US4537916A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Structured latex particles which are film forming and a process for their preparation
Assignee: Dow Chemical Co
•
Filing: 1984-06-25
•
Granted: 1985-08-27
•
Expires: 2004-06-25
Abstract
Abstract A process for preparing structured latex particles having a core and shell region wherein said latex particles are film forming at room temperature by adjusting the feed rates of the shell monomer feeds such that as the weight fraction of the shell increases the feed rate of an acrylate and/or monovinyl monomer or extended core monomer feed of monovinyl aromatic monomer is decreased whereby a shell region encapsulates the core region are described. Structured latex particles prepared by the process are also described. Films of the subject structured latex particle where the shell monomer feed is methylmethacrylate or similar high Tg monomer have good film strength. Further, films of the subject structured latex where the shell monomer feed is butyl acrylate or similar monomers having water repellency characteristics have improved corrosion resistant properties.
Inventors
- 👤 Fabio B. Bruschtein
- 👤 Robert G. Jahn
- 👤 Edwin L. Wittbrodt
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 05:16
CPC Classifications
C; C08; C08F; C08F285/00; C08F291/00
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
187 words
A process for preparing a structured latex particle whose film exhibits good film strength having a core and shell region by a continuous addition emulsion polymerization technique wherein said core region is formed from core monomer feeds comprising: (a) aliphatic conjugated diene monomer feed, (b) vinylidene halide or vinyl halide monomer feed, and/or (c) monovinyl aromatic monomer feed, (d) from about 0 to about 10 weight percent by monoethylenically unsaturated carboxylic acid monomer feed; and said shell region is formed from shell monomer feeds comprising: (e) from about 10 to about 20 percent by weight of said latex particle of an acrylate monomer feed, and/or (f) a monovinyl aromatic monomer or extended core monomer feed (c); and (g) extended core monomer feeds comprising, independently, (a), (b) or (d); wherein said process is characterized by adjusting the feed rate of said shell monomer feeds such that as the weight fraction of the shell increases the feed rate of said (e) and (f) monomers are decreased, whereby a shell region which encapsulates said core region is formed and said structured latex particle is rendered film forming at room temperature.
Claim 2
Dependent Claim
187 words
A process for preparing a structured latex particle whose film exhibits good film strength having a core and shell region by a continuous addition emulsion polymerization technique wherein said core region is formed from core monomer feeds comprising: (a) aliphatic conjugated diene monomer feed, (b) vinylidene halide or vinyl halide monomer feed, and/or (c) monovinyl aromatic monomer feed, (d) from about 0 to about 10 weight percent by monoethylenically unsaturated carboxylic acid monomer feed; and said shell region is formed from shell monomer feeds comprising: (e) from about 10 to about 20 percent by weight of said latex particle of an acrylate monomer feed, and/or (f) a monovinyl aromatic monomer or extended core monomer feed (c); and (g) extended core monomer feeds comprising, independently, (a), (b) or (d); wherein said process is characterized by adjusting the feed rate of said shell monomer feeds such that as the weight fraction of the shell increases the feed rate of said (e) and (f) monomers are decreased, whereby a shell region which encapsulates said core region is formed and said structured latex particle is rendered film forming at room temperature.
Claim 3
Dependent Claim
13 words
The process of claim 1 wherein said core monomer feed (a) is butadiene.
Claim 4
Dependent Claim
14 words
The process of claim 1 wherein said core monomer feed (b) is vinylidene chloride.
Claim 5
Dependent Claim
20 words
The process of claim 1 where said shell monomer feed (e) is C 1 -C 8 alkyl acrylates or methacrylates.
Claim 6
Dependent Claim
14 words
The process of claim 4 wherein said shell monomer feed (e) is butyl acrylate.
Claim 7
Dependent Claim
22 words
The process of claim 1 where the homopolymer of said shell monomer feed (e) has a T g greater than 25° C.
Claim 8
Dependent Claim
13 words
The process of claim 6 where said shell monomer feed (e) is methylmethacrylate.
Claim 9
Dependent Claim
22 words
The process of claim 1 where the homopolymer of said shell monomer feed (f) has a T g greater than 25° C.
Claim 10
Dependent Claim
15 words
The process of claim 8 where said shell monomer feed (f) is t-butylstyrene or styrene.
