Metal oxide varistor made by a co-precipation process and freeze-dried
Assignee: Toshiba Corp
•
Filing: 1983-06-22
•
Granted: 1985-09-10
•
Expires: 2003-06-22
Abstract
Abstract A metal oxide varistor is disclosed which a component of grain bodies comprised of zinc oxide and a component of grain boundary layers comprised of another metallic oxide, containing metal other than zinc wherein at least a portion of these starting materials comprised a fine particle powder prepared by a co-precipitatin method. The metal oxide varistor of the present invention is excellent in varistor characteristics such as non-linearity to voltage, life performances and capability of energy dissipation, is small in a scatter of the above characteristics between manufacture lots or within each lot at the time of manufacture, and has a good quality stability. Unexpected results are obtained when the co-precipitated fine particles are subjected to a refrigeration-dehydration type process.
Inventors
- 👤 Hideyuki Kanai
- 👤 Takashi Takahashi
- 👤 Motomasa Imai
- 👤 Osamu Furukawa
- 👤 Hiroshi Endo
- 👤 Osamu Hirao
- 👤 Masaru Hayashi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 17:22
CPC Classifications
H; H01; H01C; H01C7/00; H01C7/10; H01C7/105; H01C7/108; H01C7/112; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49082
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
109 words
A metal oxide varistor comprising a component of grain bodies comprised of zinc oxide and a component of grain boundary layers comprised of at least one metallic oxide containing metal other than zinc, wherein at least a portion of at least one of said zinc oxide and said metallic oxide comprises a fine particle powder prepared by a co-precipitation method consisting essentially of the steps of (a) preparing an aqueous solution comprising at least two metal ions; (b) by adding a base, forming a co-precipitate comprising substantially all of said metal ions in the form of corresponding metallic oxides; and thereafter (c) carrying out refrigerating dehydration of said co-precipitate.
Claim 2
Dependent Claim
109 words
A metal oxide varistor comprising a component of grain bodies comprised of zinc oxide and a component of grain boundary layers comprised of at least one metallic oxide containing metal other than zinc, wherein at least a portion of at least one of said zinc oxide and said metallic oxide comprises a fine particle powder prepared by a co-precipitation method consisting essentially of the steps of (a) preparing an aqueous solution comprising at least two metal ions; (b) by adding a base, forming a co-precipitate comprising substantially all of said metal ions in the form of corresponding metallic oxides; and thereafter (c) carrying out refrigerating dehydration of said co-precipitate.
Claim 3
Dependent Claim
35 words
A metal oxide varistor according to claim 1, wherein said metal ion in said first aqueous solution comprises at least one selected from the group consisting of antimony, bismuth, cobalt, manganese, nickel, chromium and silicon.
Claim 4
Dependent Claim
35 words
A metal oxide varistor according to claim 1, wherein said fine particle powder prepared by said co-precipitation method comprises between about 0.4 to about 100% by weight of all metallic oxides comprising said metal varistor.
Claim 5
Dependent Claim
125 words
A metal oxide varistor according to claim 1, wherein at least a portion of both of said zinc oxide and said metallic oxide comprises a fine particle powder prepared by said co-precipitation method comprising the steps of (a) preparing (i) a first aqueous solution comprising at least one metallic salt containing a metal ion other than zinc and (ii) a third aqueous solution comprising a metallic salt containing zinc ion; (b 1 ) forming a second aqueous solution by homogeneously mixing said first and third aqueous solution; and (b 2 ) adding said base to said second solution in sufficient amounts to form a co-precipitate from said second solution, said co-precipitate comprising substantially all of said zinc ion and said metal ion other than zinc.
Claim 6
Dependent Claim
33 words
A metal oxide varistor as in claim 4, wherein said metal ion other than zinc comprises at least one selected from the group consisting of antimony, bismuth, cobalt, manganese, nickel, chromium, and silicon.
