Method and apparatus for producing blends of resinous, thermoplastic fiber, and laminated structures produced therefrom
Assignee: Textile Products Inc
•
Filing: 1983-09-06
•
Granted: 1985-09-03
•
Expires: 2003-09-06
Abstract
Abstract Reinforced structures of graphite, fiberglass, and the like, together with thermoplastic resinous fibers such as in ribbon, filament and monofilament form are produced. The graphite fiber is combined or blended with a resinous fiber to form a single yarn. The blended yarn is then woven into a soft, supple and flexible fabric having the appropriate concentration of graphite and resin, and with good uniform characteristics. Hybrid fabrics produced by interweaving graphite and the polymeric fibers, ribbon, etc., may be utilized instead of the blended yarn. The fabric is finally shaped to conform with a mold or substrate and heated to melt the resin and produce the resin-graphite laminate.
Inventors
- 👤 Frederick H. Curzio
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 22:51
CPC Classifications
B; B29; B29C; B29C70/00; B29C70/04; B29C70/06; B29C70/10; B29C70/16; B29B; B29B15/00; B29B15/08; B29B15/10; B29B15/12; C; C08; C08J; C08J5/00; C08J5/04; C08J5/047; C08J5/048; D; D02; D02G; D02G3/00; D02G3/22; D02G3/40; D02G3/402; D03; D03D; D03D15/00; D03D15/20; D03D15/242; D03D15/247; D03D15/267; D03D15/275; D03D15/283; D03D15/40; D03D15/47; D03D15/50; D03D15/587; D10; D10B; D10B2101/00; D10B2101/02; D10B2101/08; D10B2101/10; D10B2101/12; D10B2101/20; D10B2321/00; D10B2321/02; D10B2321/022; D10B2331/00; D10B2331/02; D10B2331/021; D10B2331/04; D10B2331/06; D10B2331/061; D10B2401/00; D10B2401/04; D10B2401/041; D10B2505/00; D10B2505/02; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24628; Y10T428/24636; Y10T428/29; Y10T428/2913; Y10T428/2918; Y10T428/30; Y10T442/00; Y10T442/30; Y10T442/3179; Y10T442/322; Y10T442/3228; Y10T442/3236; Y10T442/3252; Y10T442/3293
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
161 words
A process for producing laminates from graphite fibers, and the like, and a plurality of resinous thermoplastic fibers, comprising: (a) combining or blending the graphite and thermoplastic fibers into yarn; (b) controlling the graphite/resin weight ratio during the blending step; (c) weaving the yarn into a flexible, dry fabric adapted for dry storage without refrigeration in which adjacent thermoplastic fibers or yarn, and graphite fibers, and the like, are adapted for sufficient movement relative to each other, thereby enabling the fabric to be conformed to a mold or substrate, the yarn and fibers having a controlled alignment in the fabric due to weaving or blending; (d) shaping the fabric in a dry, solvent-free form by conforming the fabric onto said mold or substrate; and, (e) heating the fabric under pressure to melt the resin and produce a shaped, graphite-resin laminate in which the graphite and resin are intimately combined in the laminate at the controlled graphite/resin ratio to produce uniform characteristics.
Claim 2
Dependent Claim
161 words
A process for producing laminates from graphite fibers, and the like, and a plurality of resinous thermoplastic fibers, comprising: (a) combining or blending the graphite and thermoplastic fibers into yarn; (b) controlling the graphite/resin weight ratio during the blending step; (c) weaving the yarn into a flexible, dry fabric adapted for dry storage without refrigeration in which adjacent thermoplastic fibers or yarn, and graphite fibers, and the like, are adapted for sufficient movement relative to each other, thereby enabling the fabric to be conformed to a mold or substrate, the yarn and fibers having a controlled alignment in the fabric due to weaving or blending; (d) shaping the fabric in a dry, solvent-free form by conforming the fabric onto said mold or substrate; and, (e) heating the fabric under pressure to melt the resin and produce a shaped, graphite-resin laminate in which the graphite and resin are intimately combined in the laminate at the controlled graphite/resin ratio to produce uniform characteristics.
