Thermoplastic molding of sinterable silicon carbide

Claim 2

A thermoplastically moldable ceramic composition consisting essentially of a substantially homogeneous dispersion consisting essentially of from about 40% by volume to about 60% by volume of a sinterable silicon carbide powder having an average particle size which is submicron and which consists essentially of silicon carbide, a boron additive selected from the group consisting of boron and boron carbide in an amount equivalent to from about 0.3% by weight to about 3% by weight of boron based on said silicon carbide, and an amount of a carbonaceous additive selected from the group consisting of free carbon, a carbonaceous organic material and mixtures thereof equivalent to from about 0.1% to about 5% by weight of free carbon based on said silicon carbide, said carbonaceous organic material completely decomposing at a temperature ranging from 50° C. up to 450° C. to said free carbon and gaseous product of decomposition, and from about 40% by volume to about 60% by volume of a binder consisting essentially of an organic acid containing from 12 to 26 carbon atoms per molecule and having a melting point ranging from about 44° C. to about 88° C. and a thermoplastic copolymer of ethylene and from greater than about 12 weight % to about 33 weight % vinyl acetate, said copolymer having a melt index ranging from about 8 to about 43, said organic acid ranging from greater than about 18% by weight up to about 45% by weight of the total weight of said binder.

Claim 3

The ceramic composition of claim 1 wherein said organic acid is stearic acid.

Claim 4

The ceramic composition of claim 1 wherein said vinyl acetate is present in an amount of about 25 weight % and wherein said copolymer has a melt index of about 19.

Claim 5

The ceramic composition of claim 1 wherein said vinyl acetate is present in an amount of about 25 weight % and wherein said copolymer has a melt index of about 19, and said organic acid is stearic acid present in an amount of about 30% by weight of said binder.

Claim 6

The ceramic composition of claim 1 wherein said sinterable silicon carbide powder is present in an amount of about 50% by volume.

Claim 7

A process for producing a sintered polycrystalline silicon carbide body which consists essentially of forming a thermoplastically moldable ceramic composition consisting essentially of a substantially homogeneous dispersion consisting essentially of from about 40% by volume to about 60% by volume of a sinterable silicon carbide powder having an average particle size which is submicron and which consists essentially of silicon carbide, a boron additive selected from the group consisting of boron and boron carbide in an amount equivalent to from about 0.3% by weight to about 3% by weight of boron based on said silicon carbide, and an amount of a carbonaceous additive selected from the group consisting of free carbon, a carbonaceous organic material and mixtures thereof equivalent to from about 0.1% by weight to about 5% by weight of free carbon based on silicon carbide, said carbonaceous organic material completely decomposing at a temperature ranging from 50° C. up to 450° C. to said free carbon and gaseous product of decomposition, and the balance being a binder consisting essentially of an organic acid containing from 12 to 26 carbon atoms per molecule and having a melting point ranging from about 44° C. to about 88° C. and a thermoplastic copolymer of ethylene and from greater than about 12 weight % to about 33 weight % vinyl acetate, said copolymer having a melt index ranging from about 8 to about 43, said organic acid ranging from greater than about 18% by weight up to about 45% by weight of the total weight of said binder, thermoplastically molding said ceramic composition producing a molded body, embedding said molded body in an embedding powder, baking said embedded molded body at a heating rate which has no significant deleterious effect thereon at a temperature ranging up to 450° C. removing said binder leaving no amount therein which would have a significantly deleterious effect on said sintered body, said baking having no significant deleterious effect on said body, said embedding powder having no significantly deleterious effect on said body and being a supporting powder which prevents significant distortion of the body during said baking to remove said binder, recovering the resulting baked body and sintering said baked body at a temperature ranging from about 1900° C. to about 2300° C. producing said sintered body having a density greater than 80% of the theoretical density for silicon carbide.

Claim 8

A process for producing a sintered polycrystalline silicon carbide body which consists essentially of forming a thermoplastically moldable ceramic composition consisting essentially of a substantially homogeneous dispersion consisting essentially of from about 40% by volume to about 60% by volume of a sinterable silicon carbide powder having an average particle size which is submicron and which consists essentially of silicon carbide, a boron additive selected from the group consisting of boron and boron carbide in an amount equivalent to from about 0.3% by weight to about 3% by weight of boron based on said silicon carbide, and an amount of a carbonaceous additive selected from the group consisting of free carbon, a carbonaceous organic material and mixtures thereof equivalent to from about 0.1% by weight to about 5% by weight of free carbon based on silicon carbide, said carbonaceous organic material completely decomposing at a temperature ranging from 50° C. up to 450° C. to said free carbon and gaseous product of decomposition, and the balance being a binder consisting essentially of an organic acid containing from 12 to 26 carbon atoms per molecule and having a melting point ranging from about 44° C. to about 88° C. and a thermoplastic copolymer of ethylene and from greater than about 12 weight % to about 33 weight % vinyl acetate, said copolymer having a melt index ranging from about 8 to about 43, said organic acid ranging from greater than about 18% by weight up to about 45% by weight of the total weight of said binder, thermoplastically molding said ceramic composition producing a molded body, embedding said molded body in an embedding powder, baking said embedded molded body at a heating rate which has no significant deleterious effect thereon at a temperature ranging up to 450° C. removing said binder leaving no amount therein which would have a significantly deleterious effect on said sintered body, said baking having no significant deleterious effect on said body, said embedding powder having no significantly deleterious effect on said body and being a supporting powder which prevents significant distortion of the body during said baking to remove said binder, recovering the resulting baked body and sintering said baked body at a temperature ranging from about 1900° C. to about 2300° C. producing said sintered body having a density greater than 80% of the theoretical density for silicon carbide.

