Assignee: Stokes Vacuum Inc
•
Filing: 1984-02-13
•
Granted: 1985-10-01
•
Expires: 2004-02-13
Abstract
Abstract An EMI/RFI shielding panel prepared by glow discharge treatment of a substrate material to provide a chemically reactive surface, and then successively vapor plating the surface with an adhesive layer of chromium or stainless steel, a shielding layer of copper or aluminum onto the adhesive layer, and then a protective layer of chromium or aluminum onto the shielding layer.
Inventors
- 👤 Walter J. Miller
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 19:54
CPC Classifications
H; H05; H05K; H05K9/00; H05K9/0073; H05K9/0081; H05K9/0088; C; C23; C23C; C23C14/00; C23C14/02; C23C14/021; C23C14/022
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
186 words
A method of manufacturing a panel for shielding the passage of electromagnetic radio frequency interference therethrough, comprising: (a) subjecting a surface of an electrically insulating substrate sheet material to glow-discharge treatment to provide an active surface that is chemically reactive with vapors of chromium or stainless steel at an air pressure less than about 5×10 -5 TORR; (b) vapor plating chromium or stainless steel onto said active surface to provide an adhesive layer of chromium or stainless steel chemically bound to said surface, said layer having a thickness within the range of about 300 Angstroms to about 1,000 Angstroms; (c) vapor plating an aluminum or copper shielding layer onto the adhesive layer of (b) prior to substantial oxidation of the adhesive layer surface, said shielding layer having a thickness within the range of about 1,000 Angstroms to about 50,000 Angstroms; and then (d) vapor plating a chromium protective layer onto said shielding layer of (c), said protective layer having a thickness of at least about 1,000 Angstroms; to provide a relatively low cost, durable, shielded panel for shielding the passage of electromagnetic radio frequency interference therethrough.
Claim 2
Independent Claim
186 words
A method of manufacturing a panel for shielding the passage of electromagnetic radio frequency interference therethrough, comprising: (a) subjecting a surface of an electrically insulating substrate sheet material to glow-discharge treatment to provide an active surface that is chemically reactive with vapors of chromium or stainless steel at an air pressure less than about 5×10 -5 TORR; (b) vapor plating chromium or stainless steel onto said active surface to provide an adhesive layer of chromium or stainless steel chemically bound to said surface, said layer having a thickness within the range of about 300 Angstroms to about 1,000 Angstroms; (c) vapor plating an aluminum or copper shielding layer onto the adhesive layer of (b) prior to substantial oxidation of the adhesive layer surface, said shielding layer having a thickness within the range of about 1,000 Angstroms to about 50,000 Angstroms; and then (d) vapor plating a chromium protective layer onto said shielding layer of (c), said protective layer having a thickness of at least about 1,000 Angstroms; to provide a relatively low cost, durable, shielded panel for shielding the passage of electromagnetic radio frequency interference therethrough.
Claim 3
Dependent Claim
39 words
The method of manufacturing the panel in claim 1 wherein the surface in (a) is glow-discharge treated in air at a pressure of 100 to 200 microns of mercury with a plasma voltage of about 1,000 to 2,000 volts.
Claim 4
Dependent Claim
30 words
The method of manufacturing the panel in claim 10 wherein in (b), (c), and (d) the vapor plating is at an air pressure of less than about 5×10 -5 TORR.
Claim 5
Dependent Claim
31 words
The method of manufacturing the panel in claim 1 wherein said adhesive layer in (b) is comprised of chromium having a thickness within the range of about 300 to 500 Angstroms.
Claim 6
Dependent Claim
29 words
The method of manufacturing the panel in claim 4 wherein said shielding layer is comprised of copper having a thickness within the range of about 2,000 to 10,000 Angstroms.
Claim 7
Dependent Claim
29 words
The method of manufacturing the panel in claim 5 wherein said protective layer is comprised of chromium having a thickness within the range of about 2,000 to 5,000 Angstroms.
Claim 8
Dependent Claim
32 words
The method of manufacturing the panel in claim 1, 2, 3, 4, 5, or 6 wherein said substrate sheet material is selected from the group of materials consisting of plastic and ceramic.
Claim 9
Dependent Claim
31 words
The method of manufacturing the panel in claim 7 wherein said substrate sheet material is a plastic selected from the group consisting of polyphenylene, polyimide, polyacrylonitrile-butadienestyrene (ABS), polyester, polyamide, and polycarbonate.
Claim 10
Dependent Claim
14 words
The method of manufacturing the panel in claim 7 wherein said ceramic is glass.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-09-30 | 1989-04-01 | 1989-10-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-09-30 | 1993-04-01 | 1993-10-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-09-30 | 1997-04-01 | 1997-10-01 | $7700.00 | Window Closed / Lapsed |