Claim 3
Dependent Claim
47 words
The process of claim 1, in which the graphite fibers and the like, are selected from the class consisting of: graphite, fiberglass, ceramic, quartz, boron, and SiC, and the polymeric fibers are selected from the class consisting of polyethylene, aramid, polypropylene, polyester, nylon, and polyether ether ketone.
Claim 4
Dependent Claim
23 words
The process of claim 2, in which reinforcing fibers selected from the class consisting of aluminum and steel are woven into the fabric.
Claim 5
Dependent Claim
20 words
The process of claim 1, in which an overwrapping of fiber is applied to the yarn during the combining step.
Claim 6
Dependent Claim
24 words
The process of claim 1, in which a hybrid fabric is formed by interweaving thermoplastic fibers or ribbon with graphite fibers, and the like.
Claim 7
Dependent Claim
20 words
The process of claim 5, in which the thermoplastic ribbon is about 3/4-5 mils thick and about 60-70 mils wide.
Claim 8
Dependent Claim
24 words
The process of claim 1, in which the graphite fibers, and the like are mechanically separated before they are combined with the polymeric fibers.
Claim 9
Dependent Claim
162 words
A woven fabric for conversion into a laminate, the fabric being produced by: (a) combining or blending graphite and resinous thermoplastic fibers into yarn; (b) controlling the graphite/resin weight ratio during blending: and, (c) weaving the yarn into a flexible, dry fabric adapted for dry storage without refrigeration in which adjacent thermoplastic fibers or yarn, and graphite fibers, and the like, are adapted for sufficient movement relative to each other, thereby enabling the fabric to be conformed to a mold or substrate, the yarn and fibers having a controlled alignment in the fabric due to weaving or blending; whereby, i. the fabric is adapted to be shaped in a dry, solvent-free form by conforming the fabric onto said mold or substrate; ii. the resin in the fabric is adapted to melt under heat and pressure to produce a graphite-resin laminate; and, iii. the graphite and resin are intimately combined in the laminate at the controlled graphite/resin weight ratio to produce uniform characteristics.
Claim 10
Dependent Claim
162 words
A woven fabric for conversion into a laminate, the fabric being produced by: (a) combining or blending graphite and resinous thermoplastic fibers into yarn; (b) controlling the graphite/resin weight ratio during blending: and, (c) weaving the yarn into a flexible, dry fabric adapted for dry storage without refrigeration in which adjacent thermoplastic fibers or yarn, and graphite fibers, and the like, are adapted for sufficient movement relative to each other, thereby enabling the fabric to be conformed to a mold or substrate, the yarn and fibers having a controlled alignment in the fabric due to weaving or blending; whereby, i. the fabric is adapted to be shaped in a dry, solvent-free form by conforming the fabric onto said mold or substrate; ii. the resin in the fabric is adapted to melt under heat and pressure to produce a graphite-resin laminate; and, iii. the graphite and resin are intimately combined in the laminate at the controlled graphite/resin weight ratio to produce uniform characteristics.
Claim 11
Dependent Claim
21 words
The woven fabric of claim 8, in which an overwrapping of fiber is applied to the yarn in the combining step.
Claim 12
Dependent Claim
15 words
The woven fabric of claim 8, in which reinforcing fibers are woven into the fabric.
Claim 13
Dependent Claim
21 words
The woven fabric of claim 10, in which the reinforcing fibers are selected from the class consisting of aluminum and steel.
Claim 14
Dependent Claim
48 words
The woven fabric of claim 8, in which the graphite fibers and the like are selected from the class consisting of graphite, fiberglass, ceramics, quartz, boron, and SiC, and the polymeric fibers are selected from the class consisting of polyethylene, polypropylene, polyester, nylon, aramid, and polyether ether ketone.
Claim 15
Dependent Claim
25 words
The woven fabric of claim 8, in which the graphite fibers, and the like, are surrounded by at least a portion of the polymeric fibers.
Claim 16
Dependent Claim
26 words
The woven fabric of claim 8, in which the graphite and polymeric fibers are fed separately to a fabric weaving machine for weaving into the fabric.