Claim 11
Dependent Claim
176 words
A structured latex particle whose film exhibits good film stength prepared by a continuous addition emulsion polymerization technique wherein said core region is formed from core monomer feeds comprising: (a) aliphatic conjugated diene monomer feed, (b) vinylidene halide or vinyl halide monomer feed, and/or (c) monovinyl aromatic monomer feed, (d) from about 0 to about 10 weight monoethylenically unsaturated carboxylic acid monomer feed; and said shell region is formed from shell monomer feeds comprising: (e) from about 10 to about 20 percent by weight of said latex particle of an acrylate monomer feed, and/or (f) a monovinyl aromatic monomer or extended core monomer feed (c); and (g) extended core monomer feeds comprising, independently, (a), (b) or (d); wherein said process is characterized by adjusting the feed rate of said shell monomer feeds such that as the weight fraction of the shell increases the feed rate of said (e) and (f) monomers are decreased, whereby a shell region which encapsulates said core region is formed and said structured latex particle is rendered film forming at room temperature.
Claim 12
Dependent Claim
176 words
A structured latex particle whose film exhibits good film stength prepared by a continuous addition emulsion polymerization technique wherein said core region is formed from core monomer feeds comprising: (a) aliphatic conjugated diene monomer feed, (b) vinylidene halide or vinyl halide monomer feed, and/or (c) monovinyl aromatic monomer feed, (d) from about 0 to about 10 weight monoethylenically unsaturated carboxylic acid monomer feed; and said shell region is formed from shell monomer feeds comprising: (e) from about 10 to about 20 percent by weight of said latex particle of an acrylate monomer feed, and/or (f) a monovinyl aromatic monomer or extended core monomer feed (c); and (g) extended core monomer feeds comprising, independently, (a), (b) or (d); wherein said process is characterized by adjusting the feed rate of said shell monomer feeds such that as the weight fraction of the shell increases the feed rate of said (e) and (f) monomers are decreased, whereby a shell region which encapsulates said core region is formed and said structured latex particle is rendered film forming at room temperature.
Claim 13
Dependent Claim
19 words
The structured latex particle of claim 10 where said (e) is C 1 -C 8 alkyl acrylates or methacrylates.
Claim 14
Dependent Claim
13 words
The structured latex particle of claim 11 where said (e) is butyl acrylate.
Claim 15
Dependent Claim
21 words
The structured latex particle of claim 11 where the homopolymer of said (e) has a T g greater than 25° C.
Claim 16
Dependent Claim
12 words
The structured latex particle of claim 13 where said (e) is methylmethacrylate.
Claim 17
Dependent Claim
21 words
The structured latex particle of claim 10 where the homopolymer of said (f) has a T g greater than 25° C.
Claim 18
Dependent Claim
14 words
The structured latex particle of claim 15 where said (f) is t-butylstyrene or styrene.
Claim 19
Dependent Claim
11 words
A film formed from the structured latex particle of claim 10.
Claim 20
Dependent Claim
22 words
The film of claim 17 where said shell monomer feed (e) is butyl acrylate such that said film has improved corrosion resistance.
Claim 21
Dependent Claim
149 words
A structured latex particle whose film exhibits corrosion resistance prepared by a continuous addition emulsion polymerization technique wherein said core region is formed from core monomer feeds comprising: (a) aliphatic conjugated diene monomer feed, (b) vinylidene halide or vinyl halide monomer feed, and/or (c) monovinyl aromatic monomer feed, and (d) from about 0 to about 10 weight monoethylenically unsaturated carboxylic acid monomer feed; and said shell region is formed from shell monomer feeds comprising: (e) a butyl acrylate monomer feed, and (f) extended core monomer feeds comprising independently, (a), (b) or (d); wherein said process is characterized by adjusting the feed rate of said shell monomer feeds such that as the weight fraction of the shell increases the feed rate of said (e) monomer is decreased, whereby a shell region which encapsulates said core region is formed and said structured latex particle is rendered film forming at room temperature.
Claim 22
Dependent Claim
149 words
A structured latex particle whose film exhibits corrosion resistance prepared by a continuous addition emulsion polymerization technique wherein said core region is formed from core monomer feeds comprising: (a) aliphatic conjugated diene monomer feed, (b) vinylidene halide or vinyl halide monomer feed, and/or (c) monovinyl aromatic monomer feed, and (d) from about 0 to about 10 weight monoethylenically unsaturated carboxylic acid monomer feed; and said shell region is formed from shell monomer feeds comprising: (e) a butyl acrylate monomer feed, and (f) extended core monomer feeds comprising independently, (a), (b) or (d); wherein said process is characterized by adjusting the feed rate of said shell monomer feeds such that as the weight fraction of the shell increases the feed rate of said (e) monomer is decreased, whereby a shell region which encapsulates said core region is formed and said structured latex particle is rendered film forming at room temperature.
Claim 23
Dependent Claim
30 words
The structured latex particle of claim 19 where said feed rate adjustment is such that from about 3 to about 30 percent by weight of said latex particle is (e).
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-08-26 | 1989-02-25 | 1989-08-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-08-26 | 1993-02-25 | 1993-08-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-08-26 | 1997-02-25 | 1997-08-27 | $7700.00 | Window Closed / Lapsed |