Ammonia contacting to passivate metals deposited on a cracking catalyst during reduced crude processing
Assignee: Ashland LLC
•
Filing: 1983-08-08
•
Granted: 1985-11-05
•
Expires: 2003-08-08
Abstract
Abstract Contaminating metals including nickel, vanadium, iron and copper are deposited on a fluid cracking catalyst during the processing of carbo-metallic containing oils such as residual oils, reduced crudes or topped crudes. These contaminating metals lead to undesirous side reactions such as dehydrogenation, coking and methyl group removal which adversely affect conversion and gasoline selectively. Furthermore vanadia deactivates the crystalline zeolite component of the catalyst in addition to causing catalyst agglomeration because of its pentoxide melting point by treatment with a reducing gas such as ammonia. The ammonia is added as ammonia or in the presence of diluents such as nitrogen, carbon dioxide, flue gas, fuel gas and steam. The reaction of ammonia with vanadium produces vanadium nitride which is water insoluble and facilitates the disposal of high vanadium containing spent of deactivated catalyst by landfill techniques.
Inventors
- 👤 Stephen M. Kovach
- 👤 James L. Palmer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 08:32
CPC Classifications
C; C10; C10G; C10G11/00; C10G11/14; C10G11/18; B; B01; B01J; B01J29/00; B01J29/90; C10G11/02; C10G11/04; C10G11/05; C10G2300/00; C10G2300/70; C10G2300/705; Y; Y02; Y02P; Y02P30/00; Y02P30/40; Y10; Y10S; Y10S502/00; Y10S502/521
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
80 words
A process for passivating metal contaminants of an equilibrium zeolite fluid cracking catalyst containing vanadium and nickel contaminants which arise from use of said catalyst in continuous fluid catalytic cracking of a carbometallic heavy hydrocarbon oil feed, said process comprising contacting said catalyst, after regeneration thereof, with ammonia in an amount sufficient to convert at least a portion of said contaminant metals from an oxide form to nitrides and reusing the passivated catalyst in a continuous fluid catalytic cracking process.
Claim 2
Dependent Claim
80 words
A process for passivating metal contaminants of an equilibrium zeolite fluid cracking catalyst containing vanadium and nickel contaminants which arise from use of said catalyst in continuous fluid catalytic cracking of a carbometallic heavy hydrocarbon oil feed, said process comprising contacting said catalyst, after regeneration thereof, with ammonia in an amount sufficient to convert at least a portion of said contaminant metals from an oxide form to nitrides and reusing the passivated catalyst in a continuous fluid catalytic cracking process.
Claim 3
Dependent Claim
30 words
Process according to claim 1 in which the amount of ammonia employed is in the range of from about 1000 ppm to 20,000 ppm, based on nitrogen in said ammonia.
Claim 4
Dependent Claim
26 words
Process according to claim 1 in which the regenerated catalyst is contacted with ammonia at a temperature in the range of 1000° F. to 1500° F.
Claim 5
Dependent Claim
24 words
The process of claim 1 wherein said equilibrium zeolite fluid cracking catalyst contains at least 1000 ppm vanadium and nickel contaminants, calculated as metals.
Claim 6
Dependent Claim
154 words
A process for fluid catalytic cracking comprising the sequential steps of: (a) cracking in a hydrocarbon conversion zone a hydrocarbon feed containing at least 5 ppm metals as nickel and vanadium and having a Conradson carbon of at least 2 wt.% in the presence of equilibrium zeolite cracking catalyst containing at least 1000 ppm vanadium and nickel contaminants, (b) separting vaporous hydrocarbon conversion products to yield a coked catalyst, (c) regenerating said coked catalyst in a regeneration zone at conditions sufficient to remove at least a portion of any carbonaceous deposits whereby the metal contaminants are converted to an oxide form to produce a regenerated catalyst, (d) stripping said regenerated catalyst to remove occluded regeneration gases, (e) contacting the stripped catalyst in a passivation zone with ammonia in an amount sufficient to convert vanadium pentoxide to vanadium nitride to form a passivated catalyst, and (f) recycling said passivated catalyst to said hydrocarbon conversion zone.
