Abstract
Abstract A magnetic recording medium is described comprising a non-magnetic support layer, a magnetic layer and at least one layer of a high-molecular weight boron containing compound of the formula: ##STR1##
Inventors
- 👤 Masao Asano
- 👤 Wataru Fujimatsu
- 👤 Kazumasa Matsumoto
- 👤 Hideki Murata
- 👤 Toshihiko Sato
- 👤 Kenji Watanabe
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 06:33
CPC Classifications
G; G11; G11B; G11B5/00; G11B5/62; G11B5/72; G11B5/725; Y; Y10; Y10S; Y10S428/00; Y10S428/90; Y10T; Y10T428/00; Y10T428/25; Y10T428/26; Y10T428/266; Y10T428/31504; Y10T428/31551; Y10T428/31605; Y10T428/31609
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
78 words
In a magnetic recording medium comprising a support having thereon a magnetic layer containing a ferromagnetic powdery material, said magnetic recording medium comprising at least one layer containing a high-molecular compound having a boron-containing unit having the formula (I): ##STR6## wherein at least one of x 1 , x 2 , x 3 and x 4 has through an oxygen atom a linkage "-O--R-" with a polymer chain, and R is a divalent substituted or unsubstituted hydrocarbon residue.
Claim 2
Dependent Claim
78 words
In a magnetic recording medium comprising a support having thereon a magnetic layer containing a ferromagnetic powdery material, said magnetic recording medium comprising at least one layer containing a high-molecular compound having a boron-containing unit having the formula (I): ##STR6## wherein at least one of x 1 , x 2 , x 3 and x 4 has through an oxygen atom a linkage "-O--R-" with a polymer chain, and R is a divalent substituted or unsubstituted hydrocarbon residue.
Claim 3
Dependent Claim
72 words
The magnetic recording medium of claim 1, wherein said boron-containing unit is produced from a compound having the following Formula (II) or Formula (III): ##STR7## in Formula (II) and Formula (III) R is an alkylene radical having from 2 to 4 carbon atoms, x is a hydrogen atom or an acyl radical having from 8 to 22 carbon atoms, and l and m each is an integer of from 0 to 20.
Claim 4
Dependent Claim
23 words
The magnetic recording medium of claim 2, wherein the addition number of alkyleneoxide (l+m) in said Formula (II) is from 0 to 30.
Claim 5
Dependent Claim
36 words
The magnetic recording medium of claim 1, wherein said high-molecular compound having said boron-containing unit is a polyurethane formed by the reaction of a glycerol borate having said Formula (II) or (III) with an organic isocyanate.
Claim 6
Dependent Claim
44 words
The magnetic recording medium of claim 2, wherein said glycerol borate having said Formula (II) or (III) is used in the quantity range of from 5% by weight to the quantity equal to that of an active hydrogen-containing compound unit for producing said polyurethane.
Claim 7
Dependent Claim
47 words
The magnetic recording medium of claim 4, wherein said organic polyisocyanate is used in a quantity corresponding to the isocyanate radical contained therein which is in a equivalent ratio of 0.85-1.1 to the total active hydrogen content of said active hydrogen compound and of said glycerol borate.
Claim 8
Dependent Claim
85 words
The magnetic recording medium of claim 4, wherein said polyurethane is a two-liquid hardening-type polyurethane resin which is comprised of a prepolymer produced by the reaction by heating to a temperature of from 60° C. to 100° C. for several hours of said organic isocyanate with part of said active hydrogen compound and with said glycerol borate in the presence of or absent from a catalyst and a hardening agent prepared by mixing the remainder of said active hydrogen compound with, if necessary, various additives.
Claim 9
Dependent Claim
27 words
The magnetic recording medium of claim 7, wherein said prepolymer and said hardening agent are separately prepared in the liquid form and coated separately on a support.
Claim 10
Dependent Claim
44 words
The magnetic recording medium of claim 1, wherein said ferromagnetic powdery material is used with a binder material in a mixing proportion of from 10 to 200 parts by weight of said binder material to 100 parts by weight of said ferromagnetic powdery material.
Claim 11
Dependent Claim
24 words
The magnetic recording medium of claim 1, wherein said magnetic recording medium uses an abrasive whose mean particle size is from 0.1 to 2μ.
Claim 12
Dependent Claim
40 words
The magnetic recording medium of claim 1, wherein said support, if it is in the film or sheet form, is from 5 to 5μthick, and, if it is in the card form, is from 30 μm to 10 mm thick.
Claim 13
Dependent Claim
60 words
The magnetic recording medium of claim 1, wherein said ferromagnetic powdery material is subjected to an orientation magnetic field of AC or DC about 500 to 3500 gauss, and dried at a temperature of from about 50° to 100° C. for a period of from about 3 to 10 minutes for the formation of said magnetic layer on said support.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-08-26 | 1989-02-25 | 1989-08-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-08-26 | 1993-02-25 | 1993-08-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-08-26 | 1997-02-25 | 1997-08-27 | $7700.00 | Window Closed / Lapsed |