Standardized multi-stack dielectric-layer filter blank and method for fabricating color-encoding filter therefrom
Assignee: RCA Corp
•
Filing: 1983-07-11
•
Granted: 1985-08-13
•
Expires: 2003-07-11
Abstract
Abstract A green-manifesting blank comprised of yellow and cyan dielectric stacks, one on top of the other, supported by a transparent substrate can be used to fabricate a green, yellow or cyan, and white color-encoding filter having any arbitrary given spatial pattern by combining dry-etching and wet etching, if the top layer of the bottom stack is composed of a material which is inert to a given wet etchant and the bottom layer of the top stack is composed of a material which is etched by the given wet etchant. Alternatively, the wet etching can be dispensed with if, after completion of the color-encoding filter, the filter is covered with an overcoat material exhibiting an index-of-refraction substantially equal to that of the bottom layer of the top stack.
Inventors
- 👤 Michael T. Gale
- 👤 Hans W. Lehmann
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 13:51
CPC Classifications
G; G02; G02B; G02B5/00; G02B5/20; G02B5/201; H; H10; H10F; H10F39/00; H10F39/011; H10F39/024; H10F39/80; H10F39/805; H10F39/8053
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
286 words
A standardized green-manifesting dielectric filter blank having a given surface area for use in fabricating therefrom a color-encoding transmissive filter that exhibits any arbitrary given spatial pattern over said given surface area, which spatial pattern comprises at least one spatial region manifesting green, at least one spatial region manifesting only a preselected certain one of cyan or yellow, and at least one spatial region manifesting white; said blank comprising: a transparent substrate having a surface of at least said given area; a first dielectric filter in contact with and substantially entirely covering all of said given surface area of said substrate, said first dielectric filter comprising a first stack of a plurality of dielectric layers having respective specified thicknesses and exhibiting respective indices-of-refraction such that only said preselected certain one of cyan-manifesting light or yellow-manifesting light is transmitted through said first stack, the top layer of said first stack being comprised of a first dielectric material which is inert to a given wet etchant; a second dielectric filter in contact with and substantially entirely covering all of said top layer of said first stack, said second dielectric filter comprising a second stack of a plurality of dielectric layers having respective specified thicknesses and exhibiting respective indices-of-refraction such that only the other one of said preselected certain one of cyan-manifesting light and yellow-manifesting light is transmitted through said second stack, the bottom layer of said second stack (1) being in contact with said top layer of said first stack and (2) being composed of a second dielectric material which is etchable by said given wet etchant, and; wherein all of said layers of both said first and second stacks are etchable by a given dry etching process.
Claim 2
Dependent Claim
286 words
A standardized green-manifesting dielectric filter blank having a given surface area for use in fabricating therefrom a color-encoding transmissive filter that exhibits any arbitrary given spatial pattern over said given surface area, which spatial pattern comprises at least one spatial region manifesting green, at least one spatial region manifesting only a preselected certain one of cyan or yellow, and at least one spatial region manifesting white; said blank comprising: a transparent substrate having a surface of at least said given area; a first dielectric filter in contact with and substantially entirely covering all of said given surface area of said substrate, said first dielectric filter comprising a first stack of a plurality of dielectric layers having respective specified thicknesses and exhibiting respective indices-of-refraction such that only said preselected certain one of cyan-manifesting light or yellow-manifesting light is transmitted through said first stack, the top layer of said first stack being comprised of a first dielectric material which is inert to a given wet etchant; a second dielectric filter in contact with and substantially entirely covering all of said top layer of said first stack, said second dielectric filter comprising a second stack of a plurality of dielectric layers having respective specified thicknesses and exhibiting respective indices-of-refraction such that only the other one of said preselected certain one of cyan-manifesting light and yellow-manifesting light is transmitted through said second stack, the bottom layer of said second stack (1) being in contact with said top layer of said first stack and (2) being composed of a second dielectric material which is etchable by said given wet etchant, and; wherein all of said layers of both said first and second stacks are etchable by a given dry etching process.
