Oral prosthesis and method for producing same
Assignee: United States Surgical Corp
•
Filing: 1982-09-30
•
Granted: 1985-08-20
•
Expires: 2002-09-30
Abstract
Abstract A porous implantable oral prosthesis which can be used to replicate and replace any hard tissue portion of the mouth such as bone and teeth is described. The prosthesis comprises sintered polymeric particles coated with a hydrophilic material. The polymeric particles vary in size so as to provide an area of relatively coarse porosity where the prosthesis is intended to interface with bone tissue and relatively fine porosity where it is intended to interface with soft tissue. A process for producing such prosthesis by filling a mold with appropriate molding compounds comprised of polymeric particles and a hydrophilic monomer, sintering the particles and polymerizing the monomer by dielectric heating, removing the sintered material from the cooled mold, and placing the prosthesis in a hot liquid to remove residues is described. An entire tooth, including a nonporous crown may be produced. A process for producing a porous replica of a tooth root suitable for implantation immediately after extraction of a tooth is disclosed. When extraction has taken place in the past and has resulted in the bone and gum receding, a porous implant inserted in a newly drilled hole in the patient's jaw bone may be used. A central post associated with the implant projecting above the gum may be used for attaching a denture, partial bridge or a crown. A porous implant may be used for jaw bone replacement in order to improve the fitting of dentures.
Inventors
- 👤 Paul F. Bruins
- 👤 Arthur Ashman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 02:26
CPC Classifications
A; A61; A61C; A61C8/00; A61K; A61K6/00; A61K6/80; A61K6/884
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
129 words
An implantable prosthesis for hard tissue including a porous hard-tissue-ingrowth structure, the hard-tissue-ingrowth structure comprising a mass of polymeric particles, each particle having an inner core comprised of a first biologically-compatible polymeric material and having an outer coating generally surrounding the inner core, the outer coating being comprised of a second biologically-compatible polymeric material, the second material being hydrophilic and having a composition different from the composition of the first polymeric material, the particles being bonded together to form the hard-tissue-ingrowth structure, the hard-tissue-ingrowth structure having interstices between the bonded particles forming pores into which hard tissue can grow, the size of the particles of the hard-tissue-ingrowth structure being such that the pores of the structure have dimensions effective to promote the growth of hard tissue into the pores.
Claim 2
Dependent Claim
129 words
An implantable prosthesis for hard tissue including a porous hard-tissue-ingrowth structure, the hard-tissue-ingrowth structure comprising a mass of polymeric particles, each particle having an inner core comprised of a first biologically-compatible polymeric material and having an outer coating generally surrounding the inner core, the outer coating being comprised of a second biologically-compatible polymeric material, the second material being hydrophilic and having a composition different from the composition of the first polymeric material, the particles being bonded together to form the hard-tissue-ingrowth structure, the hard-tissue-ingrowth structure having interstices between the bonded particles forming pores into which hard tissue can grow, the size of the particles of the hard-tissue-ingrowth structure being such that the pores of the structure have dimensions effective to promote the growth of hard tissue into the pores.
Claim 3
Dependent Claim
123 words
The prosthesis according to claim 1 further including a soft-tissue-ingrowth structure comprising a mass of polymeric particles, each particle having an inner core comprised of the first biologically-compatible polymeric material and having an outer coating generally surrounding the inner core, the outer coating being comprised of the second hydrophilic biologically-compatible material, the particles being bonded together to form the soft-tissue-ingrowth structure, the soft-tissue-ingrowth structure having interstices between the bonded particles forming pores into which soft tissue can grow, the size of the particles of the soft-tissue-ingrowth structure being generally shorter than the size of the particles of the hard-tissue-ingrowth structure and being such that the pores of the soft-tissue-ingrowth structure have dimensions effective to promote the growth of soft tissue into the pores.
Claim 4
Dependent Claim
16 words
The prosthesis according to claim 2 in which the first polymeric material is an acrylic polymer.
Claim 5
Dependent Claim
14 words
The prosthesis according to claim 3 in which the first polymeric material is polymethylmethacrylate.
Claim 6
Dependent Claim
15 words
The prosthesis according to claim 3 in which the second polymeric material is polymeric hydroxyethylmethacrylate.
Claim 7
Dependent Claim
21 words
The prosthesis according to claim 5 in which the polymeric hydroxyethylmethacrylate comprises a copolymer of monomeric hydroxyethylmethacrylate and a cross-linking agent.
Claim 8
Dependent Claim
17 words
The prosthesis according to claim 5 in which the prosthesis is shaped to form a tooth root.