Claim 9

The process according to claim 6 wherein said organic acid is stearic acid.

Claim 10

The process according to claim 6 wherein said vinyl acetate is present in an amount of about 25 weight % and wherein said copolymer has a melt index of about 19.

Claim 11

The process according to claim 6 wherein said vinyl acetate is present in an amount of about 25 weight % and wherein said copolymer has a melt index of about 19, and said organic acid is stearic acid present in an amount of about 30% by weight of said binder.

Claim 12

The process according to claim 6 wherein said sinterable silicon carbide powder is present in an amount of about 50% by volume.

Claim 13

The process according to claim 6 wherein said embedding of said molded body in said embedding powder consists essentially of totally immersing said molded body in said embedding powder.

Claim 14

The process according to claim 6 wherein said embedding powder consists essentially of spherical or nominally spherical particles having a density greater than 80% of the theoretical density for said particles and being selected from the group consisting of polycrystalline silicon carbide, free carbon-coated polycrystalline silicon carbide, free carbon and mixtures thereof.

Claim 15

The process according to claim 6 wherein said thermoplastically molding is injection molding.

Claim 16

The process according to claim 6 wherein said thermoplastically molding is blow molding.

Claim 17

The process according to claim 6 wherein said thermoplastically molding is extrusion molding.

Claim 18

The process according to claim 6 wherein said thermoplastically molding is roll forming.

Claim 19

A blow-molded hollow polycrystalline ceramic body having a density greater than 80% of the theoretical density of silicon carbide consisting essentially of silicon carbide, from about 0.3 part by weight to about 3 parts by weight of boron based on 100 parts by weight of silicon carbide and up to about 5 parts by weight of free carbon based on 100 parts by weight of silicon carbide.

Claim 20

A blow-molded hollow polycrystalline ceramic body having a density greater than 80% of the theoretical density of silicon carbide consisting essentially of silicon carbide, from about 0.3 part by weight to about 3 parts by weight of boron based on 100 parts by weight of silicon carbide and up to about 5 parts by weight of free carbon based on 100 parts by weight of silicon carbide.

Claim 21

A process for producing a thermoplastically molded silicon carbide body which consists essentially of forming a thermoplastically moldable ceramic composition consisting essentially of a substantially homogeneous dispersion consisting essentially of from about 40% by volume to about 60% by volume of a sinterable silicon carbide powder having an average particle size which is submicron and which consists essentially of silicon carbide, a boron additive selected from the group consisting of boron and boron carbide in an amount equivalent to from bout 0.3% by weight to about 3% by weight of boron based on said silicon carbide, and an amount of a carbonaceous additive selected from the group consisting of free carbon, a carbonaceous organic material and mixtures thereof equivalent to from about 0.1% by weight to about 5% by weight of free carbon based on said silicon carbide, said carbonaceous organic material completely decomposing at a temperature ranging from 50° C. up to 450° C. to said free carbon and gaseous product of decomposition, and the balance being a binder consisting essentially of an organic acid containing from 12 to 26 carbon atoms per molecule and having a melting point ranging from about 44° C. to about 88° C. and a thermoplastic copolymer of ethylene and from greater than about 12 weight % to about 33 weight % vinyl acetate, said copolymer having a melt index ranging from about 8 to about 43, said organic acid ranging from greater than about 18% by weight up to about 45% by weight of the total weight of said binder, and thermoplastically molding said ceramic composition producing a molded body.

Claim 22

A process for producing a thermoplastically molded silicon carbide body which consists essentially of forming a thermoplastically moldable ceramic composition consisting essentially of a substantially homogeneous dispersion consisting essentially of from about 40% by volume to about 60% by volume of a sinterable silicon carbide powder having an average particle size which is submicron and which consists essentially of silicon carbide, a boron additive selected from the group consisting of boron and boron carbide in an amount equivalent to from bout 0.3% by weight to about 3% by weight of boron based on said silicon carbide, and an amount of a carbonaceous additive selected from the group consisting of free carbon, a carbonaceous organic material and mixtures thereof equivalent to from about 0.1% by weight to about 5% by weight of free carbon based on said silicon carbide, said carbonaceous organic material completely decomposing at a temperature ranging from 50° C. up to 450° C. to said free carbon and gaseous product of decomposition, and the balance being a binder consisting essentially of an organic acid containing from 12 to 26 carbon atoms per molecule and having a melting point ranging from about 44° C. to about 88° C. and a thermoplastic copolymer of ethylene and from greater than about 12 weight % to about 33 weight % vinyl acetate, said copolymer having a melt index ranging from about 8 to about 43, said organic acid ranging from greater than about 18% by weight up to about 45% by weight of the total weight of said binder, and thermoplastically molding said ceramic composition producing a molded body.

Claim 23

The process according to claim 18 wherein said organic acid is stearic acid.

Claim 24

The process according to claim 18 wherein said vinly acetate is present in an amount of about 25% by weight and wherein said copolymer has a melt index of about 19.

Claim 25

The process according to claim 18 wherein said vinly acetate is present in an amount of about 25% by weight and wherein said copolymer has a melt index of about 19, and said organic acid is stearic acid present in an amount of about 30% by weight of said binder.

Claim 26

The process according to claim 18 wherein said sinterable silicon carbide powder is present in an amount of about 50% by volume.

Claim 27

The process according to claim 18 wherein said thermoplastically molding is injection molding.

Claim 28

The process according to claim 18 wherein said thermoplastically molding is blow molding.

Claim 29

The process according to claim 18 wherein said thermoplastically molding is extrusion molding.

Claim 30

The process according to claim 18 wherein said thermoplastically molding is roll forming.