High solids, high heat resistant polyester resins and coating compositions containing the same
Assignee: Valspar Corp
•
Filing: 1984-05-14
•
Granted: 1985-09-10
•
Expires: 2004-05-14
Abstract
Abstract The production of novel polyester resins is disclosed as is the preparation of high solids coatings and paints containing the same. The polyester resins are produced by reacting a mixture comprising: (a) A saturated fatty acid having from 8 to 18 carbon atoms in an amount between about 3 and about 8 percent; (b) A polyol in an amount between 40 and 50 percent, said polyol consisting of between about 55 and 75 percent of a triol with the remainder being a diol; (c) A polycarboxylic acid in an amount of about 45 to about 55 percent, said polycarboxylic acid consisting of between 65 and 75 percent of an aromatic polycarboxylic acid with the remainder being aliphatic acid having from 4 to 10 carbon atoms. The coatings and paints are preferably prepared by reacting the polyester resin with an aminoplast resin to cause cross-linking.
Inventors
- 👤 Conrad L. Lynch
- 👤 Michael A. Tobias
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 08:14
CPC Classifications
C; C08; C08G; C08G63/00; C08G63/02; C08G63/12; C08G63/46; C08G63/48; C09; C09D; C09D167/00; C09D167/08
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
132 words
The polyester resin obtained by the esterification of: (a) a saturated fatty acid having 8 to 18 carbon atoms in an amount by weight between about 3 and about 8 percent of the total weight of (a), (b) and (c); (b) a polyol in an amount by weight between about 40 and about 50 percent, said polyol consisting of between about 55 and 75 percent of a triol with the remainder being a diol; and (c) a polycarboxylic acid in an amount of about 45 to about 55 percent, said carboxylic acid consisting of between 65 and 75 percent of an aromatic polycarboxylic acid with the remainder being an aliphatic polycarboxylic acid having from 4 to 10 carbon atoms, said polyester resin having a hydroxyl number from about 75 to about 175.
Claim 2
Dependent Claim
132 words
The polyester resin obtained by the esterification of: (a) a saturated fatty acid having 8 to 18 carbon atoms in an amount by weight between about 3 and about 8 percent of the total weight of (a), (b) and (c); (b) a polyol in an amount by weight between about 40 and about 50 percent, said polyol consisting of between about 55 and 75 percent of a triol with the remainder being a diol; and (c) a polycarboxylic acid in an amount of about 45 to about 55 percent, said carboxylic acid consisting of between 65 and 75 percent of an aromatic polycarboxylic acid with the remainder being an aliphatic polycarboxylic acid having from 4 to 10 carbon atoms, said polyester resin having a hydroxyl number from about 75 to about 175.
Claim 3
Dependent Claim
26 words
The polyester resin of claim 1, wherein said triol is selected from the group consisting of glycerine, trimethylol ethane, trimethylol propane, trimethylol butane, hexanetriol and pentanetriol.
Claim 4
Dependent Claim
43 words
The polyester resin of claim 1, wherein said diol is selected from the group consisting of ethylene glycol, 1,2- and 1,3-propylene glycol, 1,3- and 1,4-butylene glycol, 1,5-pentane diol, 1,6-hexane diol, cyclohexane dimethanol, 2-ethyl, 2-methyl, 1,3-propane diol, neopentyl glycol, diethylene glycol and dipropylene glycol.
Claim 5
Dependent Claim
23 words
The polyester resin of claim 1, wherein said aromatic polycarboxylic acid is selected from the group consisting of orthophthalic acid and isophthalic acid.
Claim 6
Dependent Claim
26 words
The polyester resin of claim 1, wherein said aliphatic polycarboxylic acid is selected from the group consisting of succinic, glutaric, adipic, suberic, azelaic and sebacic acids.
Claim 7
Dependent Claim
45 words
A high temperature-resisting coating composition obtained by the reaction of the polyester resin of claim 1 with an aminoplast resin in an amount from about 7 to about 30 percent by weight of the weight of said polyester and aminoplast resins and a solvent therefor.
Claim 8
Dependent Claim
8 words
The composition of claim 6 which contains pigment.
Claim 9
Dependent Claim
18 words
An article coated with the composition of claim 6 in which the coating has been cured by cross-linking.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-09-09 | 1989-03-11 | 1989-09-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-09-09 | 1993-03-11 | 1993-09-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-09-09 | 1997-03-11 | 1997-09-10 | $7700.00 | Window Closed / Lapsed |