US4535123A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Releasable film forming compositions
Assignee: DuPont Toray Specialty Materials KK
•
Filing: 1984-08-23
•
Granted: 1985-08-13
•
Expires: 2004-08-23
Abstract
Abstract The present invention provides a releasable film forming composition comprising (1) an organopolysiloxane having hydroxyl groups at the ends of the molecular chain, (2) a finely divided silica, (3) a phenyl-containing organosilane or organopolysiloxane, (4) an organohydrogenpolysiloxane containing at least three SiH groups per molecule, (5) a metallic salt of an organic acid and (6) an organic solvent, and a process for preparing same, as well as a releasable film forming composition comprising (1) an organopolysiloxane containing at least two silicon atom-bonded alkenyl groups per molecule, (2) a finely divided silica, (3) a phenyl-containing organosilane or organopolysiloxane, (4) an organohydrogenpolysiloxane containing at least two SiH groups per molecule, (5) a platinic compound and (6) an organic solvent, and a process for preparing same. These compositions exhibit a superior printability and a stable releasability from adhesive materials and are less slippery.
Inventors
- 👤 Shosaku Sasaki
- 👤 Nobuo Kaiya
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 01:00
CPC Classifications
C; C08; C08L; C08L83/00; C08L83/04; C08G; C08G77/00; C08G77/04; C08G77/12; C08G77/14; C08G77/16; C08G77/20; C08G77/70; Y; Y10; Y10S; Y10S528/00; Y10S528/901
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
164 words
A releasable film forming composition comprising: (1) 100 parts by weight of a substantially straight-chain organopolysiloxane containing at least two silicon atom-bonded alkenyl groups per molecule and having a viscosity not lower than 1,000 centipoise at 25° C.; (2) 5 to 80 parts by weight of a finely divided silica; (3) 2 to 40 parts by weight of a phenyl-containing organosilane or organopolysiloxane represented by the general formula ##STR4## wherein R 1 and R 2 are each a monovalent hydrocarbon group, at least 25 mol % of R 1 and R 2 being phenyl, and n is a number of 1 to 100; (4) 0.5 to 40 parts by weight of an organohydrogenpolysiloxane containing at least two SiH groups per molecule, provided the sum of the number of alkenyl groups per molecule of the component (1) and that of SiH groups per molecule of the component (4) is at least five; (5) a catalytic amount of a platinic compound; and (6) an organic solvent.
Claim 2
Dependent Claim
164 words
A releasable film forming composition comprising: (1) 100 parts by weight of a substantially straight-chain organopolysiloxane containing at least two silicon atom-bonded alkenyl groups per molecule and having a viscosity not lower than 1,000 centipoise at 25° C.; (2) 5 to 80 parts by weight of a finely divided silica; (3) 2 to 40 parts by weight of a phenyl-containing organosilane or organopolysiloxane represented by the general formula ##STR4## wherein R 1 and R 2 are each a monovalent hydrocarbon group, at least 25 mol % of R 1 and R 2 being phenyl, and n is a number of 1 to 100; (4) 0.5 to 40 parts by weight of an organohydrogenpolysiloxane containing at least two SiH groups per molecule, provided the sum of the number of alkenyl groups per molecule of the component (1) and that of SiH groups per molecule of the component (4) is at least five; (5) a catalytic amount of a platinic compound; and (6) an organic solvent.
Claim 3
Dependent Claim
18 words
The composition of claim 1 wherein said finely divided silica as component (2) is a wet process silica.
Claim 4
Dependent Claim
26 words
The composition of claim 1 wherein said finely divided silica as component (2) is a mixture of a wet process silica and a dry process silica.
Claim 5
Dependent Claim
182 words
A process for preparing a releasable film forming composition, which process comprises kneading under heating (1) 100 parts by weight of a substantially straight-chain organopolysiloxane containing at least two silicon atom-bonded alkenyl groups per molecule and having a viscosity not lower than 1,000 centipoise at 25° C., (2) 5 to 80 parts by weight of a finely divided silica and (3) 2 to 40 parts by weight of a phenyl-containing organosilane or organopolysiloxane represented by the general formula ##STR5## wherein R 1 and R 2 are each a monovalent hydrocarbon group, at least 25 mol % of R 1 and R 2 being phenyl, and n is a number of 1 to 100, and then dissolving the resulting mixture in an organic solvent together with (4) 0.5 to 40 parts by weight of an organohydrogenpolysiloxane containing at least two SiH groups per molecule, provided the sum of the number of alkenyl groups per molecule of the component (1) and that of SiH groups per molecule of the component (4) is at least five, and (5) a catalytic amount of a platinic compound.
Claim 6
Dependent Claim
182 words
A process for preparing a releasable film forming composition, which process comprises kneading under heating (1) 100 parts by weight of a substantially straight-chain organopolysiloxane containing at least two silicon atom-bonded alkenyl groups per molecule and having a viscosity not lower than 1,000 centipoise at 25° C., (2) 5 to 80 parts by weight of a finely divided silica and (3) 2 to 40 parts by weight of a phenyl-containing organosilane or organopolysiloxane represented by the general formula ##STR5## wherein R 1 and R 2 are each a monovalent hydrocarbon group, at least 25 mol % of R 1 and R 2 being phenyl, and n is a number of 1 to 100, and then dissolving the resulting mixture in an organic solvent together with (4) 0.5 to 40 parts by weight of an organohydrogenpolysiloxane containing at least two SiH groups per molecule, provided the sum of the number of alkenyl groups per molecule of the component (1) and that of SiH groups per molecule of the component (4) is at least five, and (5) a catalytic amount of a platinic compound.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-08-12 | 1989-02-11 | 1989-08-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-08-12 | 1993-02-11 | 1993-08-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-08-12 | 1997-02-11 | 1997-08-13 | $7700.00 | Window Closed / Lapsed |