Process for continuous recovery of nitric acid/hydrofluoric acid titanium etchant
Assignee: McDonnell Douglas Corp
•
Filing: 1984-06-11
•
Granted: 1985-09-10
•
Expires: 2004-06-11
Abstract
Abstract A process of continuously chemically milling refractory metals, e.g., titanium using a supersaturated milling solution which form a water soluble precipitate, milling at temperatures of 140°-160° F., and using two chemical milling tanks so that the milling solution is pumped from one to the other when the precipitate builds up in the first tank to a predetermined level. The water soluble precipitate is easily and inexpensively disposed of and the process makes more efficient use of chemicals.
Inventors
- 👤 Dolphus L. Coggins
- 👤 Walter E. Lindner
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 05:25
CPC Classifications
C; C23; C23F; C23F1/00; C23F1/08
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
49 words
A process for chemically milling titanium and its alloys comprising: (a) forming a chemically milling solution saturated in titanium in a first etch tank; (b) immersing titanium containing parts in the solution while maintaining the solution saturated in titanium; and (c) forming a water soluble precipitate in the tank;
Claim 2
Dependent Claim
49 words
A process for chemically milling titanium and its alloys comprising: (a) forming a chemically milling solution saturated in titanium in a first etch tank; (b) immersing titanium containing parts in the solution while maintaining the solution saturated in titanium; and (c) forming a water soluble precipitate in the tank;
Claim 3
Dependent Claim
16 words
The process of claim 1 wherein the chemical milling solution contains a derivative of carbonic acid.
Claim 4
Dependent Claim
36 words
The process of claim 1 wherein the process is continuous and including the step of transferring the etchant to a second tank after a predetermined amount of precipitate has been formed in the first etch tank.
Claim 5
Dependent Claim
85 words
The process of claim 3 including the step of removing the sludge from the first etch tank, chemically milling in the second etch tank under supersaturated conditions, terminating the chemical milling in the second etch tank at a predetermined level of precipitate, and transferring the remaining chemical milling solution back to the first etch tank and repeating the steps of chemically milling under supersaturated conditions, stopping chemical milling at a predetermining point, removing and dissolving precipitate and returning chemical milling solution to the second tank.
Claim 6
Dependent Claim
143 words
A process for continuously chemically milling titanium and its alloys comprising the steps of: (a) forming an etch solution containing a carbonic acid derivative in a first tank; (b) etching titanium parts in said first tank until the etchant is substantially saturated; (c) transferring the etchant to a second etch tank; (d) treating titanium parts in said second etch tank with the etchant substantially supersaturated; (e) terminating the chemical milling in the second tank when the sludge has built up to a predetermined point; (f) transferring the etchant to the first tank; (g) treating the sludge in the second tank with water to solubilize the part of the sludge which is (NH 4 ) 2 TiF 6 ; (h) separating the soluble part of the sludge from the insoluble parts; (i) neutralizing the soluble part; and (j) recovering titanium nitride as a precipitate.
Claim 7
Dependent Claim
143 words
A process for continuously chemically milling titanium and its alloys comprising the steps of: (a) forming an etch solution containing a carbonic acid derivative in a first tank; (b) etching titanium parts in said first tank until the etchant is substantially saturated; (c) transferring the etchant to a second etch tank; (d) treating titanium parts in said second etch tank with the etchant substantially supersaturated; (e) terminating the chemical milling in the second tank when the sludge has built up to a predetermined point; (f) transferring the etchant to the first tank; (g) treating the sludge in the second tank with water to solubilize the part of the sludge which is (NH 4 ) 2 TiF 6 ; (h) separating the soluble part of the sludge from the insoluble parts; (i) neutralizing the soluble part; and (j) recovering titanium nitride as a precipitate.
Claim 8
Dependent Claim
23 words
The process of claim 5 including the step of removing the sludge in the first tank prior to returning the etchant to it.
Claim 9
Dependent Claim
35 words
The process of claim 5 including the step of repeating steps (d) and (e) in the first tank, returning the etchant to the second tank, and repeating steps (g) to (j) in the first tank.
Claim 10
Dependent Claim
16 words
The process of claim 5 wherein the chemical milling solution is at 140°-160° F. during milling.
References Cited (Backward Citations)
US3052582A
Cited
US3666580A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-09-09 | 1989-03-11 | 1989-09-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-09-09 | 1993-03-11 | 1993-09-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-09-09 | 1997-03-11 | 1997-09-10 | $7700.00 | Window Closed / Lapsed |