US4548682A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process of producing magnetic recording media
Assignee: Nippon Light Metal Co Ltd
•
Filing: 1984-06-08
•
Granted: 1985-10-22
•
Expires: 2004-06-08
Abstract
Abstract A magnetic recording medium having excellent magnetic properties and a uniform recording envelope suitable for, in particular, high-density recording is obtained by packing a magnetic substance in the micro pores of anodic oxide film formed on an aluminum substrate by subjecting the same to an anodic oxidation treatment to produce an anodic oxide film having a thickness of at least 4 μm. The recording medium can be improved by immersing the anodized aluminum substrate in an acid or alkali bath to chemically dissolve a part of the anodic oxide film, and thereby enlarge the micro pores in the anodic oxide film to a pore diameter in the range of 300 Å to 1,400 Å, optionally applying an electric current to the aluminum substrate in the immersion bath if necessary to control the thickness of the barrier layer in the anodic oxide film, before subjecting the treated substrate to an electrolytic treatment in a bath containing ions of a magnetic substance to deposit the magnetic substance in the enlarged micro pores. Thereafter, the surface of the anodic oxide film, and any excess deposited magnetic material thereon, is physically ground to expose the packed magnetic substance at the surface of the film.
Inventors
- 👤 Koichi Yoshida
- 👤 Yoshio Hirayama
- 👤 Yasuo Oka
- 👤 Takashi Kajiyama
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 15:52
CPC Classifications
C; C25; C25D; C25D11/00; C25D11/02; C25D11/04; C25D11/18; G; G11; G11B; G11B5/00; G11B5/84; Y; Y10; Y10S; Y10S205/00; Y10S205/917
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
155 words
A process for producing a magnetic recording medium by packing a magnetic substance in micro pores of an anodic oxide film formed on an aluminum substrate by an anodic oxidation treatment, comprising the steps of subjecting said substrate to an anodic oxidation treatment in an electrolytic bath to form an anodic oxide film having a thickness of at least 4 μm, immersing the anodized aluminum substrate in an acid bath or an alkali bath to enlarge the micro pores in said anodic oxide film to a pore diameter in the range of 300 Å to 1,400 Å by chemically dissolving the walls of said pores, then subjecting said substrate to an electrolytic treatment in a bath containing ions of a magnetic substance to deposit the metallic magnetic substance in the enlarged micro pores, and physically grinding the surface of the anodic oxide film to expose the packed magnetic substance on the surface of said film.
Claim 2
Dependent Claim
155 words
A process for producing a magnetic recording medium by packing a magnetic substance in micro pores of an anodic oxide film formed on an aluminum substrate by an anodic oxidation treatment, comprising the steps of subjecting said substrate to an anodic oxidation treatment in an electrolytic bath to form an anodic oxide film having a thickness of at least 4 μm, immersing the anodized aluminum substrate in an acid bath or an alkali bath to enlarge the micro pores in said anodic oxide film to a pore diameter in the range of 300 Å to 1,400 Å by chemically dissolving the walls of said pores, then subjecting said substrate to an electrolytic treatment in a bath containing ions of a magnetic substance to deposit the metallic magnetic substance in the enlarged micro pores, and physically grinding the surface of the anodic oxide film to expose the packed magnetic substance on the surface of said film.
Claim 3
Dependent Claim
63 words
The process of producing a magnetic recording medium as claimed in claim 1, wherein the step of physical grinding is performed by depositing said magnetic substance in the micro pores and on the surface of the anodic oxide film to cover the surface thereof and then physically grinding the surface of the magnetic substance thus deposited together with the surface of said film.
Claim 4
Dependent Claim
56 words
The process of producing a magnetic recording medium as claimed in claim 1, wherein after enlarging the micro pores in the acid bath or alkali bath, an electric current is applied to the aluminum while in the same bath for a time sufficient to control the thickness of a barrier layer on the anodic oxide film.
Claim 5
Dependent Claim
51 words
The process of producing a magnetic recording medium as claimed in claim 3, wherein in the step of controlling the thickness of the barrier layer, an electrolytic current is applied for 3 to 10 minutes at 5 to 20 volts in direct current or 6 to 20 volts in alternating current.
Claim 6
Dependent Claim
50 words
The process of producing a magnetic recording medium as claimed in claim 1, wherein said electrolytic bath for said anodic oxidation treatment is acidic and comprises an acid of the group constituted of sulfuric acid, sulfamic acid, chromic acid or a mixture of an organic acid and an inorganic acid.
Claim 7
Dependent Claim
32 words
The process of producing a magnetic recording medium as claimed in claim 1, wherein said electrolytic bath for said anodic oxidation treatment is an alkaline bath comprising sodium phosphate or sodium hydroxide.
