Carbon molecular sieves and a process for their preparation and use
Assignee: Calgon Carbon Corp
•
Filing: 1983-12-13
•
Granted: 1985-09-10
•
Expires: 2003-12-13
Abstract
Abstract The instant invention is directed to a process for the continuous manufacturing of carbon molecular sieves having average effective pore diameters of from 2 to 15 Angstroms which comprises continuously feeding a charred naturally occurring substrate to a means for heating said substrate and heating said substrate under non-activation conditions, without the use of an externally added pore blocking substance, at a temperature range of about 900° F. (482° C.) to 2000° F. (1093° C.) for a time period of about 5 to 90 minutes. The instant invention is also directed to a carbon molecular sieve, useful for separating gas or liquid mixtures containing components of at least two different molecular diameters, molecular weights or molecular shapes which has the following physical characteristics: (a) an apparent density of from 0.60 to 0.70 g/cc, (b) an oxygen diffusivity (×10 -8 ) of from 500 to 900 cm 2 /sec, (c) an oxygen/nitrogen selectivity ratio of from 5.0 to 8.5 (d) an oxygen capacity of from 4.00 to 6.00 cc/cc, and (e) an average effective pore diameter of about 3 to 5 Angstroms.
Inventors
- 👤 Robert F. Sutt, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 06:25
CPC Classifications
C; C01; C01B; C01B32/00; C01B32/30; C01B32/306
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
98 words
A process for the continuous manufacturing of carbon molecular sieves having average effective pore diameters of from 2 to 15 Angstroms and an oxygen/nitrogen selectivity ratio of from 5.0 to 8.5 which comprises continuously feeding a charred naturally occurring substrate to a transport means for heating said substrate and heating said substrate at a maximum oxygen content of 500 ppm under non-activation conditions, without the use of an externally added pore blocking substance, at a temperature range of about 900° F. (482° C.) to 2000° F. (1093° C.) for a time period of about 5 to 90 minutes.
Claim 2
Dependent Claim
98 words
A process for the continuous manufacturing of carbon molecular sieves having average effective pore diameters of from 2 to 15 Angstroms and an oxygen/nitrogen selectivity ratio of from 5.0 to 8.5 which comprises continuously feeding a charred naturally occurring substrate to a transport means for heating said substrate and heating said substrate at a maximum oxygen content of 500 ppm under non-activation conditions, without the use of an externally added pore blocking substance, at a temperature range of about 900° F. (482° C.) to 2000° F. (1093° C.) for a time period of about 5 to 90 minutes.
Claim 3
Dependent Claim
28 words
The process of claim 1, wherein said naturally occurring substrate is selected from the group consisting of coconut char, babassu nut char, anthracite and high ranking bituminous coals.
Claim 4
Dependent Claim
11 words
The process of claim 1, wherein the substrate is coconut char.
Claim 5
Dependent Claim
28 words
The process of claim 1, wherein said temperature range is from about 1400° F. to 1900° F. and said time period is from about 5 to 30 minutes.
Claim 6
Dependent Claim
19 words
The process of claim 1, wherein said heating means is an electrically powered, infrared heated continuous transport type furnace.
Claim 7
Dependent Claim
12 words
The process of claim 1, wherein said substrate is an agglomerated substrate.
Claim 8
Dependent Claim
36 words
The process of claim 1, wherein said non-activation conditions include an oxygen-free environment of less than 100 ppm oxygen and an inert, countercurrent, gas purge at a linear velocity of 3.5 to 8.1 feet per minute.
Claim 9
Dependent Claim
22 words
The process of claim 1, wherein said carbon molecular sieves have an average effective pore diameter of about 3 to 5 Angstroms.
Claim 10
Dependent Claim
28 words
The process of claim 8, wherein said temperature range is from about 1800° F. to 1900° F. and the time period is from about 15 to 30 minutes.
Claim 11
Dependent Claim
26 words
The process of claim 8, wherein said substrate is selected from the group consisting of coconut shell, babassu nut shell, anthracite and high ranking bituminous coal.
Claim 12
Dependent Claim
9 words
The product produced by the process of claim 1.
Claim 13
Dependent Claim
89 words
A carbon molecular sieve, useful for separating gas or liquid mixtures containing components of at least two different molecular diameters, molecular weights or molecular shapes which has the following physical characteristics: (a) an apparent density of from 0.60 to 0.70 g/cc, (b) an oxygen diffusivity (×10 -8 ) of from 500 to 900 cm 2 /sec, (c) an oxygen/nitrogen selectivity ratio of from 5.0 to 8.5 (d) an oxygen capacity of from 4.00 to 6.00 cc/cc, and (e) an average effective pore diameter of about 3 to 5 Angstroms.
Claim 14
Dependent Claim
89 words
A carbon molecular sieve, useful for separating gas or liquid mixtures containing components of at least two different molecular diameters, molecular weights or molecular shapes which has the following physical characteristics: (a) an apparent density of from 0.60 to 0.70 g/cc, (b) an oxygen diffusivity (×10 -8 ) of from 500 to 900 cm 2 /sec, (c) an oxygen/nitrogen selectivity ratio of from 5.0 to 8.5 (d) an oxygen capacity of from 4.00 to 6.00 cc/cc, and (e) an average effective pore diameter of about 3 to 5 Angstroms.
Claim 15
Dependent Claim
49 words
A carbon molecular sieve of claim 12 which has the following physical characteristics: (a) an apparent density of from 0.64 to 0.70 g/cc, (b) an oxygen diffusivity (×10 -8 ) of from 650 to 750 cm 2 /sec, and (c) an oxygen/nitrogen selectivity ratio of from 7 to 7.5.
References Cited (Backward Citations)
US4420415A
Cited
GB2086867A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-09-09 | 1989-03-11 | 1989-09-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-09-09 | 1993-03-11 | 1993-09-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-09-09 | 1997-03-11 | 1997-09-10 | $7700.00 | Window Closed / Lapsed |