Process for the preparation of a composite material and composite material obtained by this process
Assignee: Commissariat à l'Énergie Atomique et Aux Énergies Alternatives
•
Filing: 1982-07-26
•
Granted: 1985-09-17
•
Expires: 2002-07-26
Abstract
Abstract Process for the preparation of a composite material incorporating an inorganic matrix in which are distributed inclusions of carbon-containing material, where it comprises the following stages: (a) mixing an inorganic powder with a liquid or viscous resin, which can be transformed into vitreous carbon by heat treatment, (b) subjecting the mixture of resin and inorganic powder to a first heat treatment performed under conditions such that the resin is hardened by crosslinking or polycondensation, and (c) subjecting the thus obtained hardened product to a second heat treatment for transforming the resin into vitreous carbon and thus forming said vitreous carbon inclusions. The composite material obtained comprises a copper matrix in which are uniformly and homogeneously dispersed vitreous carbon inclusions, the vitreous carbon content being at the most 8% by weight. The material is used in the production of electric contacts.
Inventors
- 👤 Jacques Devillard
- 👤 Jean Granier
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 20:34
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/52; C04B35/524; C22; C22C; C22C32/00; C22C32/0084; H; H01; H01H; H01H1/00; H01H1/02; H01H1/021; H01H1/025; H01H1/027
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
183 words
A process for the preparation of a composite material having an inorganic matrix and inclusions of carbon-containing material distributed in said matrix comprising the following steps: (a) mixing an inorganic frittable powder with a liquid or viscous resin which can be transformed into vitreous carbon by heat treatment, said inorganic powder being selected from the group consisting of metals, metal alloys, oxides, carbides, nitrides, cermets and mixtures thereof, said resin being obtained from phenol and aldehyde reactants, the mixture of resin and inorganic powder thus obtained containing at the most 20% by weight of resin, (b) subjecting the mixture of resin and inorganic powder to a first heat treatment performed at a temperature at the most equal to 350° C. for 1 to 3 hours such that the resin is hardened by crosslinking or polycondensation, and (c) subjecting the thus obtained hardened product to a second heat treatment performed under vacuum or in a neutral atmosphere at a temperature of 600° to 1100° C. for 30 to 50 hours for transforming the resin into vitreous carbon and thus forming said vitreous carbon inclusions.
Claim 2
Dependent Claim
183 words
A process for the preparation of a composite material having an inorganic matrix and inclusions of carbon-containing material distributed in said matrix comprising the following steps: (a) mixing an inorganic frittable powder with a liquid or viscous resin which can be transformed into vitreous carbon by heat treatment, said inorganic powder being selected from the group consisting of metals, metal alloys, oxides, carbides, nitrides, cermets and mixtures thereof, said resin being obtained from phenol and aldehyde reactants, the mixture of resin and inorganic powder thus obtained containing at the most 20% by weight of resin, (b) subjecting the mixture of resin and inorganic powder to a first heat treatment performed at a temperature at the most equal to 350° C. for 1 to 3 hours such that the resin is hardened by crosslinking or polycondensation, and (c) subjecting the thus obtained hardened product to a second heat treatment performed under vacuum or in a neutral atmosphere at a temperature of 600° to 1100° C. for 30 to 50 hours for transforming the resin into vitreous carbon and thus forming said vitreous carbon inclusions.
Claim 3
Dependent Claim
29 words
A process according to claim 1, wherein before carrying out the first heat treatment, the mixture of resin and powder undergoes shaping by cold compression to obtain a preform.
Claim 4
Dependent Claim
18 words
A process according to claims 1 or 2, wherein the inorganic powder is an alloy or metal powder.
Claim 5
Dependent Claim
14 words
A process according to claim 3, wherein the inorganic powder is a copper powder.
Claim 6
Dependent Claim
19 words
A process according to claim 1, wherein the resin is obtained by the polycondensation of phenol and aldehyde reactants.
Claim 7
Dependent Claim
14 words
A process according to claim 5, wherein the resin is a phenol formaldehyde resin.
Claim 8
Dependent Claim
26 words
A process according to claim 1, wherein the composite material incorporating the vitreous carbon inclusions obtained at the end of the second heat treatment undergoes densification.
Claim 9
Dependent Claim
14 words
A process according to claim 7, wherein this densification is performed by hot spinning.
Claim 10
Dependent Claim
60 words
A process according to claim 1, wherein graphite powder is added to the liquid resin and the composite material incorporating the vitreous carbon inclusions obtained at the end of the second heat treatment undergoes a complementary graphitization heat treatment performed at a temperature of at the most 2200° C. for at least partly transforming the vitreous carbon inclusions into graphite.
Claim 11
Dependent Claim
51 words
A process according to claim 1, wherein the composite material obtained at the end of the second heat treatment undergoes a complementary treatment in order to at least partly react to the carbon of the inclusions with the inorganic matrix and thus form inclusions of carbide dispersed in the said matrix.
Claim 12
Dependent Claim
14 words
A process according to claim 1, wherein the resin is a phenol formaldehyde resin.
Claim 13
Dependent Claim
19 words
A process according to claim 1, wherein the inorganic powder is an oxide, a carbide or a nitride powder.
Claim 14
Dependent Claim
13 words
A process according to claim 12, wherein the inorganic powder is boron nitride.
Claim 15
Dependent Claim
14 words
A process according to claim 12, wherein the inorganic powder is a cermet powder.
Claim 16
Dependent Claim
15 words
A process according to claim 7, wherein this densification is performed by hot isostatic compression.
Claim 17
Dependent Claim
61 words
A process according to claim 1, wherein boron nitride powder is added to the liquid resin and the composite material incorporating the vitreous carbon inclusions obtained at the end of the second heat treatment undergoes a complementary graphitization heat treatment performed at a temperature of at the most 2200° C. for at least partly transforming the vitreous carbon inclusions into graphite.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-09-16 | 1989-03-18 | 1989-09-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-09-16 | 1993-03-18 | 1993-09-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-09-16 | 1997-03-18 | 1997-09-17 | $7700.00 | Window Closed / Lapsed |