinement fusion target comprising the method according to claim 8, wherein the foam used has a density within the range from about 0.005 g/cm 3 to about 0.2 g/cm 3 .
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-11-25 | 1989-05-27 | 1989-11-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-11-25 | 1993-05-27 | 1993-11-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-11-25 | 1997-05-27 | 1997-11-26 | $7700.00 | Window Closed / Lapsed |