Thermosetting powder lacquer for covering weld seams
Assignee: VERNICOLOR AG A CORP OF SWITZERLAND
•
Filing: 1984-03-05
•
Granted: 1985-10-22
•
Expires: 2004-03-05
Abstract
Abstract The thermosetting powder lacquer is suited for covering the weld seams in metal containers for foodstuffs or beverages and comprises a mixture of at least two aromatic epoxide resins, a first component of which contains a maximum of two epoxide groups per molecule on the average and a second component of which contains more than two epoxide groups per molecule on the average, a hardener and a catalyst. As a hardener there is used a condensation product formed from the diglycidylether of bisphenol-A and bisphenol-A and as a catalyst dimethylaminophenol is used.
Inventors
- 👤 Hans R. Widmer
- 👤 Christian Schmid
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 04:13
CPC Classifications
C; C08; C08G; C08G59/00; C08G59/18; C08G59/20; C08G59/32; C08G59/38; C08G59/182; C08G59/40; C09; C09D; C09D163/00; Y; Y10; Y10T; Y10T428/00; Y10T428/13; Y10T428/1352; Y10T428/1355
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
100 words
A thermosetting powder lacquer on an epoxide resin basis essentially consisting of: a mixture of polymeric aromatic epoxide resins comprising at least two components a first of which contains a maximum of two epoxide groups per molecule on the average and a second of which contains more than two epoxide groups per molecule on the average; a hardener selected from the group consisting of: (i) condensation product of diglycidylether of bisphenol-A and bisphenol-A; (ii) polyester made of trimellitic acid anhydride and aliphatic polyol and containing free carboxylic acid groups; (iii) phenolic resin; or (iv) a mixture thereof; and a catalyst.
Claim 2
Dependent Claim
100 words
A thermosetting powder lacquer on an epoxide resin basis essentially consisting of: a mixture of polymeric aromatic epoxide resins comprising at least two components a first of which contains a maximum of two epoxide groups per molecule on the average and a second of which contains more than two epoxide groups per molecule on the average; a hardener selected from the group consisting of: (i) condensation product of diglycidylether of bisphenol-A and bisphenol-A; (ii) polyester made of trimellitic acid anhydride and aliphatic polyol and containing free carboxylic acid groups; (iii) phenolic resin; or (iv) a mixture thereof; and a catalyst.
Claim 3
Dependent Claim
30 words
The powder lacquer as defined in claim 1, wherein: said first component of said aromatic epoxide resin mixture has an epoxide equivalent weight in the range of 500 to 20,000.
Claim 4
Dependent Claim
30 words
The powder lacquer as defined in claim 2, wherein: said first component of said aromatic epoxide resin mixture has an epoxide equivalent weight in the range of 800 to 3,000.
Claim 5
Dependent Claim
35 words
The powder lacquer as defined in claim 1, wherein: said second component of said aromatic epoxide resin mixture comprises an epoxidized novolac resin having an epoxide equivalent weight in the range of 150 to 220.
Claim 6
Dependent Claim
34 words
The powder lacquer as defined in claim 4, wherein: said epoxidized novolac resin is present in an amount in the range of 5 to 15 percent by weight of the aromatic epoxide resin mixture.
Claim 7
Dependent Claim
48 words
The powder lacquer as defined in claim 1, wherein: said hardener prepared as a condensation product of the diglycidylether of bisphenol-A and bisphenol-A is formed from the diglycidylether of bisphenol-A and bisphenol-A in a weight ratio having a value in the range of 0.5 to less than 1.5.
Claim 8
Dependent Claim
76 words
The powder lacquer as defined in claim 6, wherein: said hardener forming a condensation product of the diglycidylether of bisphenol-A and bisphenol-A in a weight ratio in the range of 0.5 to 1.5 has an equivalent weight in the range of 220 to 280 with respect to phenolic hydroxyl groups, a viscosity in the range of 50 to 1,000 mPas at a temperature of 150° C. and a melting range of 40° C. to 100° C.
Claim 9
Dependent Claim
49 words
The powder lacquer as defined in claim 6, wherein: said aromatic epoxide resin mixture and the condensation product forming the hardener are present in an amount in the range of 72 to 73 and in the range of 25 to 27 percent by weight, respectively, of the powder lacquer.
Claim 10
Dependent Claim
35 words
The powder lacquer as defined in claim 1, wherein: said catalyst is selected from the group: imidazole, 2-methyl imidazole, ethyltriphenylphosphoniumchloride or another salt thereof, aluminum acetylacetonate, primary, secondary or tertiary aminophenol, toluene sulfonic acid salt.
Claim 11
Dependent Claim
25 words
The powder lacquer as defined in claim 1, wherein: said powder lacquer has a softening point in the range of 65° C. to 100° C.
Claim 12
Dependent Claim
19 words
The powder lacquer as defined in claim 1, wherein: said powder lacquer has a long shelf-life at environmental temperature.
Claim 13
Dependent Claim
34 words
The powder lacquer as defined in claim 1, wherein: said powder lacquer is curable at temperatures at or above 200° C. in a very short period of time to form a flexible thermoset lacquer.
Claim 14
Dependent Claim
32 words
The powder lacquer as defined in claim 12, wherein: said powder lacquer is curable at a temperature in the range of 230° C. to 350° C. to form a flexible thermoset lacquer.
Claim 15
Dependent Claim
32 words
The powder lacquer as defined in claim 12, wherein: said powder lacquer is curable in a time period in the range of 3 to 20 seconds to form a flexible thermoset lacquer.
Claim 16
Dependent Claim
17 words
The powder lacquer as defined in claim 1, wherein: said powder lacquer has a wide curing window.
Claim 17
Dependent Claim
32 words
The powder lacquer as defined in claim 1, wherein: said powder lacquer contains an additive selected from the group: leveling agent, pourability assisting agent, pigment, filler, thickening agent, or a mixture thereof.
Claim 18
Dependent Claim
26 words
The powder lacquer as defined in claim 16, wherein: said filler is present in a maximum amount of 30 percent by weight of the powder lacquer.
References Cited (Backward Citations)
US3367990A
Cited
DE2130607A1
Cited
US3932343A
Cited
US4169187A
Cited
GB2055843A
Cited
US4440914A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-10-21 | 1989-04-22 | 1989-10-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-10-21 | 1993-04-22 | 1993-10-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-10-21 | 1997-04-22 | 1997-10-22 | $7700.00 | Window Closed / Lapsed |