Procedure for making nickel electrodes
Assignee: Nokia Bell Labs
•
Filing: 1984-12-05
•
Granted: 1985-09-10
•
Expires: 2004-12-05
Abstract
Abstract A process is described for electrolytically producing nickel electrodes by subjecting a porous nickel structure (generally a nickel plaque) to alternating anodic and cathodic pulses in an aqueous halide (generally chloride) solution. The alternating pulses first anodically dissolve the nickel from the porous nickel plaque and then cathodically precipitate the nickel in the form of the hydroxide. Particularly attractive is the use of a stable, simple solution, room temperature operation and the broad variation in operating conditions (pH, etc.) that still produce optimum results.
Inventors
- 👤 Christopher K. Dyer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 18:07
CPC Classifications
H; H01; H01M; H01M4/00; H01M4/02; H01M4/36; H01M4/48; H01M4/52; H01M4/24; H01M4/26; H01M4/28; H01M4/29; H01M4/32; Y; Y02; Y02E; Y02E60/00; Y02E60/10; Y10; Y10S; Y10S204/00; Y10S204/09
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
134 words
A process for the fabrication of an aqueous battery cell in which the battery cell comprises at least one nickel electrode characterized in that the nickel electrode is made by a procedure comprising the step of exposing a conducting nickel structure to alternate anodic and cathodic potentials in an electrolytic solution with conductivity greater than 0.001 mho-cm, said alternating anodic and cathodic pulses occurring at a frequency between 0.01 and 100 Hz and which comprises ions that enhance dissolution of metallic nickel from the conducting nickel structure and cathodically reduce water to produce a sufficiently high hydroxide concentration to precipitate the anodically oxidized metallic nickel as active material and in which the conducting nickel structure is a porous nickel plaque, and the nickel in the active material originates only from the porous nickel plaque.
Claim 2
Dependent Claim
134 words
A process for the fabrication of an aqueous battery cell in which the battery cell comprises at least one nickel electrode characterized in that the nickel electrode is made by a procedure comprising the step of exposing a conducting nickel structure to alternate anodic and cathodic potentials in an electrolytic solution with conductivity greater than 0.001 mho-cm, said alternating anodic and cathodic pulses occurring at a frequency between 0.01 and 100 Hz and which comprises ions that enhance dissolution of metallic nickel from the conducting nickel structure and cathodically reduce water to produce a sufficiently high hydroxide concentration to precipitate the anodically oxidized metallic nickel as active material and in which the conducting nickel structure is a porous nickel plaque, and the nickel in the active material originates only from the porous nickel plaque.
Claim 3
Dependent Claim
26 words
The process of claim 1 in which the battery cell is selected from the group consisting of nickel-hydrogen cells, nickel-cadmium cells, nickel-zinc cells, and nickel-iron cells.
Claim 4
Dependent Claim
14 words
The process of claim 1 in which the electrolytic solution comprises a halide ion.
Claim 5
Dependent Claim
22 words
The process of claim 3 in which the halide ion is selected from the group consisting of bromide ion and chloride ion.
Claim 6
Dependent Claim
18 words
The process of claim 3 in which the concentration of halide ion is between 0.01 molar and saturation.
Claim 7
Dependent Claim
15 words
The process of claim 5 in which the concentration is between 0.1 and 2 molar.
Claim 8
Dependent Claim
30 words
The process of claim 6 in which the halide ion is chloride ion added in the form of KCl and the concentration of KCl is between 0.2 and 1.2 molar.
Claim 9
Dependent Claim
18 words
The process of claim 1 in which the pH of the electrolytic solution is between 3 and 10.
Claim 10
Dependent Claim
14 words
The process of claim 8 in which the pH is between 6.0 and 8.0.
Claim 11
Dependent Claim
15 words
The process of claim 1 in which the frequency is between 0.1 and 10 Hz.
Claim 12
Dependent Claim
15 words
The process of claim 10 in which the frequency is between 0.2 and 2 Hz.
Claim 13
Dependent Claim
28 words
The process of claim 1 in which the anodic potential is more positive than 0.1 volts (nhe) and the cathodic potential is more negative than 0.0 volts (nhe).
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-09-09 | 1989-03-11 | 1989-09-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-09-09 | 1993-03-11 | 1993-09-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-09-09 | 1997-03-11 | 1997-09-10 | $7700.00 | Window Closed / Lapsed |