Claim 3
Dependent Claim
52 words
The filter blank defined in claim 1, wherein said blank further includes a protective epoxy layer overcoat in contact with and substantially covering said given area of the top layer of said second stack, said epoxy layer having a thickness which is much larger than any light wavelength in the visible spectrum.
Claim 4
Dependent Claim
44 words
The filter blank defined in claim 1, wherein said preselectered certain one of cyan-manifesting light and yellow-manifesting light is cyan-manifesting light; and said top layer of said first stack is TiO 2 and said bottom layer of said second stack is SiO 2 .
Claim 5
Dependent Claim
30 words
The filter blank defined in claim 3, wherein each of said first stack and said second stack is entirely comprised of alternating layers of TiO 2 and SiO 2 .
Claim 6
Dependent Claim
186 words
The filter blank defined in claim 4, wherein: said filter blank further includes a protective epoxy layer overcoat in contact with and substantially covering said given area of the top layer of said second stack, said epoxy layer having a thickness which is much larger than any light wavelength in the visible spectrum; said substrate and said overcoat each exhibit an index-of-refraction of substantially 1.5, SiO 2 exhibits an index-of-refraction of 1.46 and TiO 2 exhibits an index-of-refraction of substantially 2.4; and said first and second stacks together consist of 19 layers having respective thicknesses and composition, beginning with the top layer of said second stack in contact with said overcoat and ending with the bottom layer of said first stack in contact with said substrate, substantially in accordance with the following list: ______________________________________
Layer No. TiO.sub.2 SiO.sub.2
______________________________________
SECOND STACK Epoxy (overcoat)
1 29.4 nm
2 48.3
3 58.8
4 48.3
5 58.8
6 48.3
7 58.8
8 48.3
9 29.4
10 145.0
FIRST STACK 11 96.8
12 59.2
13 96.8
14 59.2
15 96.8
16 59.2
17 96.8
18 59.2
19 96.8
Substrate
______________________________________
Claim 7
Dependent Claim
12 words
The filter blank defined in claim 5, wherein said substrate is glass.
Claim 8
Dependent Claim
15 words
The filter blank defined in claim 3, wherein said given wet etchant is buffered HF.
Claim 9
Dependent Claim
45 words
The filter blank defined in claim 1, wherein: said preselected certain one of cyan-manifesting light and yellow-manifesting light is yellow-manifesting light; and said top layer of said first stack is TiO 2 , and said bottom layer of said second stack is SnO 2 .
Claim 10
Dependent Claim
65 words
The filter blank defined in claim 8, wherein: said first stack is entirely composed of alternating layers of TiO 2 and SiO 2 ; and said second stack, except for its bottom layer, is composed alternating layers of SiO 2 and TiO 2 with an SiO 2 layer of said second stack being in contact with said SnO 2 bottom layer of said second stack.
Claim 11
Dependent Claim
193 words
The filter blank defined in claim 9, wherein: said blank further includes a protective epoxy layer overcoat in contact with and substantially covering said given area of the top layer of said second stack, said epoxy layer having a thickness which is much larger than any light wavelength in the visible spectrum; said substrate and said overcoat each exhibit an index-of-refraction of about 1.5, SiO 2 exhibits an index-of-refraction of substantially 1.46, TiO 2 exhibits an index-of-refraction of substantially 2.4, and SnO 2 exhibits an index-of-refraction of substantially 1.86; and said first and second stacks together consist of 18 layers having respective thicknesses and composition, beginning with the top layer of second stack in contact with said overcoat and ending with the bottom layer of said first stack in contact with said substrate, substantially in accordance with the following list: ______________________________________
Layer No.
TiO.sub.2 SiO.sub.2
SnO.sub.2
______________________________________
SECOND STACK
Epoxy (overcoat)
1 95.8 nm
2 58.6
3 95.8
4 58.6
5 95.8
6 58.6
7 95.8
8 58.6
9 123.6 nm
FIRST STACK 10 29.9
11 49.2
12 59.8
13 49.2
14 59.8
15 49.2
16 59.8
17 49.2
18 29.9
Substrate
______________________________________
Claim 12
Dependent Claim
12 words
The filter blank defined in claim 10, wherein said substrate is glass.
