Method for making a transferrable dye medium
Assignee: Sony Corp
•
Filing: 1984-03-09
•
Granted: 1985-10-15
•
Expires: 2004-03-09
Abstract
Abstract A transferable dye medium for use in a thermal printer is made by applying a layer of dye material to a base layer; softening the applied layer of dyed material, as by heating same, and then calendering the softened, dye-coated base layer.
Inventors
- 👤 Osamu Majima
- 👤 Shigemichi Honda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 06:55
CPC Classifications
B; B41; B41M; B41M5/00; B41M5/26; B41M5/40; B41M5/42; B41M5/382; B41M5/38207
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
119 words
A method of making a thermally transferable dye medium for a thermal printer comprising the steps of: providing a base layer; coating a surface of said base layer with a dye layer comprised of a sublimable dye material dispersed in a binder and having a sublimation temperature less than a melting temperature of said binder to form a dye-coated base layer; drying said dye layer on said base layer; heating said dried dye layer at a temperature less than either of said melting and sublimation temperatures, thereby to soften said dried dye layer; and calendering said softened dried dye-coated base layer so as to cause impregnation of at least a portion of said dye layer into said base layer.
Claim 2
Independent Claim
119 words
A method of making a thermally transferable dye medium for a thermal printer comprising the steps of: providing a base layer; coating a surface of said base layer with a dye layer comprised of a sublimable dye material dispersed in a binder and having a sublimation temperature less than a melting temperature of said binder to form a dye-coated base layer; drying said dye layer on said base layer; heating said dried dye layer at a temperature less than either of said melting and sublimation temperatures, thereby to soften said dried dye layer; and calendering said softened dried dye-coated base layer so as to cause impregnation of at least a portion of said dye layer into said base layer.
Claim 3
Dependent Claim
20 words
The method of claim 1 wherein said step of calendering comprises passing said dye-coated base layer between pressure roll means.
Claim 4
Dependent Claim
16 words
The method of claim 2 wherein said steps of heating and calendering are carried out concurrently.
Claim 5
Dependent Claim
16 words
The method of claim 3 wherein one of said pressure roll means comprises a heated roller.
Claim 6
Dependent Claim
24 words
The method of claim 2 wherein said impregnation is enhanced by sucking said at least portion of said dye layer into said base layer.
Claim 7
Dependent Claim
49 words
The method of claim 5, wherein said step of sucking comprises reducing the ambient atmospheric pressure at the side of said base layer on which no dye layer is coated to draw thereinto said at least portion of the dye layer applied to said surface of said base layer.
Claim 8
Dependent Claim
45 words
The method of claim 6, wherein said step of reducing the ambient atmospheric pressure at said base layer comprises the further steps of passing said dye-coated base layer over a roller and reducing the atmospheric pressure within said roller to less than ambient atmospheric pressure.
Claim 9
Dependent Claim
32 words
The method of claim 7 wherein the surface of said base layer that is opposite the surface on which said dye layer is applied is in facing relationship with said reduced-pressure roller.
Claim 10
Dependent Claim
23 words
The method of claim 8 wherein said steps of heating and reducing the ambient pressure at said base layer are carried out concurrently.
Claim 11
Dependent Claim
22 words
The method of claim 8 wherein said step of heating precedes said step of reducing the ambient pressure at said base layer.
Claim 12
Dependent Claim
19 words
The method of claim 6 wherein said step of heating comprises applying infra-red heat to said applied dye layer.
Claim 13
Dependent Claim
42 words
The method of claim 2 wherein said impregnation is enhanced by applying an electric charge to said dye layer; and applying an electric force to the softened, charged dye layer to urge said at least a portion thereof into said base layer.
Claim 14
Dependent Claim
36 words
The method of claim 12 wherein said step of applying an electric charge to said dye layer comprises passing said dye-coated base layer past a corona discharge device prior to the heating of said dye layer.
Claim 15
Dependent Claim
28 words
The method of claim 13 wherein said step of applying an electric force comprises passing said dye-coated base layer having the charged dye layer over an electrical reference.
Claim 16
Dependent Claim
41 words
The method of claim 14, further comprising the step of reducing the ambient pressure at said base layer concurrently with passing said dye-coated base layer over said electrical reference to apply an additional mechanical force to said softened, charged dye layer.
Claim 17
Dependent Claim
43 words
The method of claim 15 wherein said steps of passing said dye-coated base layer over an electrical reference and reducing the ambient pressure at said base layer are carried out by reduced pressure roll means having a predetermined electrical reference potential applied thereto.
Claim 18
Dependent Claim
19 words
The method of claim 12 wherein said step of heating comprises passing said dye-coated base layer past heat roll-means.
Claim 19
Dependent Claim
25 words
The method of claim 17 wherein said electric charge is applied to said dye layer before said dye-coated base layer passes said heat roll means.
Claim 20
Dependent Claim
35 words
The method of claim 18 wherein said step of applying an electric force comprises applying a predetermined electrical voltage to said heat roll means while concurrently passing said dye-coated base layer over an electrical reference.
Claim 21
Dependent Claim
46 words
The method of claim 17 wherein said step of applying an electric force comprises passing said dye-coated base layer having the softened, charged dye layer through an electric field of polarity to urge said at least portion of said charged dye layer into said base layer.
References Cited (Backward Citations)
US2321939A
Cited
US2839025A
Cited
US3019130A
Cited
GB1115082A
Cited
GB1195727A
Cited
US3667422A
Cited
US3565039A
Cited
US4058644A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-10-14 | 1989-04-15 | 1989-10-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-10-14 | 1993-04-15 | 1993-10-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-10-14 | 1997-04-15 | 1997-10-15 | $7700.00 | Window Closed / Lapsed |