Claim 7
Dependent Claim
154 words
A process for fluid catalytic cracking comprising the sequential steps of: (a) cracking in a hydrocarbon conversion zone a hydrocarbon feed containing at least 5 ppm metals as nickel and vanadium and having a Conradson carbon of at least 2 wt.% in the presence of equilibrium zeolite cracking catalyst containing at least 1000 ppm vanadium and nickel contaminants, (b) separting vaporous hydrocarbon conversion products to yield a coked catalyst, (c) regenerating said coked catalyst in a regeneration zone at conditions sufficient to remove at least a portion of any carbonaceous deposits whereby the metal contaminants are converted to an oxide form to produce a regenerated catalyst, (d) stripping said regenerated catalyst to remove occluded regeneration gases, (e) contacting the stripped catalyst in a passivation zone with ammonia in an amount sufficient to convert vanadium pentoxide to vanadium nitride to form a passivated catalyst, and (f) recycling said passivated catalyst to said hydrocarbon conversion zone.
Claim 8
Dependent Claim
23 words
Process according to claim 5 in which coked catalyst is regenerated at a temperature in the range of 1275° F. to 1450° F.
Claim 9
Dependent Claim
30 words
The method of claim 5 wherein regenerated catalyst is withdrawn by a standpipe zone communicating with said regeneration zone and said withdrawn catalyst is contacted with ammonia in said standpipe.
Claim 10
Dependent Claim
29 words
The method of claim 5 wherein the regenerated catalyst is contacted with ammonia under conditions to convert at least a portion of vanadia and iron oxides to nitrides thereof.
Claim 11
Dependent Claim
47 words
The method of claim 5 wherein said hydrocarbon feed is selected from whole crude oils, atmospheric and/or vacuum gas oils, topped crudes, reduced crudes, residual oils, reduced crudes, coal-derived oils, shale oils, waxes, untreated or deasphalted residia and blends thereof comprising from 1 to 5 ppm vanadium.
Claim 12
Dependent Claim
24 words
The method of claim 5 wherein the weight ratio of vanadium to nickel in the feed is in the range of 1:3 to 5:1.
Claim 13
Dependent Claim
30 words
The method of claim 5 wherein the hydrocarbon feed comprises 70% or more of 650° F. plus material and greater than 20% thereof boils above 1025° F. at atmospheric pressure.
Claim 14
Dependent Claim
135 words
A process for fluid catalytic cracking comprising the steps of: (a) cracking in a hydrocarbon conversion zone a carbometallic hydrocarbon feed at a pressure of about 10-50 psia and at temperatures of about 925° F.-1050° F. in the presence of a zeolite catalyst contaminated with vanadium compounds, (b) regenerating coked catalyst at conditions wherein vanadium pentoxides are produced, (c) passing the regenerated catalyst to a stripping zone and stripping entrained oxygen containing gas from the catalyst, (d) contacting the stripped catalyst with ammonia to convert vanadium pentoxides to vanadium nitride and thereby to passivate said catalyst, (e) removing a minor portion of the passivated catalyst containing at least 1000 ppm vanadium from the cracking process for disposal in a landfill and (f) recycling a major portion of the passivated catalyst to said hydrocarbon conversion zone.
Claim 15
Dependent Claim
135 words
A process for fluid catalytic cracking comprising the steps of: (a) cracking in a hydrocarbon conversion zone a carbometallic hydrocarbon feed at a pressure of about 10-50 psia and at temperatures of about 925° F.-1050° F. in the presence of a zeolite catalyst contaminated with vanadium compounds, (b) regenerating coked catalyst at conditions wherein vanadium pentoxides are produced, (c) passing the regenerated catalyst to a stripping zone and stripping entrained oxygen containing gas from the catalyst, (d) contacting the stripped catalyst with ammonia to convert vanadium pentoxides to vanadium nitride and thereby to passivate said catalyst, (e) removing a minor portion of the passivated catalyst containing at least 1000 ppm vanadium from the cracking process for disposal in a landfill and (f) recycling a major portion of the passivated catalyst to said hydrocarbon conversion zone.
Claim 16
Dependent Claim
26 words
The process of claim 12, wherein the minor portion of the passivated catalyst contains from about 5000 to 20,000 ppm nickel and vanadium, calculated as metals.
Claim 17
Dependent Claim
24 words
The method of claim 1 wherein regeneration of the catalyst is accomplished at a temperature in the range of 1275° F. to 1450° F.
References Cited (Backward Citations)
US1931550A
Cited
US2225782A
Cited
US2412868A
Cited
US2758958A
Cited
US4268416A
Cited
US4268188A
Cited
US4280895A
Cited
US4280896A
Cited
US4348273A
Cited
US4417975A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-11-04 | 1989-05-06 | 1989-11-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-11-04 | 1993-05-06 | 1993-11-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-11-04 | 1997-05-06 | 1997-11-05 | $7700.00 | Window Closed / Lapsed |