Claim 8
Dependent Claim
41 words
The process of producing a magnetic recording medium as claimed in claim 1, wherein the step of the anodic oxidation treatment is performed at a current density of 0.1 to 3.0 A/dm 2 and a voltage of 5 to 80 volts.
Claim 9
Dependent Claim
47 words
The process of producing a magnetic recording medium as claimed in claim 1, wherein the bath used for enlarging the pore diameter is an acid bath comprising phosphoric acid, chromic acid, sulfamic acid, sulfuric acid, oxalic acid or a mixture of at least two of these acids.
Claim 10
Dependent Claim
43 words
The process of producing a magnetic recording medium as claimed in claim 1, wherein the bath used for enlarging the pore diameter is an alkaline bath comprising a dilute solution of sodium hydroxide or potassium hydroxide, or a solution of sodium tertiary phosphate.
Claim 11
Dependent Claim
35 words
The process of producing a magnetic recording medium as claimed in claim 1, wherein the temperature of the bath used in the step of enlarging the pore diameter ranges from room temperature to 50° C.
Claim 12
Dependent Claim
36 words
The process of producing a magnetic recording medium as claimed in claim 1, wherein the bath in the metal deposition step is a bath containing a sulfate or sulfamate of a magnetic metal, and magnesium sulfate.
Claim 13
Dependent Claim
180 words
A process of producing a magnetic recording medium by packing a magnetic substance in the micro pores of an anodic oxide film formed by an anodic oxidation treatment on an aluminum substrate, which comprises forming an anodic oxide film having a thickness of at least 4 μm on said aluminum substrate by anodizing the same in an electrolytic bath, immersing the anodized aluminum in an acid bath or an alkali bath capable of chemically dissolving the anodic oxide film, whereby the micro pores in the anodic oxide film are enlarged to a pore diameter in the range of 300 Å to 1,400 Å, applying an electric current to said aluminum in said immersion bath for a sufficient time that the thickness of the barrier layer in the anodic oxide film is controlled, subjecting said substrate to an electrolytic treatment in a bath containing a magnetic substance ion to deposit the magnetic substance in said enlarged micro pores, and then physically grinding the surface of the anodic oxide film to expose the packed magnetic substance at the surface of said film.
Claim 14
Dependent Claim
180 words
A process of producing a magnetic recording medium by packing a magnetic substance in the micro pores of an anodic oxide film formed by an anodic oxidation treatment on an aluminum substrate, which comprises forming an anodic oxide film having a thickness of at least 4 μm on said aluminum substrate by anodizing the same in an electrolytic bath, immersing the anodized aluminum in an acid bath or an alkali bath capable of chemically dissolving the anodic oxide film, whereby the micro pores in the anodic oxide film are enlarged to a pore diameter in the range of 300 Å to 1,400 Å, applying an electric current to said aluminum in said immersion bath for a sufficient time that the thickness of the barrier layer in the anodic oxide film is controlled, subjecting said substrate to an electrolytic treatment in a bath containing a magnetic substance ion to deposit the magnetic substance in said enlarged micro pores, and then physically grinding the surface of the anodic oxide film to expose the packed magnetic substance at the surface of said film.
Claim 15
Dependent Claim
154 words
A process of producing a magnetic recording medium by packing a magnetic substance in the micro pores of an anodic oxide film having a thickness of at least 4 μm on an aluminum substrate comprising: immersing an aluminum substrate with said anodic oxide film thereon in an acid bath or an alkali bath to chemically dissolve a part of of the anodic oxide film, whereby the micro pores in the anodic oxide film are enlarged to a pore diameter in the range of 300 Å to 1,400 Å, subjecting the thus-treated aluminum substrate to an electrolytic treatment in a bath containing ions of a magnetic substance to deposit the magnetic substance in said micro pores and cover the surface of the anodic oxide film with the magnetic substance, and physically grinding the surface of the magnetic substance covering the surface of the anodic oxide film together with the surface of the anodic oxide film.
Claim 16
Dependent Claim
154 words
A process of producing a magnetic recording medium by packing a magnetic substance in the micro pores of an anodic oxide film having a thickness of at least 4 μm on an aluminum substrate comprising: immersing an aluminum substrate with said anodic oxide film thereon in an acid bath or an alkali bath to chemically dissolve a part of of the anodic oxide film, whereby the micro pores in the anodic oxide film are enlarged to a pore diameter in the range of 300 Å to 1,400 Å, subjecting the thus-treated aluminum substrate to an electrolytic treatment in a bath containing ions of a magnetic substance to deposit the magnetic substance in said micro pores and cover the surface of the anodic oxide film with the magnetic substance, and physically grinding the surface of the magnetic substance covering the surface of the anodic oxide film together with the surface of the anodic oxide film.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-10-21 | 1989-04-22 | 1989-10-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-10-21 | 1993-04-22 | 1993-10-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-10-21 | 1997-04-22 | 1997-10-22 | $7700.00 | Window Closed / Lapsed |