Abstract An improved process for the preparation of heat resistant copolymers of an alpha-methylstyrene and acrylonitrile by polymerization thereof in aqueous emulsion, and in the presence of a free-radical-supplying compound and a chain-transfer agent. The polymerization reaction is insufficiently cooled to remove all of the released reaction heat, and in combination therewith the polymerization is conducted at a temperature of the aqueous emulsion maintained at a level of at most 110 DEG , while further maintaining the mean rate of temperature increase per hour, v, at a value of at most 60 DEG C. per hour, wherein v is determined by the formula: <IMAGE> in which: Tm=maximum temperature of the aqueous emulsion ( DEG C.), To=temperature of the aqueous emulsion at the start of the polymerization ( DEG C.) tm=time in hours at which Tm is reached, and to=time in hours at which the polymerization is started whereby the rate of monomer conversion is maximized.
In a process for the copolymerization of alpha-methylstyrene and acrylonitrile wherein said monomers are co-polymerized (a) in aqueous emulsion, and (b) in the presence of a free-radical-supplying compound and a chain-transfer agent, and (c) wherein the polymerization reaction is insufficiently cooled to remove all of the released reaction heat, the improvement in combination therewith consisting essentially in conducting said polymerization at a temperature of the aqueous emulsion maintained at a level of at most 110° C. and while further maintaining the mean rate of temperature increase per hour, v, at a value in the range of between 5° and 60° C. per hour, wherein v is determined by the formula: ##EQU3## in which: T m =maximum temperature of the aqueous emulsion (°C.), T o =temperature of the aqueous emulsion at the start of the polymerization (°C.) t m =time in hours at which T m is reached, and t o =time in hours at which the polymerization is started, whereby the rate of monomer conversion is maximized, and whereby a heat resistant copolymer is obtained.
Claim 2
Dependent Claim
175 words
In a process for the copolymerization of alpha-methylstyrene and acrylonitrile wherein said monomers are co-polymerized (a) in aqueous emulsion, and (b) in the presence of a free-radical-supplying compound and a chain-transfer agent, and (c) wherein the polymerization reaction is insufficiently cooled to remove all of the released reaction heat, the improvement in combination therewith consisting essentially in conducting said polymerization at a temperature of the aqueous emulsion maintained at a level of at most 110° C. and while further maintaining the mean rate of temperature increase per hour, v, at a value in the range of between 5° and 60° C. per hour, wherein v is determined by the formula: ##EQU3## in which: T m =maximum temperature of the aqueous emulsion (°C.), T o =temperature of the aqueous emulsion at the start of the polymerization (°C.) t m =time in hours at which T m is reached, and t o =time in hours at which the polymerization is started, whereby the rate of monomer conversion is maximized, and whereby a heat resistant copolymer is obtained.
Claim 3
Dependent Claim
23 words
Process according to claim 1, characterized in that the temperature of the aqueous emulsion is not allowed to become higher than 95° C.
Claim 4
Dependent Claim
24 words
Process according to claim 1 characterized in that the mean rate of temperature increase per hour is kept at a value below 30° C.