US4549064A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Laser treatment of silicon nitride
Assignee: National Semiconductor Corp
•
Filing: 1983-04-05
•
Granted: 1985-10-22
•
Expires: 2003-04-05
Abstract
Abstract An argon-fluorine (ArF) excimer laser is used to selectively heat various Si3N4 materials used in the manufacture of semiconductor devices to elevated temperatures while maintaining active device regions and electrical interconnects at relatively low temperatures, to, for example, anneal the structural layer, induce compositional changes or densification and/or flow of the silicon nitride-based material to round off sharp edges and stops, all without damaging or appreciably affecting the active regions and electrical interconnects of a semiconductor device.
Inventors
- 👤 Michelangelo Delfino
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 02:32
CPC Classifications
H; H10; H10P; H10P95/00; H10P34/00; H10P34/40; H10P34/42
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
100 words
The method of inducing annealing, flow or densification in a silicon nitride portion of a semiconductor device structure covered at least partly by other portions of said device made of other non-silicon nitride materials, wherein annealing, flow or densification is induced on said silicon nitride portion upon application of heat thereto, comprising applying a laser beam to said silicon nitride portion wherein said laser beam is an ArF excimer laser beam having an emission wavelength which is approximately equal to the wavelength most absorbed by the silicon nitride portion and not of a wavelength most absorbed by said other portions.
Claim 2
Independent Claim
100 words
The method of inducing annealing, flow or densification in a silicon nitride portion of a semiconductor device structure covered at least partly by other portions of said device made of other non-silicon nitride materials, wherein annealing, flow or densification is induced on said silicon nitride portion upon application of heat thereto, comprising applying a laser beam to said silicon nitride portion wherein said laser beam is an ArF excimer laser beam having an emission wavelength which is approximately equal to the wavelength most absorbed by the silicon nitride portion and not of a wavelength most absorbed by said other portions.
Claim 3
Dependent Claim
16 words
The method of claim 1 in which said beam is applied as a repetitively pulsed beam.
Claim 4
Dependent Claim
16 words
The method of claim 1 in which said laser beam has a wavelength of 193 nm.
Claim 5
Dependent Claim
14 words
The method of claim 1 in which said semiconductor device structure is a transistor.
Claim 6
Dependent Claim
30 words
The method of claim 1 in which said other portions are either transparent to said beam or are of high reflectivity so as to preclude absorption coupling with said beam.
Claim 7
Dependent Claim
16 words
The method of claim 5 in which said other portions are silicon oxide, silicon and aluminum.
Claim 8
Dependent Claim
26 words
The method of claim 1 in which said beam is applied in the form of intermittent pulses of from 0.1 to 10 joules of discharge energy.
Claim 9
Dependent Claim
28 words
The method of claim 1 in which said laser beam is generated by an excimer laser powered at a repetition rate of from about 1 to 100 Hz.
Claim 10
Dependent Claim
17 words
The method of claim 1 wherein said other portions are heated to less than about 1100° C.
Claim 11
Dependent Claim
23 words
The method of claim 1 in which said silicon nitride is (Si 3 N 4 ) x (SiO 2 ) x-1 where x>0.9.
Claim 12
Dependent Claim
50 words
The method of claim 1 including depositing said silicon nitride portion on a substrate; depositing on said silicon nitride portion a non-silicon nitride material which largely transmits radiation from said ArF excimer laser beam; and then applying said laser beam to said silicon nitride portion through said non-silicon nitride material.
Claim 13
Dependent Claim
50 words
The method of claim 1 including depositing said silicon nitride portion on a substrate; depositing on said silicon nitride portion a non-silicon nitride material which largely reflects radiation from said ArF excimer laser beam; and then applying said laser beam to said silicon nitride portion adjacent said non-silicon nitride material.
Claim 14
Dependent Claim
51 words
The method of claim 1 including depositing said silicon nitride portion on a substrate; depositing on said silicon nitride portion non-silicon nitride materials which largely transmit or reflect radiation from said ArF excimer laser beam; and then applying said laser beam to said silicon nitride portion adjacent said non-silicon nitride material.
References Cited (Backward Citations)
US4341569A
Cited
JPS5646523A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-10-21 | 1989-04-22 | 1989-10-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-10-21 | 1993-04-22 | 1993-10-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-10-21 | 1997-04-22 | 1997-10-22 | $7700.00 | Window Closed / Lapsed |