Claim 7
Dependent Claim
24 words
A metal oxide varistor according to claim 1, wherein said refrigerating dehydration is carried out at a temperature of about -25° C. or less.
Claim 8
Dependent Claim
67 words
A process for manufacturing a metal oxide varistor, consisting essentially of the steps of (a) preparing an aqueous solution comprising at least two ions; (b) by adding a base, forming a co-precipitate comprising substantially all of said metal ions in the form of corresponding metallic oxides; then (c) carrying out refrigerating dehydration of said co-precipitate; and (d) molding said co-precipitate under pressure to form a compact body.
Claim 9
Dependent Claim
67 words
A process for manufacturing a metal oxide varistor, consisting essentially of the steps of (a) preparing an aqueous solution comprising at least two ions; (b) by adding a base, forming a co-precipitate comprising substantially all of said metal ions in the form of corresponding metallic oxides; then (c) carrying out refrigerating dehydration of said co-precipitate; and (d) molding said co-precipitate under pressure to form a compact body.
Claim 10
Dependent Claim
109 words
A process according to claim 7, comprising the steps of (a) preparing (i) a first aqueous solution comprising at least one metallic salt containing a metal ion other than zinc and (ii) a third aqueous solution comprising a metallic salt containing zinc ion; (b 1 ) forming said second aqueous solution by homogeneously mixing said first and third aqueous solutions; (b 2 ) adding said base to said second solution in sufficient amounts to form a co-precipitate from said second solution, said precipitate comprising substantially all of said zinc ion and said metal ion other than zinc; and (c) molding said co-precipitate under pressure to form a compact body.
Claim 11
Dependent Claim
22 words
A process according to claim 7 wherein said refrigerating dehydration is carried out at a temperature of about -25° C. or less.
Claim 12
Dependent Claim
73 words
A fine particle powder consisting essentially of metallic oxides, formed by a co-precipitation method consisting essentially of the steps of (a) preparing an aqueous solution comprising at least two metal ions; (b) by adding a base, forming a co-precipitate comprising substantially all of said metal ions in the form of corresponding metallic oxide; and then (c) carrying out refrigerating dehydration of said co-precipitate, said co-precipitate being adapted for manufacturing metallic oxide varistors therefrom.
Claim 13
Dependent Claim
73 words
A fine particle powder consisting essentially of metallic oxides, formed by a co-precipitation method consisting essentially of the steps of (a) preparing an aqueous solution comprising at least two metal ions; (b) by adding a base, forming a co-precipitate comprising substantially all of said metal ions in the form of corresponding metallic oxide; and then (c) carrying out refrigerating dehydration of said co-precipitate, said co-precipitate being adapted for manufacturing metallic oxide varistors therefrom.
Claim 14
Dependent Claim
104 words
A fine particle powder as in claim 10, wherein said co-precipitation method comprises the steps of (a) preparing (i) a first aqueous solution comprising at least one metallic salt containing a metal ion other than zinc and (ii) a third aqueous solution comprising a metallic salt containing zinc ion; (b 1 ) forming a second aqueous solution by homogeneously mixing said first and third aqueous solutions; and (b 2 ) adding said base to said second solution in sufficient amounts to form a co-precipitate from said second solution, said co-precipitate comprising substantially all of said zinc ion and said metal ion other than zinc.
Claim 15
Dependent Claim
24 words
A fine particle powder according to claim 10, wherein said refrigerating dehydration is carried out at a temperature of about -25° C. or less.
References Cited (Backward Citations)
JPS49118661A
Cited
US4097392A
Cited
DE2526137A1
Cited
US4142996A
Cited
JPS5480595A
Cited
DE2910841A1
Cited
JPS56101711A
Cited
US4318995A
Cited
US4372865A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-09-09 | 1989-03-11 | 1989-09-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-09-09 | 1993-03-11 | 1993-09-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-09-09 | 1997-03-11 | 1997-09-10 | $7700.00 | Window Closed / Lapsed |