Catalyst and method of preparing catalyst

Claim 2

A process for preparing a skin catalyst comprising; (a) immersing a porous support in a presoak liquid for a length of time sufficient to fill the interior of each support particle, (b) withdrawing the support particle of (a) and removing the excess liquid, (c) impregnating the support particles of (b) with an impregnating metal compound solution that is substantially immiscible with and has a surface tension that is at least about 5 dyne/cm @ 20° C. lower than the presoak liquid, and (d) drying and treating to activate the catalyst thereby producing a skin catalyst.

Claim 3

A process according to claim 1 wherein the dried catalyst is treated at an elevated temperature in a reducing atmosphere thereby producing a skin catalyst.

Claim 4

A process for preparing a skin catalyst according to claim 2 wherein the reducing atmosphere is hydrogen first at room temperature to reduce some metal ions then second at at least about 450° F. for at least about two hours to complete the metal reduction.

Claim 5

A process for preparing a skin catalyst according to claim 1 wherein the support particles are dried under vacuum.

Claim 6

A process for preparing a skin catalyst according to claim 1 wherein the support particles are alumina pellets at least about 1 mm in diameter.

Claim 7

A process for preparing a skin catalyst according to claim 1 wherein said presoak liquid has a surface tension at 20° C. of about 40-90 dyne/cm and said impregnating solution has a surface tension at 20° C. of about 15-60 dyne/cm.

Claim 8

A process for preparing a skin catalyst according to claim 1 wherein the presoak liquid has a surface tension at 20° C. of about 45-75 dyne/cm and the impregnating solution has a surface tension at 20° C. of about 20-35 dyne/cm.

Claim 9

A process for preparing a skin catalyst according to claim 7 wherein the impregnating solution is palladium (II) acetate in dichloromethane.

Claim 10

A process for preparing a skin catalyst according to claim 7 wherein said presoak liquid is water.

Claim 11

A process for preparing a skin catalyst comprising; (a) immersing alumina pellets in an aqueous presoak solution until the presoak solution has completely penetrated to the core, (b) filtering and removing excess liquid from the outside of the pellets, (c) impregnating the alumina pellets from (b) with a Group VIII metal containing impregnating solution that is both immiscible and has a lower surface tension than the aqueous solution, (d) evaporating the solvent of the impregnating solution, (e) drying the impregnated pellets at an elevated temperature under vacuum, and (f) treating the metal on the dried impregnated pellets in an atmosphere suitable to activate the catalyst.

Claim 12

A process for preparing a skin catalyst comprising; (a) immersing alumina pellets in an aqueous presoak solution until the presoak solution has completely penetrated to the core, (b) filtering and removing excess liquid from the outside of the pellets, (c) impregnating the alumina pellets from (b) with a Group VIII metal containing impregnating solution that is both immiscible and has a lower surface tension than the aqueous solution, (d) evaporating the solvent of the impregnating solution, (e) drying the impregnated pellets at an elevated temperature under vacuum, and (f) treating the metal on the dried impregnated pellets in an atmosphere suitable to activate the catalyst.

Claim 13

A process according to claim 10 wherein the dried catalyst is treated at an elevated temperature in a reducing atmosphere thereby producing a skin catalyst.

Claim 14

A process according to claim 11 wherein the reducing atmosphere is hydrogen first at room temperature to reduce some metal ions then second at at least about 450° F. for at least about two hours to complete the metal reduction.

Claim 15

A process for preparing a skin catalyst according to claim 11 wherein said impregnating solution is palladium (II) acetate in dichloromethane and the reducing atmosphere is hydrogen.

Claim 16

A process for preparing a skin catalyst according to claim 10 wherein said presoak liquid has a surface tension at 20° C. of about 40-90 dyne/cm and said impregnating solution has a surface tension at 20° C. of about 15-60 dyne/cm.

Claim 17

A process for preparing a skin catalyst according to claim 14 wherein said presoak liquid is water.

Claim 18

A process for preparing a skin catalyst according to claim 14 wherein said impregnating solution is palladium (II) acetate in dichloromethane.

Claim 19

A catalyst prepared according to the process of claim 1.

Claim 20

A catalyst prepared according to the process of claim 13.

Claim 21

A process for preparing a skin catalyst the improvement which comprises: (a) presoaking a porous support with a presoak liquid, (b) impregnating with a metal containing impregnating solution that is not miscible with and has a lower surface tension than the presoak liquid.

Claim 22

A process for preparing a skin catalyst the improvement which comprises: (a) presoaking a porous support with a presoak liquid, (b) impregnating with a metal containing impregnating solution that is not miscible with and has a lower surface tension than the presoak liquid.

Claim 23

A process for preparing a skin catalyst according to claim 1 wherein the metal is selected from the transition metals in the subgroups III B, IV B, V B, VI B, VII B, VIII, I B and II B of the Periodic Table of the Elements.

Claim 24

A process for preparing a skin catalyst according to claim 4 wherein the support particles are dried under vacuum at at least about 200° F. for at least about one hour.