US4549891A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for forming a non-symmetrical optical fiber
Assignee: Viavi Solutions Inc
•
Filing: 1984-02-23
•
Granted: 1985-10-29
•
Expires: 2004-02-23
Abstract
Abstract A method of preparing an optical fiber includes the steps of applying a first cladding layer of a sinterable, glasseous particulate matter providing a selected index of refraction to a support surface, forming at least one longitudinally-extending groove in the layer prior to sintering, applying a deposit of glasseous particulate matter in said groove to ultimately define a core stripe having an index of refraction greater than that of the previously applied layer, applying a covering layer of glasseous particulate matter, sintering the various layers and the core strip to provide an optical fiber preform, and drawing the preform to provide an optical fiber having a rotationally non-symmetric characteristics with a core of higher index of refraction than the surrounding cladding.
Inventors
- 👤 William T. Plummer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 10:52
CPC Classifications
C; C03; C03B; C03B37/00; C03B37/01; C03B37/012; C03B37/014; C03B37/018; C03B37/01205; C03B2203/00; C03B2203/32
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
183 words
A method for forming an optical fiber preform for drawing to an optical fiber, said method comprising the steps of: forming an elongated support blank; applying a first layer of glasseous material to at least a portion of a given surface of said blank as an unsintered, soot glass layer which (1) is sinterable to a hard glass layer of given index of refraction suitable as a cladding layer and (2) is easily machineable as compared to its sintered form; machining a groove in said unsintered layer; depositing glasseous soot material within said groove and ultimately providing a core strip of hard glass material having an index of refraction higher than that of said first layer; applying a second layer of glasseous material over said first layer and said core stripe to provide a cladding layer of hard glass material having an index of refraction lower than that of said core stripe; and heating the structure at one or more stages following the step of machining said groove to sinter said first layer to a hard glass layer, to provide an optical preform.
Claim 2
Independent Claim
183 words
A method for forming an optical fiber preform for drawing to an optical fiber, said method comprising the steps of: forming an elongated support blank; applying a first layer of glasseous material to at least a portion of a given surface of said blank as an unsintered, soot glass layer which (1) is sinterable to a hard glass layer of given index of refraction suitable as a cladding layer and (2) is easily machineable as compared to its sintered form; machining a groove in said unsintered layer; depositing glasseous soot material within said groove and ultimately providing a core strip of hard glass material having an index of refraction higher than that of said first layer; applying a second layer of glasseous material over said first layer and said core stripe to provide a cladding layer of hard glass material having an index of refraction lower than that of said core stripe; and heating the structure at one or more stages following the step of machining said groove to sinter said first layer to a hard glass layer, to provide an optical preform.
Claim 3
Dependent Claim
21 words
The method of claim 1 wherein said forming step includes providing said given surface of said blank as a flat surface.
Claim 4
Dependent Claim
18 words
The method of claim 1 wherein at least said first glasseous layer is applied by chemical vapor deposition.
Claim 5
Dependent Claim
18 words
The method of claim 1 wherein the glasseous material deposited in the groove is applied by flame hydrolysis.
Claim 6
Dependent Claim
43 words
The method of claim 1 wherein said second layer covers the entire exterior surface of said glass blank and said first layer, and said second layer has a thermal coefficient of expansion different from that of said glass blank and said first layer.
Claim 7
Dependent Claim
27 words
The method of claim 5 wherein the thermal coefficient of expansion of said second layer is lower than that of said glass preform and said first layer.
Claim 8
Dependent Claim
53 words
The method of claim 1 including the step of forming, before said applying step, a second groove in said first layer spaced from said first mentioned groove, to form a pair of grooves therein, and said depositing step includes depositing glasseous material in both said grooves to provide a pair of core stripes.
Claim 9
Dependent Claim
11 words
The method of claim 7 wherein said grooves are substantially parallel.
Claim 10
Dependent Claim
58 words
The method of claim 1 including, when forming said groove, forming two more adjoining grooves in said first layer, depositing said material forming said core stripe in the middle one of said grooves and depositing in the others of said grooves glasseous material having a coefficient of thermal expansion higher than that of the material of said core.
Claim 11
Dependent Claim
109 words
The method of claim 1 wherein said depositing step includes depositing said glasseous material in said groove as an unsintered, glass soot stripe which is sinterable to a hard glass stripe and which is easily machinable as compared to its sintered form, said depositing step further including depositing said glasseous material to a thickness exceeding the depth of said groove, and said method further including removing the machinable material which exceeds the depth of said groove, and said heating step includes heating the structure at one or more stages following said step of removing the machinable material so as to sinter said particulate stripe to a hard glass stripe.
Claim 12
Dependent Claim
59 words
The method of claim 10 wherein said step of applying said second layer includes depositing unsintered, particulate material which is sinterable to a hard glass layer, and said heating step includes heating the structure at one or more stages following the step of applying said second layer so as to sinter said second layer to a hard glass layer.
References Cited (Backward Citations)
US3216807A
Cited
US3659916A
Cited
US3806223A
Cited
US3980461A
Cited
US4145457A
Cited
US4019051A
Cited
US4089584A
Cited
US4315666A
Cited
US4388800A
Cited
JPS57173814A
Cited
US4428761A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-10-28 | 1989-04-29 | 1989-10-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-10-28 | 1993-04-29 | 1993-10-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-10-28 | 1997-04-29 | 1997-10-29 | $7700.00 | Window Closed / Lapsed |