HCT Crystal growth method

Claim 2

In a method of growing pseudobinary crystals and the like by a modified Bridgman-Stockbarger technique, the improvement comprising, maintaining the temperature of an upper zone in a crystal growth furnace at a temperature effective to create a cavitated solid/liquid in the portion of an alloy composition placed in the upper zone and directionally solidifying the liquid from the cavitated solid/liquid in the lower zone of the furnace while translating the alloy relatively through the furnace in the direction of from the upper zone to the lower zone and controlling the temperatures of the upper and lower zones at levels effective to produce multi-directional homogeneity in the alloy crystals.

Claim 3

The method of claim 1 wherein the upper and lower zones are separated by a thin insulating barrier.

Claim 4

The method of claim 2 wherein the insulating barrier is less than about 4 mm in thickness.

Claim 5

The method of claim 2 wherein the insulating barrier is constructed of materials selected from the group consisting of fibrous alumina, silica and zirconia.

Claim 6

The method of claim 2 wherein the thermal view angles α and β of the alloy composition in relation to the barrier are substantially equal.

Claim 7

The method of claim 1 wherein the alloy solidifies at an interface between the upper and lower zones and wherein the temperatures of the upper zone T U , the lower zone T L , and the temperature of the alloy at the solidifying interface T I , are maintained substantially according to the following relationship: T.sub.U.sup.4 -T.sub.I.sup.4 +T.sub.I.sup.4 -T.sub.L.sup.4.

Claim 8

The method of claim 6 wherein T U is maintained at a temperature of less than about the liquidus temperature for the alloy.

Claim 9

The method of claim 6 wherein T U is maintained at about 10° C. below the liquidus temperature for the alloy.

Claim 10

The method of claim 1 wherein the alloy is HCT alloy of composition Hg 1-x Cd x Te and wherein the value of mole fraction x is between about 0.15 and 0.6.

Claim 11

The method of claim 1 wherein the translation rate, R, is maintained according to the relationship dx/dl.sub.l=0 =(x.sub.o R/D)(k-1)/k), where D is the diffusion coefficient, x o is the initial overall material composition, k is the segregation coefficient for the composition and l is the distance to the interface.

Claim 12

The method of claim 10 wherein the translation rate is maintained at about 0.068 μm/second.

Claim 13

In a method of growing pseudobinary HCT alloy crystals and the like by a modified Bridgman-Stockbarger technique the improvement comprising introducing an ampule containing a solidified HCT alloy having the composition Hg 1-x Cd x Te, where x is the mole fraction of Cd and x is between about 0.15 and 0.6, into a Bridgman-Stockbarger function having an upper hot zone and a lower cold zone, the upper zone and the lower zone being separated by an insulating barrier, the ampule being initially positioned substantially in the upper zone, and the upper zone being maintained at a temperature sufficient to produce a cavitated alloy solid/liquid in the ampule in the portion maintained in the upper zone, directionally solidifying the liquid alloy from the cavitated solid/liquid by collecting liquid alloy from the cavitated solid/liquid in the portion of the ampule below the cavitated solid/liquid and translating the ampule relatively through the furnace from the upper zone to the lower zone, the lower zone being maintained at a temperature sufficient to solidify the alloy, the liquid from the cavitated solid/liquid and the solidifying alloy forming an interface, and maintaining the interface substantially at the location of the thermal barrier, the temperatures of the upper zone T U , the lower zone T L , and the solidifying temperature of the alloy at the interface T I being maintained substantially according to the following relationship: T.sub.U.sup.4 -T.sub.I.sup.4 =T.sub.I.sup.4 -T.sub.L.sup.4, the method being effective to produce a homogeneous alloy composition.

Claim 14

In a method of growing pseudobinary HCT alloy crystals and the like by a modified Bridgman-Stockbarger technique the improvement comprising introducing an ampule containing a solidified HCT alloy having the composition Hg 1-x Cd x Te, where x is the mole fraction of Cd and x is between about 0.15 and 0.6, into a Bridgman-Stockbarger function having an upper hot zone and a lower cold zone, the upper zone and the lower zone being separated by an insulating barrier, the ampule being initially positioned substantially in the upper zone, and the upper zone being maintained at a temperature sufficient to produce a cavitated alloy solid/liquid in the ampule in the portion maintained in the upper zone, directionally solidifying the liquid alloy from the cavitated solid/liquid by collecting liquid alloy from the cavitated solid/liquid in the portion of the ampule below the cavitated solid/liquid and translating the ampule relatively through the furnace from the upper zone to the lower zone, the lower zone being maintained at a temperature sufficient to solidify the alloy, the liquid from the cavitated solid/liquid and the solidifying alloy forming an interface, and maintaining the interface substantially at the location of the thermal barrier, the temperatures of the upper zone T U , the lower zone T L , and the solidifying temperature of the alloy at the interface T I being maintained substantially according to the following relationship: T.sub.U.sup.4 -T.sub.I.sup.4 =T.sub.I.sup.4 -T.sub.L.sup.4, the method being effective to produce a homogeneous alloy composition.

Claim 15

The method of claim 12 wherein T U is maintained at about 10° C. below the liquidus temperature for the alloy.

Claim 16

The method of claim 12 wherein the thermal barrier is less than about 4 mm in thickness.

Claim 17

The method of claim 14 wherein the thermal barrier is selected from insulating materials consisting of fibrous alumina, silica and zirconia.

Claim 18

The method of claim 12 wherein the thermal view angles of the solidifying alloy interface at the thermal barrier, α and β, are substantially equal.

Claim 19

The method of claim 12 wherein the translation rate, R, is maintained according to the relationship: dx/dl.sub.l=0 =(x.sub.o R/D)(k-1)/k), wherein D is the diffusion coefficient, x o is the initial overall material composition, k is the segregation coefficient for the composition and l is the distance to the interface.

Claim 20

The method of claim 17 wherein the translation rate is about 0.068 μm/ second.

Claim 21

The process of claim 1 wherein the cavitated solid is maintained in the upper zone during at least part of the solidifying step.

Claim 22

The process of claim 12 including the step of maintaining a cavitated solid in the upper zone throughout a substantial portion of the solidifying step.