Process for producing aromatic sulfide polymer with alkaline earth metal oxide dehydrating agent
Assignee: Kureha Corp
•
Filing: 1984-09-06
•
Granted: 1985-08-27
•
Expires: 2004-09-06
Abstract
Abstract The improvement in a process for producing an aromatic sulfide polymer from (A) hydrous sulfide of an alkali or alkaline earth metal and (B) a dihalo-aromatic compound is disclosed. The improvement is concerned with how the hydrous sulfide is dehydrated and comprises dehydrating the hydrous sulfide by the action thereon of (C) an alkaline earth metal oxide before substantial formation of the aromatic sulfide polymer.
Inventors
- 👤 Yukichika Kawakami
- 👤 Zenya Shiiki
- 👤 Yo Iizuka
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 05:42
CPC Classifications
C; C08; C08G; C08G75/00; C08G75/02; C08G75/0204; C08G75/025; C08G75/0254
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
92 words
In a process for producing an aromatic sulfide polymer which comprises subjecting (A) a hydrous sulfide of a metal selected from the group consisting of alkali metals and alkaline earth metals and (B) a dihalo-aromatic compound to a reaction in an aprotic solvent to form the aromatic sulfide polymer, the improvement which comprises contacting in the aprotic solvent the hydrous sulfide (A) with an effective amount of (C) an alkaline earth metal oxide before said reaction between the reactants (A) and (B) is substantially initiated thereby to dehydrate the hydrous sulfide (A).
Claim 2
Dependent Claim
92 words
In a process for producing an aromatic sulfide polymer which comprises subjecting (A) a hydrous sulfide of a metal selected from the group consisting of alkali metals and alkaline earth metals and (B) a dihalo-aromatic compound to a reaction in an aprotic solvent to form the aromatic sulfide polymer, the improvement which comprises contacting in the aprotic solvent the hydrous sulfide (A) with an effective amount of (C) an alkaline earth metal oxide before said reaction between the reactants (A) and (B) is substantially initiated thereby to dehydrate the hydrous sulfide (A).
Claim 3
Dependent Claim
42 words
A process for producing an aromatic sulfide polymer according to claim 1, wherein the amount of the alkaline earth metal oxide (C) employed is within the range of from 0.5 to 20 moles per mole of the hydrous metal sulfide (A) employed.
Claim 4
Dependent Claim
23 words
A process for producing an aromatic sulfide polymer according to claim 1, wherein the alkaline earth metal oxide (C) is CaO or MgO.
Claim 5
Dependent Claim
39 words
A process for producing an aromatic sulfide polymer according to claim 1, wherein the amount of the dihalo-aromatic compound (B) is within the range of from 0.8 to 1.1 moles per mole of the hydrous metal sulfide (A) employed.
Claim 6
Dependent Claim
19 words
A process for producing an aromatic sulfide polymer according to claim 1, wherein the dihalo-aromatic compound (B) is dichlorobenzene.
Claim 7
Dependent Claim
33 words
A process for producing an aromatic sulfide polymer according to claim 1, wherein the dihalo-aromatic compound (B) comprises a small amount of a higher halo-substituted aromatic compound which is at least trihalo-aromatic compound.
Claim 8
Dependent Claim
85 words
A process for producing an aromatic sulfide polymer according to claim 1, which comprises contacting in the absence of the dihalo-aromatic compound (B) the hydrous sulfide (A) with the alkaline earth metal oxide (C) in the aprotic solvent at a temperature of from room temperature to 250° C. thereby to dehydrate the hydrous sulfide (A), adding to the resultant mixture the dihalo-aromatic compound (B), and heating the resultant mixture at a temperature of from 100° to 250° C. thereby to form the aromatic sulfide polymer.
Claim 9
Dependent Claim
92 words
A process for producing an aromatic sulfide polymer according to claim 1, which comprises contacting in the presence of the dihalo-aromatic compound the hydrous sulfide (A) with the alkaline earth metal oxide (C) in the aprotic solvent at a temperature which is from room temperature to 250° C. and is so low that no reaction between the reactants (A) and (B) is substantially initiated thereby to dehydrate the hydrous sulfide (A), and heating the resultant mixture at a temperature of from 100° to 250° C. thereby to form the aromatic sulfide polymer.
References Cited (Backward Citations)
EP0103279A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-08-26 | 1989-02-25 | 1989-08-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-08-26 | 1993-02-25 | 1993-08-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-08-26 | 1997-02-25 | 1997-08-27 | $7700.00 | Window Closed / Lapsed |