Additive dispersions and process for their incorporation with fiber-forming polymer

Claim 2

In a process for melt-spinning yarn from fiber-forming polyamide polymer, the improvement comprising: adding to the polymer, prior to spinning, a dispersion comprising: (a) 20 to 79.9 weight percent of at least one polymer additive having an average diameter of up to 50 microns at a temperature of 25° C.; (b) 20 to 79.9 weight percent of a carrier selected from the group consisting of (i) a glyceride which is non-resin forming when exposed to temperatures of up to 280° C. and pressures of up to 4000 psig (27 600 kPa) for up to 30 seconds, and which has an average molecular weight of between about 600 and 2400; (ii) a C 5 -C 26 fatty acid ester of pentaerythritol; and (iii) a C 5 -C 26 fatty acid ester of dipentaerythritol; and (c) 0.1 to 2 weight percent of a thickener selected from the group consisting of: (i) dibenzylidene sorbitol; and (ii) silica having an ultimate particle size of 7 to 14 nanometers (nm).

Claim 3

The process of claim 1 wherein the dispersion is added into the polymer when the polymer is in chip form.

Claim 4

The process of claim 1 wherein the dispersion is added into the polymer when the polymer is molten.

Claim 5

The process of claim 1 wherein the carrier forms 30 to 60 weight percent of the dispersion, the additive forms 40 to 69.75 weight percent of the dispersion, and the thickener forms 0.25 to 1.25 weight percent of the dispersion.

Claim 6

The process of claim 4 wherein the carrier is the glyceride formed by transesterification of coconut oil with glycerol trioleate, the thickener is silica having an ultimate particle size of 7 to 14 nm.

Claim 7

In a process for melt-spinning yarn from a fiber-forming polyester polymer, the improvement comprising: adding to the polymer, prior to spinning, a dispersion comprising: (a) 20 to 79.9 weight percent of at least one polymer additive having an average diameter of up to 50 microns at a temperature of 25° C.; (b) 20 to 79.9 weight percent of a carrier selected from the group consisting of: (i) a glyceride which is non-resin forming when exposed to temperatures of up to 320° C. and pressures of up to 4000 psig (27 600 kPa) for up to 60 seconds, and which has an average molecular weight of between about 600 and 2400; (ii) a C 5 -C 26 fatty acid ester of pentaerythritol; and (iii) a C 5 -C 26 fatty acid ester of dipentaerythritol; and (c) 0.1 to 2 weight percent of a thickener selected from the group consisting of: (i) dibenzylidene sorbitol; and (ii) silica having an ultimate particle size of 7 to 14 nanometers (nm).

Claim 8

In a process for melt-spinning yarn from a fiber-forming polyester polymer, the improvement comprising: adding to the polymer, prior to spinning, a dispersion comprising: (a) 20 to 79.9 weight percent of at least one polymer additive having an average diameter of up to 50 microns at a temperature of 25° C.; (b) 20 to 79.9 weight percent of a carrier selected from the group consisting of: (i) a glyceride which is non-resin forming when exposed to temperatures of up to 320° C. and pressures of up to 4000 psig (27 600 kPa) for up to 60 seconds, and which has an average molecular weight of between about 600 and 2400; (ii) a C 5 -C 26 fatty acid ester of pentaerythritol; and (iii) a C 5 -C 26 fatty acid ester of dipentaerythritol; and (c) 0.1 to 2 weight percent of a thickener selected from the group consisting of: (i) dibenzylidene sorbitol; and (ii) silica having an ultimate particle size of 7 to 14 nanometers (nm).

Claim 9

The process of claim 6 wherein the dispersion is added into the polymer when the polymer is in chip form.

Claim 10

The process of claim 6 wherein the dispersion is added into the polymer when the polymer is molten.

Claim 11

The process of claim 6 wherein the carrier forms 30 to 60 weight percent of the dispersion, the additive forms 40 to 69.75 weight percent of the dispersion, and the thickener forms 0.25 to 1.25 weight percent of the dispersion.

Claim 12

The process of claim 9 wherein the carrier is the glyceride formed by transesterification of coconut oil with glycerol trioleate, the thickener is silica having an ultimate particle size of 7 to 14 nm.