Claim 9
Dependent Claim
21 words
The prosthesis according to claim 5 in which the prosthesis is shaped to form a tooth having a porous tooth root.
Claim 10
Dependent Claim
18 words
The prosthesis according to claim 1 in which the prosthesis is shaped to form a section of jawbone.
Claim 11
Dependent Claim
11 words
The prosthesis according to claim 1 further including a radio-opaque material.
Claim 12
Dependent Claim
14 words
The prosthesis according to claim 10 in which the radio-opaque material is barium sulfate.
Claim 13
Dependent Claim
39 words
The prosthesis according to claim 4, in which the second material is a polymerized solution of a monomer and a cross linking agent, said cross linking agent comprising one tenth percent to five percent by weight of said solution.
Claim 14
Dependent Claim
32 words
The prosthesis according to claim 4, in which said second material comprises a polymerized solution of hydroxyethylmethacrylate and one tenth percent to five percent by weight a methacrylic diester of ethylene glycol.
Claim 15
Dependent Claim
37 words
The prosthesis according to claim 13, in which said methacrylic diester of ethylene glycol is selected from the group consisting of: (a) tetraethyleneglycol dimethacrylate, (b) triethyleneglycol dimethacrylate, (c) diethyleneglycol dimethacrylate, (d) monoethyleneglycol dimethacrylate, and (e) mixtures thereof.
Claim 16
Dependent Claim
81 words
The prosthesis according to any one of claims 1-14, wherein the particles of both structures are bead shaped with the particles of the first material having a particle diameter of between about 700 and 840 microns to form pores having pore size of between about 350 and 415 microns and the particles of the second material having a particle diameter of between about 250 and 420 microns to form pores having a pore size of between about 125 and 210 microns.
Claim 17
Dependent Claim
26 words
The prosthesis according to claim 15, wherein the pores of the ingrowth structures define between about 20 and 40 percent of the volume of the structures.
Claim 18
Dependent Claim
21 words
The prosthesis according to claim 16, wherein the pore volume is about 30 percent of the volume of the two structures.
Claim 19
Dependent Claim
16 words
The prosthesis according to claim 15, wherein the particles of the ingrowth structures are sintered together.
Claim 20
Dependent Claim
52 words
The prosthesis according to claim 18, having a shape corresponding to a tooth root with the hard-tissue-ingrowth structure forming the part of the root adapted to interface with the bone of the jawbone socket and the soft-tissue-ingrowth structure forming the part of the root adapted to interface with the soft gum tissue.
Claim 21
Dependent Claim
44 words
The prosthesis according to claim 19, further comprising a solid post having one end imbedded in the root shaped portion of the prosthesis and the other end projecting therefrom for attaching a replica of a crown of a tooth onto the root shaped portion.
Claim 22
Dependent Claim
21 words
The prosthesis according to claim 20, wherein the post is constructed of non-polar plastic and threaded into the root shaped portion.
Claim 23
Dependent Claim
14 words
The prosthesis according to claim 21, wherein the post is constructed of solid polymethylmethacrylate.
Claim 24
Dependent Claim
31 words
The prosthesis according to claim 22, further comprising a crown shaped member bonded to the root shaped portion with the other end of the post imbedded in the crown shaped member.
Claim 25
Dependent Claim
26 words
The prosthesis according to claim 18, wherein the percentage, by weight, of the coating material to the core material is between about 5 and 20 percent.
Claim 26
Dependent Claim
23 words
The prosthesis according to claim 24, wherein the percentage, by weight, of the coating material to the core material is about ten percent.
References Cited (Backward Citations)
US24401A
Cited
USRE24401E
Cited
US3446875A
Cited
US3628988A
Cited
US3632416A
Cited
US3628248A
Cited
US3789029A
Cited
FR2105998A5
Cited
US3749685A
Cited
US3808606A
Cited
US3943045A
Cited
US4118532A
Cited
DE2255916A1
Cited
US3882858A
Cited
US3930076A
Cited
DE2449831A1
Cited
US3992725A
Cited
US3919773A
Cited
US3906550A
Cited
US4051598A
Cited
US3943267A
Cited
US4131597A
Cited
US3971134A
Cited
US4093576A
Cited
US4199864A
Cited
US4186448A
Cited
US4164794A
Cited
US4178686A
Cited
US4181983A
Cited
US4244689A
Cited
US4396476A
Cited
US4247287A
Cited
US4252525A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-08-19 | 1989-02-18 | 1989-08-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-08-19 | 1993-02-18 | 1993-08-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-08-19 | 1997-02-18 | 1997-08-20 | $7700.00 | Window Closed / Lapsed |