Method of fabricating optical glass base material and apparatus for fabricating the same
Assignee: Furukawa Electric Co Ltd
•
Filing: 1984-08-20
•
Granted: 1985-11-12
•
Expires: 2004-08-20
Abstract
Abstract A method of fabricating an optical glass base material by injecting and depositing fine glass particles produced by chemically reacting glass stock which comprises means for growing the fine glass particles in a depositing direction to form porous rod-shaped base material, support means for supporting the porous rod-shaped base material after growing, and heat treatment means for sintering at least the outer periphery of the rod-shaped base material in a semisintering state before supporting the rod-shaped base material by said support means to harden the same. Thus, since the rod-shaped base material is held in the stable state through the support means, the mechanical strength of the base material is strengthened strength by the semisintering hardening through the heat treating means before being supported by the support means, the base material is not deformed nor damaged in the supported state, and a large base material may be fabricated.
Inventors
- 👤 Ryoichi Hara
- 👤 Toshiaki Kuroha
- 👤 Nobuo Inagaki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 01:58
CPC Classifications
C; C03; C03B; C03B37/00; C03B37/01; C03B37/012; C03B37/014
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
166 words
A method of fabricating an optical glass base material, comprising the steps of: (a) generating in an input zone, soot-like oxide powders from SiO 2 or GeO 2 raw material from a burning zone (8) so as to produce fine glass powders and injecting these powders in a predetermined direction along a rotating longitudinal travel path; (b) growing with these powders a rod-shaped base material workpiece (24) and detecting the formation of said workpiece by means of an emitted beam to produce a control signal; (c) controlling the forward moving speed of the rod-shaped workpiece in response to the control signal; (d) passing said rod-shaped workpiece through a first heat treating zone to semi-sinter said workpiece, and simultaneously degassing the workpiece of OH components while reducing its volume; and, (e) introducing the semi-sintered workpiece to a second heat treating zone while supporting the workpiece so as to degas the workpiece and transparently vitrifying the workpiece while feeding an inert gas into this second heat treating zone.
Claim 2
Independent Claim
166 words
A method of fabricating an optical glass base material, comprising the steps of: (a) generating in an input zone, soot-like oxide powders from SiO 2 or GeO 2 raw material from a burning zone (8) so as to produce fine glass powders and injecting these powders in a predetermined direction along a rotating longitudinal travel path; (b) growing with these powders a rod-shaped base material workpiece (24) and detecting the formation of said workpiece by means of an emitted beam to produce a control signal; (c) controlling the forward moving speed of the rod-shaped workpiece in response to the control signal; (d) passing said rod-shaped workpiece through a first heat treating zone to semi-sinter said workpiece, and simultaneously degassing the workpiece of OH components while reducing its volume; and, (e) introducing the semi-sintered workpiece to a second heat treating zone while supporting the workpiece so as to degas the workpiece and transparently vitrifying the workpiece while feeding an inert gas into this second heat treating zone.
Claim 3
Dependent Claim
25 words
A method as claimed in claim 1 wherein the semi-sintering temperature in the first heat treating zone is between about 1,000° to about 1,300° C.
Claim 4
Dependent Claim
23 words
A method as claimed in claim 2 wherein the temperature in the second heat treating zone is between about 1,400° and 1,600° C.
Claim 5
Dependent Claim
15 words
A method as claimed in claim 3 wherein said emitted beam is a laser beam.
Claim 6
Dependent Claim
94 words
A method as claimed in claim 4 including the further steps of drawing the workpiece produced in the second heat treating zone through a third heat treating zone with an input and an output side while introducing HCl, Cl 2 , H 2 O and He to the input side while generating fine glass particles on said input so as to form a porous glass layer on the outer periphery of the workpiece to increase the diameter of the workpiece while at the same time introducing Cl 2 and He to the output side.
Claim 7
Independent Claim
173 words
An apparatus for fabricating an optical glass base material comprising in combination: (a) a frame, defining a longitudinal travel path along which fine glass powders are directed to form a workpiece which is to travel along said travel path; (b) a defined input side to said apparatus including feeding means to feed fine glass raw material in soot-like form, and detection means to detect the formation of the workpiece, said input side being a first workstation; (c) belt and pulley support means, at a second workstation, disposed for receiving the workpiece from the first workstation; (d) heating means and rotating means at said second workstation to rotate and heat the workpiece, also gas feed means to feed HCl 2 , Cl 2 , H 2 O, and He in the gas phase on the input side of the second workstation and also gas feed means to feed Cl 2 , and He on the output side of the second workstation; and, (e) drawing means to draw out the workpiece from the second workstation.
Claim 8
Independent Claim
173 words
An apparatus for fabricating an optical glass base material comprising in combination: (a) a frame, defining a longitudinal travel path along which fine glass powders are directed to form a workpiece which is to travel along said travel path; (b) a defined input side to said apparatus including feeding means to feed fine glass raw material in soot-like form, and detection means to detect the formation of the workpiece, said input side being a first workstation; (c) belt and pulley support means, at a second workstation, disposed for receiving the workpiece from the first workstation; (d) heating means and rotating means at said second workstation to rotate and heat the workpiece, also gas feed means to feed HCl 2 , Cl 2 , H 2 O, and He in the gas phase on the input side of the second workstation and also gas feed means to feed Cl 2 , and He on the output side of the second workstation; and, (e) drawing means to draw out the workpiece from the second workstation.
Claim 9
Dependent Claim
78 words
An apparatus as claimed in claim 6 including a third workstation disposed for receiving the workpiece from the drawing means, said third workstation including gas feed means as provided in the second workstation, feeding means to feed fine glass raw material in soot-like form onto the workpiece, rotating means to rotate the workpiece passing through the third workstation and heating means in said third workstation, and, third workstation drawing means to withdraw the finished workpiece as a product.
References Cited (Backward Citations)
US3177057A
Cited
JPS5319036A
Cited
JPS5319034A
Cited
US4202679A
Cited
JPS5546982A
Cited
JPS5792534A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-11-11 | 1989-05-13 | 1989-11-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-11-11 | 1993-05-13 | 1993-11-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-11-11 | 1997-05-13 | 1997-11-12 | $7700.00 | Window Closed / Lapsed |