Claim 17
Dependent Claim
23 words
The woven fabric of claim 8, comprising a hybrid fabric formed by interweaving thermoplastic fibers or ribbon with graphite fibers, and the like.
Claim 18
Dependent Claim
21 words
The woven fabric of claim 15, in which the thermoplastic ribbon is about 3/4-5 mils thick and about 60-70 mils wide.
Claim 19
Dependent Claim
25 words
The woven fabric of claim 8, in which the graphite fibers, and the like are mechanically separated before they are combined with the polymeric fibers.
Claim 20
Dependent Claim
176 words
A laminate containing a fabric of woven graphite fibers, and the like, and a resinous, thermoplastic fiber, the laminate being formed by the steps of: (a) combining or blending the graphite and thermoplastic fibers into yarn, the graphite fibers being surrounded by at least a portion of the thermoplastic fibers; (b) weaving the yarn into flexible, dry fabric adapted for dry storage without refrigeration, in which adjacent thermoplastic fibers or yarn, and graphite fibers, and the like, are adapted for sufficient movement relative to each other, thereby enabling the fabric to be conformed to a mold or substrate, the yarn and fibers having a controlled alignment in the fabric due to weaving or blending; (c) shaping the fabric in a dry, solvent-free form by conforming the fabric onto said mold or substrate; and, (d) heating the fabric under pressure to melt the resin and produce a graphite-resin laminate; whereby, (i) the combining or blending step includes controlling the graphite-resin ratio; and, ii. the graphite and resin are intimately combined in the laminate to produce uniform characteristics.
Claim 21
Dependent Claim
176 words
A laminate containing a fabric of woven graphite fibers, and the like, and a resinous, thermoplastic fiber, the laminate being formed by the steps of: (a) combining or blending the graphite and thermoplastic fibers into yarn, the graphite fibers being surrounded by at least a portion of the thermoplastic fibers; (b) weaving the yarn into flexible, dry fabric adapted for dry storage without refrigeration, in which adjacent thermoplastic fibers or yarn, and graphite fibers, and the like, are adapted for sufficient movement relative to each other, thereby enabling the fabric to be conformed to a mold or substrate, the yarn and fibers having a controlled alignment in the fabric due to weaving or blending; (c) shaping the fabric in a dry, solvent-free form by conforming the fabric onto said mold or substrate; and, (d) heating the fabric under pressure to melt the resin and produce a graphite-resin laminate; whereby, (i) the combining or blending step includes controlling the graphite-resin ratio; and, ii. the graphite and resin are intimately combined in the laminate to produce uniform characteristics.
Claim 22
Dependent Claim
44 words
The laminate of claim 18, in which the graphite fibers are selected from the class consisting of graphite, fiberglass, ceramics, quartz, boron, and SiC, and the polymeric fibers are selected from the class consisting of polyethylene, polypropylene, polyester, nylon, aramid and polyether ether ketone.
Claim 23
Dependent Claim
14 words
The laminate of claim 19, in which reinforcing fibers are woven into the fabric.
Claim 24
Dependent Claim
20 words
The laminate of claim 20, in which an overwrapping of fiber is applied to the yarn during the combining step.
Claim 25
Dependent Claim
24 words
The laminate of claim 18, in which a hybrid fabric is formed by interweaving thermoplastic fibers or ribbon with graphite fibers, and the like.
Claim 26
Dependent Claim
20 words
The laminate of claim 22, in which the thermoplastic ribbon is about 3/4-5 mils thick, and about 60-70 mils wide.
Claim 27
Dependent Claim
24 words
The laminate of claim 18, in which the graphite fibers, and the like are mechanically separated before they are combined with the polymeric fibers.
References Cited (Backward Citations)
US3573086A
Cited
US3850785A
Cited
US3769144A
Cited
US3955022A
Cited
US3914494A
Cited
US3925587A
Cited
US3993827A
Cited
US4329387A
Cited
US4263367A
Cited
US4312913A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-09-02 | 1989-03-04 | 1989-09-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-09-02 | 1993-03-04 | 1993-09-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-09-02 | 1997-03-04 | 1997-09-03 | $7700.00 | Window Closed / Lapsed |