Process for preparing carboxymethyl ethyl cellulose suitable for enteric coating

Assignee: Kohjin Holdings Co Ltd
•
Filing: 1984-10-05
•
Granted: 1985-10-15
•
Expires: 2004-10-05
📄 Original PDF 🌐 Google Patents 🔄 Sync Now

Abstract

Abstract A process for preparing carboxymethyl ethyl cellulose (CMEC) suitable for enteric coating which comprises (1) adding an alkali metal hydroxide and water to a substantially water-immiscible organic solvent dispersion of carboxymethyl cellulose (CMC) and reacting CMC with an ethyl halide in the presence of a phase transfer catalyst, (2) dissolving the produced CMEC in an aqueous solution of a basic compound selected from the group consisting of ammonia, a water-soluble amine and an alkali metal hydroxide and subjecting the resulting solution to depolymerization in the presence of a peroxide, (3) neutralizing the resulting basic reaction mixture with an acidic substance in the presence of a lower alkyl alcohol or acetone to form a hydrogel of the depolymerized CMEC, subjecting the hydrogel to dehydration with agitation, isolating the depolymerized CMEC and washing with water, and (4) drying the wet depolymerized CMEC without pulverization or after pulverizing in the wet state to particles having an average particle size of at most 100 μm. The product has an excellent quality, and is easily soluble in organic solvents and easily dispersible in water, and provides a coating film having excellent strength, resistance to gastric juice and solubility in intestinal juice. Also, the solubility in organic solvents and dispersibility in water of the product can be controlled by selecting the basic compound used in the depolymerization.

Inventors

  • 👤 Hideaki Mukohyama
  • 👤 Ryoichi Hiraoka
  • 👤 Shohachi Ushijima
  • 👤 Motoyasu Saito

Bibliographic Details

Application Number —
Jurisdiction US
Data Source google_patents
Last Synchronized 2026-10-26 00:27
CPC Classifications
A; A61; A61K; A61K9/00; A61K9/20; A61K9/28; A61K9/2806; A61K9/2833; A61K9/286; A61K9/2866; C; C08; C08B; C08B11/00; C08B11/193

Claims Analysis

Total Claims: 7
Claim 1
Independent Claim 206 words
A process for preparing carboxymethyl ethyl cellulose suitable for enteric coating which comprises: (1) adding an alkali metal hydroxide to a dispersion of carboxymethyl cellulose in an organic solvent and subjecting the dispersion to a reaction with an ethyl halide in the presence of a phase transfer catalyst to produce carboxymethyl ethyl cellulose, said carboxymethyl cellulose having a degree of substitution of carboxymethyl group of 0.2 to 1.2, and said organic solvent being substantially immiscible with an aqueous solution of the alkali metal hydroxide and capable of dissolving the ethyl halide. (2) dissolving carboxymethyl ethyl cellulose in an aqueous solution of a basic compound selected from the group consisting of ammonia, a water-soluble amine and an alkali metal hydroxide, and subjecting the resulting solution to depolymerization in the presence of a peroxide, (3) neutralizing the resulting basic solution of the depolymerized carboxymethyl ethyl cellulose with an acidic substance in the presence of an alkyl alcohol having 1 to 3 carbon atoms or acetone to form a hydrogel of carboxymethyl ethyl cellulose, and subjecting the hydrogel to dehydration with agitation at a temperature not lower than the temperature at which dehydration occurs, followed by isolation and washing with water, and (4) drying the wet carboxymethyl ethyl cellulose.
Claim 2
Dependent Claim 206 words
A process for preparing carboxymethyl ethyl cellulose suitable for enteric coating which comprises: (1) adding an alkali metal hydroxide to a dispersion of carboxymethyl cellulose in an organic solvent and subjecting the dispersion to a reaction with an ethyl halide in the presence of a phase transfer catalyst to produce carboxymethyl ethyl cellulose, said carboxymethyl cellulose having a degree of substitution of carboxymethyl group of 0.2 to 1.2, and said organic solvent being substantially immiscible with an aqueous solution of the alkali metal hydroxide and capable of dissolving the ethyl halide. (2) dissolving carboxymethyl ethyl cellulose in an aqueous solution of a basic compound selected from the group consisting of ammonia, a water-soluble amine and an alkali metal hydroxide, and subjecting the resulting solution to depolymerization in the presence of a peroxide, (3) neutralizing the resulting basic solution of the depolymerized carboxymethyl ethyl cellulose with an acidic substance in the presence of an alkyl alcohol having 1 to 3 carbon atoms or acetone to form a hydrogel of carboxymethyl ethyl cellulose, and subjecting the hydrogel to dehydration with agitation at a temperature not lower than the temperature at which dehydration occurs, followed by isolation and washing with water, and (4) drying the wet carboxymethyl ethyl cellulose.
Claim 3
Dependent Claim 38 words
The process of claim 1, wherein said phase transfer catalyst is a tetraalkylammonium salt provided that the alkyl means an alkyl group having 1 to 4 carbon atoms or an aralkyl group having 7 to 8 carbon atoms.
Claim 4
Dependent Claim 19 words
The process of claim 1, wherein said dehydration is carried out at a temperature of 60° to 90° C.
Claim 5
Dependent Claim 22 words
The process of claim 1, wherein said drying is carried out after pulverizing the wet carboxymethyl ethyl cellulose in the wet state.
Claim 6
Dependent Claim 22 words
The process of claim 4, wherein the pulverized carboxymethyl ethyl cellulose has an average particle size of not more than 100 μm.
Claim 7
Dependent Claim 33 words
The process of claim 1, wherein said basic compound is a mixture of an alkali metal hydroxide and at least one member selected from the group consisting of ammonia and a water-soluble amine.

References Cited (Backward Citations)

US3789117A Cited
US4250305A Cited
US4311833A Cited
US4477657A Cited
US4456751A Cited

USPTO Annuity & Maintenance Windows

Annuity Stage Window Opens Payment Deadline Surcharge Period Until Estimated Fee Status
3.5 Years (Year 4) 1988-10-14 1989-04-15 1989-10-15 $2000.00 Window Closed / Lapsed
7.5 Years (Year 8) 1992-10-14 1993-04-15 1993-10-15 $3760.00 Window Closed / Lapsed