Process for the production of propylene block copolymers by a three step method
Assignee: Idemitsu Petrochemical Co Ltd
•
Filing: 1983-12-08
•
Granted: 1985-10-29
•
Expires: 2003-12-08
Abstract
Abstract A process for producing a propylene block copolymer by a three-step reaction in the presence of a stereoregular catalyst. At the first step, propylene is polymerized at a temperature of 55° C. or more to form polypropylene having an intrinsic viscosity of from 0.5 to 3.5 in the prescribed amount. At the second step, propylene is polymerized at a temperature of from 30° to 90° C. to form polypropylene having an intrinsic viscosity of at least 4 in the prescribed amount. And at the third step, ethylene and propylene are copolymerized at a temperature of from 30° to 90° C. to form an ethylene-propylene copolymer having an intrinsic viscosity of at least three in the prescribed amount. The propylene block copolymer formed by the three steps is superior and well balanced in impact resistance and stiffness.
Inventors
- 👤 Toshikazu Kasahara
- 👤 Tsutomu Nishikawa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 19:04
CPC Classifications
C; C08; C08F; C08F297/00; C08F297/06; C08F297/08; C08F297/083; C08F297/086
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
188 words
A process for producing a propylene block copolymer by a three-step reaction in the presence of a stereo-regular catalyst, which comprises: (1) polymerizing propylene at a temperature of 55° C. or more to form polypropylene having an intrinsic viscosity of from 0.5 to 3.5 in an amount of from 50 to 94% by weight based on the total amount of the final propylene block copolymer formed during this three-step reaction; (2) polymerizing propylene at a temperature of from 30° to 90° C. to form polypropylene in an amount of from 25 to 3% by weight based on the total amount of the final propylene block copolymer formed during this three-step reaction, the polypropylene formed during this second step having an intrinsic viscosity of at least 4; and (3) copolymerizing ethylene and propylene at a temperature of from 30° to 90° C. to form an ethylene-propylene copolymer in an amount of from 25 to 3% by weight based on the total amount of the final propylene block copolymer formed during this three-step reaction, the ethylene-propylene copolymer formed during this third step having an intrinsic viscosity of at least 3.
Claim 2
Dependent Claim
188 words
A process for producing a propylene block copolymer by a three-step reaction in the presence of a stereo-regular catalyst, which comprises: (1) polymerizing propylene at a temperature of 55° C. or more to form polypropylene having an intrinsic viscosity of from 0.5 to 3.5 in an amount of from 50 to 94% by weight based on the total amount of the final propylene block copolymer formed during this three-step reaction; (2) polymerizing propylene at a temperature of from 30° to 90° C. to form polypropylene in an amount of from 25 to 3% by weight based on the total amount of the final propylene block copolymer formed during this three-step reaction, the polypropylene formed during this second step having an intrinsic viscosity of at least 4; and (3) copolymerizing ethylene and propylene at a temperature of from 30° to 90° C. to form an ethylene-propylene copolymer in an amount of from 25 to 3% by weight based on the total amount of the final propylene block copolymer formed during this three-step reaction, the ethylene-propylene copolymer formed during this third step having an intrinsic viscosity of at least 3.
Claim 3
Dependent Claim
21 words
The process of claim 1, wherein the stereoregular catalyst comprises a transition metal halogen compound component and an organoaluminum compound component.
Claim 4
Dependent Claim
56 words
The process of claim 1, wherein at the first step, propylene is polymerized at a temperature of from 61° to 70° C. to form polypropylene having an intrinsic viscosity of from 0.7 to 3.0 in an amount of from 70 to 90% by weight based on the total amount of the propylene block copolymer formed finally.
Claim 5
Dependent Claim
55 words
The process of claim 1, wherein at the second step, propylene is polymerized at a temperature of from 40° to 70° C. to form polypropylene having an intrinsic viscosity of from 4.5 to 7.5 in amount of from 15 to 5% by weight based on the total amount of the propylene block copolymer formed finally.
Claim 6
Dependent Claim
60 words
The process of claim 1, wherein at the third step, ethylene and propylene are copolymerized at a temperature of from 40° to 70° C. to form an ethylene-propylene copolymer having an intrinsic viscosity of from 4 to 12 in an amount of from 18 to 5% by weight based on the total amount of the propylene block copolymer formed finally.
Claim 7
Dependent Claim
29 words
The process of claim 1, wherein the ethylene-unit content of the ethylene-propylene copolymer formed at the third step is within the range of from 1 to 10% by weight.
Claim 8
Dependent Claim
29 words
The process of claim 5, wherein the ethylene-unit content of the ethylene-propylene copolymer formed at the third step is within the range of from 1 to 10% by weight.
Claim 9
Dependent Claim
175 words
The process of claim 1, wherein at the first step, propylene is polymerized at a temperature of from 61° to 70° C. to form polypropylene having an intrinsic viscosity of from 0.7 to 3.0 in an amount of from 70 to 90% by weight based on the total amount of the final propylene block copolymer formed during this three-step reaction; wherein at the second step, propylene is polymerized at a temperature of from 40° to 70° C. to form polypropylene having an intrinsic viscosity of from 4.5 to 7.5 in an amount of from 15 to 5% by weight based on the total amount of the final propylene block copolymer formed during this three-step reaction; and wherein at the third step, ethylene and propylene are copolymerized at a temperature of from 40° to 70° C. to form an ethylene-propylene copolymer having an intrinsic viscosity of from 4 to 12 in an amount of from 18 to 5% by weight based on the total amount of the final propylene block copolymer formed during this three-step reaction.
Claim 10
Dependent Claim
29 words
The process of claim 8, wherein the ethylene-unit content of the ethylene-propylene copolymer formed at the third step is within the range of from 2 to 8% by weight.
Claim 11
Dependent Claim
21 words
The process of claim 9, wherein said stereoregular catalyst comprises a transition metal halogen compound component and an organoaluminum compound component.
Claim 12
Dependent Claim
29 words
The process of claim 8, wherein the ethylene-unit content of the ethylene-propylene copolymer formed at the third step is within the range of from 1 to 10% by weight.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-10-28 | 1989-04-29 | 1989-10-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-10-28 | 1993-04-29 | 1993-10-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-10-28 | 1997-04-29 | 1997-10-29 | $7700.00 | Window Closed / Lapsed |