Processing silicon nitride by use of boron nitride as a barrier layer
Assignee: Osram Sylvania Inc
•
Filing: 1984-05-09
•
Granted: 1985-09-17
•
Expires: 2004-05-09
Abstract
Abstract A process is disclosed for producing a ceramic body coated with boron nitride. A green ceramic body is coated with boron nitride and sintered at a temperature and for a time sufficient for the body to achieve near theoretical density. Ceramic bodies of near theoretical density can be produced without deformation by coating the bodies with boron nitride, assembling the bodies with a supporting ceramic member which is also coated with boron nitride, sintering the assembly at a temperature and for a time for the bodies to achieve near theoretical density without deformation.
Inventors
- 👤 Martin Y. Hsieh
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 06:18
CPC Classifications
C; C04; C04B; C04B41/00; C04B41/009; C04B35/00; C04B35/515; C04B35/58; C04B35/584; C04B35/622; C04B35/64; C04B41/45; C04B41/50; C04B41/5053; C04B41/5062; C04B41/5064; C04B41/80; C04B41/81; C04B41/85; C04B41/87
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
84 words
A process suitable for preventing the deformation of ceramic bodies said process comprising: (a) forming a green ceramic body having a portion that during sintering deforms if unsupported, (b) forming at least one ceramic member suitable for providing support to said portion, (c) coating said body and said member with boron nitride, (d) assembling said body and said member whereby said member provides support for said portion and (e) sintering the resulting assembly at a temperature for said body to achieve near theoretical density.
Claim 2
Dependent Claim
84 words
A process suitable for preventing the deformation of ceramic bodies said process comprising: (a) forming a green ceramic body having a portion that during sintering deforms if unsupported, (b) forming at least one ceramic member suitable for providing support to said portion, (c) coating said body and said member with boron nitride, (d) assembling said body and said member whereby said member provides support for said portion and (e) sintering the resulting assembly at a temperature for said body to achieve near theoretical density.
Claim 3
Dependent Claim
73 words
An article consisting essentially of body consisting essentially of from about 80% to about 97.5% by weight of silicon nitride and from about 2.5% to about 20% of a sintering aid selected from the group consisting of yttrium oxide, aluminum oxide, magnesium oxide, lanthanum oxide and mixtures thereof and a coating having a thickness of from 0.5 to about 10 mils of boron nitride relatively uniformly distributed over the surface of said body.
Claim 4
Dependent Claim
73 words
An article consisting essentially of body consisting essentially of from about 80% to about 97.5% by weight of silicon nitride and from about 2.5% to about 20% of a sintering aid selected from the group consisting of yttrium oxide, aluminum oxide, magnesium oxide, lanthanum oxide and mixtures thereof and a coating having a thickness of from 0.5 to about 10 mils of boron nitride relatively uniformly distributed over the surface of said body.
Claim 5
Dependent Claim
45 words
A process for producing a ceramic body coated with a boron nitride coating composition comprising coating a green ceramic body with boron nitride and sintering said green ceramic body at a temperature and for a time sufficient for said body to achieve near theoretical density.
Claim 6
Dependent Claim
45 words
A process for producing a ceramic body coated with a boron nitride coating composition comprising coating a green ceramic body with boron nitride and sintering said green ceramic body at a temperature and for a time sufficient for said body to achieve near theoretical density.
Claim 7
Dependent Claim
24 words
A process according to claim 1 wherein the ceramic body is made from material selected from the group consisting of silicon nitride and sialon.
Claim 8
Dependent Claim
27 words
A process according to claim 1 wherein the ceramic body material contains sintering aids selected from the group consisting of yttrium oxide, aluminum oxide, and lanthanum oxide.
Claim 9
Dependent Claim
60 words
A process according to claim 1 wherein the ceramic material consists essentialy of by weight: (a) from about 0.5% to about 4% aluminum oxide, from about 2% to about 14% yttrium oxide and the balance silicon nitride and (b) from about 0.5% to about 5% aluminum oxide, from about 2% to about 15% lanthanum oxide, and the balance silcion nitride.
Claim 10
Dependent Claim
61 words
An article according to claim 2 consisting essentially of a body consisting essentially of by weight: (a) from about 0.5% to about 4% aluminum oxide, from about 2% to about 14% yttrium oxide and the balance silicon nitride, and (b) from about 0.5% to about 5% aluminum oxide, from about 2% to about 15% lanthanum oxide, and the balance silicon nitride.
Claim 11
Dependent Claim
42 words
A process according to claim 3 wherein the boron nitride coating composition consists essentially of boron nitride powder, ammonium citrate, water, and a binder selected from the group consisting of a water dipsersible alkyd resins, polyvinyl alcohol, polyurethane, polyglycols and mixtures thereof.
References Cited (Backward Citations)
US4485143A
Cited
US4447283A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-09-16 | 1989-03-18 | 1989-09-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-09-16 | 1993-03-18 | 1993-09-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-09-16 | 1997-03-18 | 1997-09-17 | $7700.00 | Window Closed / Lapsed |