Process for controlling thickness of die attach adhesive
Assignee: Advanced Micro Devices Inc
•
Filing: 1983-03-08
•
Granted: 1985-10-08
•
Expires: 2003-03-08
Abstract
Abstract A semiconductor die attach adhesive is provided which is formed of a plurality of spacers formed in a suspension of silver filled glass. In one embodiment of this invention, the spacers are spheres. The spacers utilized in one embodiment of this invention have a melting temperature below the temperature at which the solvents are evaporated from the die attach adhesive. In this manner, as the solvents are driven from the silver filled glass during the die attach operation, thus causing the volume of the silver filled glass to decrease, the spacers utilized in this invention partially melt, thus decreasing their thickness. This decreased thickness of the spacers decreases the separation between the die and the substrate, thus preventing the formation of voids within the die attach adhesive. In one embodiment, the spacers are formed of a lead/tin alloy. In another embodiment of this invention, the spacers are formed of a lead/tin/bismuth alloy, and in yet another embodiment of this invention the spacers are formed of lead/tin/bismuth eutectic.
Inventors
- 👤 Robert Newman
- 👤 Fred Johnson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 12:42
CPC Classifications
H; H10; H10W; H10W72/00; H10W72/30; H10W72/071; H10W72/073; H10W72/07321; H10W72/07327; H10W72/07331; H10W72/07337; H10W72/321; H10W72/325; H10W72/351; H10W72/352; H10W72/353; H10W72/354; H10W72/50; H10W72/551; H10W72/552; H10W72/5522; H10W74/00; H10W74/10; H10W74/15; H10W90/00; H10W90/701; H10W90/721; H10W90/724; H10W90/731; H10W90/734
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
184 words
The method for attaching a first structure to a second structure comprising the steps of: providing an adhesive composition comprising an adhesive, a solvent, and a plurality of spacer means; physically placing said first structure and said second structure on opposite sides of and in contact with a layer of said adhesive composition; subjecting said first and second structures and said layer of adhesive composition to a first selected temperature sufficient to cause the evaporation of said solvent from said layer of adhesive composition and greater than or equal to the melting point of said spacer means, thereby causing said spacer means to decrease in thickness, subjecting said first and said second structures and said layer of adhesive composition to a second selected temperature greater than said first selected temperature, said second selected temperature being sufficient to cause said layer of adhesive composition to melt; and cooling said first and second structures and said layer of adhesive composition to a temperature beneath said second selected temperature, thereby causing said layer of adhesive to solidify, thereby permanently attaching said first structure to said second structure.
Claim 2
Independent Claim
184 words
The method for attaching a first structure to a second structure comprising the steps of: providing an adhesive composition comprising an adhesive, a solvent, and a plurality of spacer means; physically placing said first structure and said second structure on opposite sides of and in contact with a layer of said adhesive composition; subjecting said first and second structures and said layer of adhesive composition to a first selected temperature sufficient to cause the evaporation of said solvent from said layer of adhesive composition and greater than or equal to the melting point of said spacer means, thereby causing said spacer means to decrease in thickness, subjecting said first and said second structures and said layer of adhesive composition to a second selected temperature greater than said first selected temperature, said second selected temperature being sufficient to cause said layer of adhesive composition to melt; and cooling said first and second structures and said layer of adhesive composition to a temperature beneath said second selected temperature, thereby causing said layer of adhesive to solidify, thereby permanently attaching said first structure to said second structure.
Claim 3
Dependent Claim
24 words
The method of claim 1 wherein said adhesive comprises a material selected from the group of materials consisting of glass, polyimide and organic adhesives.
Claim 4
Dependent Claim
17 words
The method of claim 1 wherein said spacer means comprise an alloy of lead, tin, and bismuth.
Claim 5
Dependent Claim
26 words
The method of claim 1 wherein said spacer means comprise a eutectic of, by weight, approximately 32 percent lead, 15.5 percent tin, and 52.5 percent bismuth.
Claim 6
Dependent Claim
25 words
The method of claim 1 wherein said solvent comprises a solvent selected from the group of solvents consisting of terpineol, ethylene glycol, desinol, and flourocarbons.
Claim 7
Dependent Claim
25 words
The method of claim 1 wherein said spacer means comprise a material selected from the group of materials consisting of lead, tin, bismuth, and glass.
Claim 8
Dependent Claim
32 words
The method of claim 1 wherein said step of physically placing comprises the steps of: placing said adhesive composition on said first structure; and placing said second structure on said adhesive composition.
Claim 9
Dependent Claim
32 words
The method of claim 1 wherein said step of physically placing comprises the steps of: placing said adhesive composition on said second structure; and placing said second structure on said first structure.
Claim 10
Dependent Claim
15 words
The method as in claim 1, 5, or 6 wherein said spacer means are spheres.
Claim 11
Dependent Claim
23 words
The method of claim 1, 6 or 7 wherein said first structure comprises a substrate and said second structure comprising a semiconductor device.
Claim 12
Dependent Claim
43 words
The method as in claim 1 wherein at said first selected temperature said spacer means are deformed such that their thickness decreases by an amount which approximately equals the decrease in thickness of said adhesive composition due to said evaporation of said solvent.
References Cited (Backward Citations)
US2335615A
Cited
US3406053A
Cited
US3655482A
Cited
US3923581A
Cited
US3795047A
Cited
US4083718A
Cited
US4157273A
Cited
US4129881A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-10-07 | 1989-04-08 | 1989-10-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-10-07 | 1993-04-08 | 1993-10-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-10-07 | 1997-04-08 | 1997-10-08 | $7700.00 | Window Closed / Lapsed |