Abstract A process for treating the surface of aluminum foil for use as an electrode of electrolytic capacitors to increase the surface area of the foil to the greatest possible extent includes the three steps of pre-etching treatment, intermediate nitric acid treatment and post-etching treatment. The pre-etching treatment is conducted electrolytically in an aqueous solution of chromic acid and at least one of chromic acid and chromates. The intermediate nitric acid treatment is carried out by immersing the pre-etched foil in an aqueous solution of nitric acid to remove a chromate film formed by the pre-etching from the foil surface, especially from the interior of the resulting pits. The post-etching treatment is conducted electrolytically in an aqueous solution of hydrochloric acid, or hydrochloric acid and an oxidizing acid.
A process for treating the surface of aluminum foil for use as an electrode of electrolytic capacitors characterized in that the aluminum foil is subjected to an electrolytic pre-etching treatment in an aqueous solution containing hydrochloric acid and at least one compound selected from the group consisting of chromic acid and chromates, then to an intermediate nitric acid treatment, and thereafter to an electrolytic post-etching treatment in an aqueous solution containing hydrochloric acid, or hydrochloric acid and an oxidizing acid.
Claim 2
Dependent Claim
80 words
A process for treating the surface of aluminum foil for use as an electrode of electrolytic capacitors characterized in that the aluminum foil is subjected to an electrolytic pre-etching treatment in an aqueous solution containing hydrochloric acid and at least one compound selected from the group consisting of chromic acid and chromates, then to an intermediate nitric acid treatment, and thereafter to an electrolytic post-etching treatment in an aqueous solution containing hydrochloric acid, or hydrochloric acid and an oxidizing acid.
Claim 3
Dependent Claim
33 words
A process as defined in claim 1 wherein the aqueous solution for the electrolytic pre-etching treatment contains 2 to 15% of hydrochloric acid and 0.01 to 35% of said at least one compound.
Claim 4
Dependent Claim
34 words
A process as defined in claim 2 wherein the electrolytic pre-etching treatment is conducted at a bath temperature of 50° to 100° C. and at a current density of to 40 A/dm 2 .
Claim 5
Dependent Claim
25 words
A process as defined in claim 1 wherein the nitric acid treatment is conducted in an aqueous solution containing 5 to 60% of nitric acid.
Claim 6
Dependent Claim
28 words
A process as defined in claim 4 wherein the nitric acid treatment is conducted at a bath temperature of 40° to 90° C. for 1 to 10 minutes.
Claim 7
Dependent Claim
38 words
A process as defined in claim 1 wherein the aqueous solution for the electrolytic post-etching treatment contains 2 to 15% of hydrochloric acid, or 2 to 15% of hydrochloric acid and 0.03 to 3% of the oxidizing acid.
Claim 8
Dependent Claim
35 words
A process as defined in claim 6 wherein the electrolytic post-etching treatment is conducted at a bath temperature of 50° to 100° C. and at a current density of 0.5 to 7 A/dm 2 .