Pretreatment method for increasing conversion of reforming catalyst
Assignee: Chevron USA Inc
•
Filing: 1984-03-08
•
Granted: 1985-09-03
•
Expires: 2004-03-08
Abstract
Abstract A pretreatment process is disclosed for increasing conversion of reforming catalysts wherein the catalyst is treated at from 120° C. to 260° C.; then the temperature of the treated catalyst is maintained at a temperature of from 370° C. to 600° C. in a reducing atmosphere prior to starting the hydrocarbon feed. Preferably, the catalyst is treated in the presence of hydrogen at atmospheric pressure for at least twenty minutes; then the temperature of the treated catalyst is maintained at 475° C. in a reducing atmosphere for at least ten minutes prior to starting the hydrocarbon feed.
Inventors
- 👤 Leslie A. Field
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 15:08
CPC Classifications
C; C10; C10G; C10G35/00; C10G35/04; C10G35/06; C10G35/095; B; B01; B01J; B01J29/00; B01J29/04; B01J29/06; B01J29/08; B01J29/10; B01J29/12; B01J29/60; B01J29/61; B01J29/62
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
38 words
A method of pretreating a catalyst comprising: (a) treating said catalyst at from 120° C. to 260° C.; and (b) maintaining the temperature of the treated catalyst at from 370° C. to 600° C. in a reducing atmosphere.
Claim 2
Independent Claim
38 words
A method of pretreating a catalyst comprising: (a) treating said catalyst at from 120° C. to 260° C.; and (b) maintaining the temperature of the treated catalyst at from 370° C. to 600° C. in a reducing atmosphere.
Claim 3
Dependent Claim
27 words
A method of pretreating a catalyst according to claim 1 wherein step (a) occurs in the presence of hydrogen at atmospheric pressure for at least twenty minutes.
Claim 4
Dependent Claim
26 words
A method of pretreating a catalyst according to claim 2 wherein step (b) occurs in the presence of hydrogen for from ten minutes to 24 hours.
Claim 5
Dependent Claim
18 words
A method of pretreating a catalyst according to claim 3 wherein step (b) occurs for about ten minutes.
Claim 6
Dependent Claim
24 words
A method of pretreating a catalyst according to claim 1 wherein said catalyst comprises a large-pore zeolite containing at least one Group VIII metal.
Claim 7
Dependent Claim
17 words
A method of pretreating a catalyst according to claim 5 wherein said Group VIII metal is platinum.
Claim 8
Dependent Claim
25 words
A method of pretreating a catalyst according to claim 5 wherein said large-pore zeolite has an apparent pore size of from 7 to 9 Angstroms.
Claim 9
Dependent Claim
29 words
A method of pretreating a catalyst according to claim 7 wherein said large-pore zeolite is selected from the group consisting of zeolite X, zeolite Y, and type L zeolite.
Claim 10
Dependent Claim
19 words
A method of pretreating a catalyst according to claim 8 wherein said large-pore zeolite is a type L zeolite.
Claim 11
Dependent Claim
25 words
A method of pretreating a catalyst according to claim 1 wherein said catalyst comprises: (a) a large-pore zeolite containing platinum; and (b) an inorganic binder.
Claim 12
Dependent Claim
26 words
A method of pretreating a catalyst according to claim 10 wherein said inorganic binder is selected from the group consisting of silica, alumina, aluminosilicates, and clays.
Claim 13
Dependent Claim
82 words
A method of pretreating a catalyst according to claim 1 comprising: (a) reducing said catalyst in the presence of hydrogen at a temperature of 200° C. for at least twenty minutes; and (b) maintaining the temperature of the reduced catalyst at about 475° C. for at least ten minutes; wherein said catalyst comprises: (1) a type L zeolite containing from 0.1% to 1.5% by weight platinum; and (2) an inorganic binder selected from the group consisting of silica, alumina, aluminosilicates, and clays.
Claim 14
Dependent Claim
28 words
A method of pretreating a catalyst according to claim 5 wherein said catalyst contains an alkaline earth metal selected from the group consisting of barium, strontium, and calcium.
Claim 15
Dependent Claim
25 words
A method of pretreating a catalyst according to claim 13 wherein said alkaline earth metal is barium and wherein said Group VIII metal is platinum.
Claim 16
Dependent Claim
29 words
A method of pretreating a catalyst according to claim 14 wherein said catalyst has from 8% to 10% by weight barium and from 0.1% to 1.5% by weight platinum.
Claim 17
Independent Claim
86 words
A method of pretreating a catalyst comprising: (a) reducing said catalyst in the presence of hydrogen at a temperature of 200° C. for at least twenty minutes; and (b) maintaining the temperature of the reduced catalyst at about 475° C. for at least ten minutes; wherein said catalyst comprises: (1) a type L zeolite containing from 8% to 10% by weight barium and from 0.1% to 1.5% by weight platinum; and (2) an inorganic binder selected from the group consisting of silica, alumina, aluminosilicates, and clays.
Claim 18
Independent Claim
86 words
A method of pretreating a catalyst comprising: (a) reducing said catalyst in the presence of hydrogen at a temperature of 200° C. for at least twenty minutes; and (b) maintaining the temperature of the reduced catalyst at about 475° C. for at least ten minutes; wherein said catalyst comprises: (1) a type L zeolite containing from 8% to 10% by weight barium and from 0.1% to 1.5% by weight platinum; and (2) an inorganic binder selected from the group consisting of silica, alumina, aluminosilicates, and clays.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-09-02 | 1989-03-04 | 1989-09-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-09-02 | 1993-03-04 | 1993-09-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-09-02 | 1997-03-04 | 1997-09-03 | $7700.00 | Window Closed / Lapsed |