Process for producing deep-drawing cold rolled steel sheets and strips
Assignee: Nippon Steel Corp
•
Filing: 1982-10-27
•
Granted: 1985-11-05
•
Expires: 2002-10-27
Abstract
Abstract Disclosed is a process for producing titanium-containing cold rolled steel sheets and strips which can stand very severe press forming, which process comprising hot rolling, coiling at a temperature not lower than 700 DEG C., cold rolling and continuous annealing at a temperature, from 700 DEG to 900 DEG C., for 20 seconds to 2 minutes.
Inventors
- 👤 Osamu Akisue
- 👤 Teruaki Yamada
- 👤 Shigeru Ueda
- 👤 Yoshikuni Tokunaga
- 👤 Masato Yamada
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 07:11
CPC Classifications
C; C22; C22C; C22C38/00; C22C38/14; C21; C21D; C21D8/00; C21D8/02; C21D8/04; C21D8/0421; C21D8/0426; C21D8/0436
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
97 words
A process for producing deep-drawing cold rolled steel strips, comprising: hot rolling a steel consisting essentially of 0.0014-0.0031% carbon, 0.010-0.100% aluminum and titanium in amounts not less than 4 times the carbon content, but within a range of from 0.019-0.052%, 0.0019-0.0038% nitrogen with the balance being iron and unavoidable impurities; coiling the hot rolled strip thus obtained at a temperature not lower than 700° C.; and subjecting the coiled strip to cold rolling and then continuous annealing including a soaking step in a temperature range of from 700° to 900° C. for 20 seconds to 2 minutes.
Claim 2
Dependent Claim
97 words
A process for producing deep-drawing cold rolled steel strips, comprising: hot rolling a steel consisting essentially of 0.0014-0.0031% carbon, 0.010-0.100% aluminum and titanium in amounts not less than 4 times the carbon content, but within a range of from 0.019-0.052%, 0.0019-0.0038% nitrogen with the balance being iron and unavoidable impurities; coiling the hot rolled strip thus obtained at a temperature not lower than 700° C.; and subjecting the coiled strip to cold rolling and then continuous annealing including a soaking step in a temperature range of from 700° to 900° C. for 20 seconds to 2 minutes.
Claim 3
Dependent Claim
21 words
A process according to claim 1 in which the cold rolling is done with a reduction ranging from 70 to 85%.
Claim 4
Dependent Claim
41 words
A process according to claim 1 in which the coiling of the hot rolled steel strip is done at an ordinary temperature and the strip thus coiled is reheated to a temperature not lower than 700° C. in a separate line.
Claim 5
Dependent Claim
18 words
A process according to claim 1 wherein the titanium is not less than 6.3 times the carbon content.
Claim 6
Dependent Claim
17 words
A process according to claim 4 wherein the titanium is 6.3 to 37.1 times the carbon content.
References Cited (Backward Citations)
US3988173A
Cited
US4145235A
Cited
DE2603097A1
Cited
JPS53137021A
Cited
JPS54104417A
Cited
JPS5524952A
Cited
JPS55107732A
Cited
JPS563656A
Cited
JPS5669358A
Cited
US4331488A
Cited
JPS5662926A
Cited
FR2480311A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-11-04 | 1989-05-06 | 1989-11-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-11-04 | 1993-05-06 | 1993-11-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-11-04 | 1997-05-06 | 1997-11-05 | $7700.00 | Window Closed / Lapsed |