Claim 13
Dependent Claim
29 words
The filter blank defined in claim 8, wherein said given wet etchant is concentrated HCl to which small amounts of Zn are added to produce nascent H 2 .
Claim 14
Independent Claim
508 words
A method for fabricating a color-encoding transmissive green-manifesting dielectric filter from a standarized green-manifesting dielectric filter blank, said blank having a given surface area for use in fabricating therefrom a color-encoding transmissive filter that exhibits any arbitrary given spatial pattern over said given surface area, which spatial pattern comprises at least one spatial region manifesting green, at least one spatial region manifesting only a preselected certain one of cyan or yellow, and at least one spatial region manifesting white; wherein said blank comprises a transparent substrate having a surface of at least said given area; a first dielectric filter in contact with and substantially entirely covering all of said given surface area of said substrate, said first dielectric filter comprising a first stack of a plurality of dielectric layers having respective specified thicknesses and exhibiting respective indices-of-refraction such that only said preselected certain one of cyan-manifesting light or yellow-manifesting light is transmitted through said first stack, the top layer of said first stack being comprised of a first dielectric material which is inert to a given wet etchant; a second dielectric filter in contact with and substantially entirely covering all of said top layer of said first stack, said second dielectric filter comprising a second stack of a plurality of dielectric layers having respective specified thicknesses and exhibiting respective indices-of-refraction such that only the other one of said preselected certain one of cyan-manifesting light and yellow-manifesting light is transmitted through said second stack, the bottom layer of said second stack (1) being in contact with said top layer of said first stack and (2) being composed of a second dielectric material which is etchable by said given wet etchant; and wherein all of said layers of both said first and second stacks are etchable by a given dry etching process; said method comprising the steps of: first, defining spatially on said blank solely the respective spatial regions of said given spatial pattern that correspond solely with all said preselected certain one of cyan or yellow spatial regions and all said white spatial regions; second, dry etching solely said first defined spatial regions of said second stack to remove all but a portion of the bottom layer of said second stack only within said first-defined spatial regions of said second stack; third wet etching said portion of the bottom layer of said second stack with said given wet etchant to remove all of said portion of the bottom layer of said second stack only within said first defined spatial regions thereby to reveal the underlying top layer of said first stack without etching any of said top layer of said first stack; fourth, defining spatially solely those first defined revealed spatial regions of said top layer of said first stack that correspond solely to said white spatial regions, and fifth, dry etching said step-four defined spatial regions of said first stack to remove all of the layers of said first stack only within said second-defined spatial regions thereby to reveal the underlying substrate only within said second-defined spatial regions.
Claim 15
Independent Claim
508 words
A method for fabricating a color-encoding transmissive green-manifesting dielectric filter from a standarized green-manifesting dielectric filter blank, said blank having a given surface area for use in fabricating therefrom a color-encoding transmissive filter that exhibits any arbitrary given spatial pattern over said given surface area, which spatial pattern comprises at least one spatial region manifesting green, at least one spatial region manifesting only a preselected certain one of cyan or yellow, and at least one spatial region manifesting white; wherein said blank comprises a transparent substrate having a surface of at least said given area; a first dielectric filter in contact with and substantially entirely covering all of said given surface area of said substrate, said first dielectric filter comprising a first stack of a plurality of dielectric layers having respective specified thicknesses and exhibiting respective indices-of-refraction such that only said preselected certain one of cyan-manifesting light or yellow-manifesting light is transmitted through said first stack, the top layer of said first stack being comprised of a first dielectric material which is inert to a given wet etchant; a second dielectric filter in contact with and substantially entirely covering all of said top layer of said first stack, said second dielectric filter comprising a second stack of a plurality of dielectric layers having respective specified thicknesses and exhibiting respective indices-of-refraction such that only the other one of said preselected certain one of cyan-manifesting light and yellow-manifesting light is transmitted through said second stack, the bottom layer of said second stack (1) being in contact with said top layer of said first stack and (2) being composed of a second dielectric material which is etchable by said given wet etchant; and wherein all of said layers of both said first and second stacks are etchable by a given dry etching process; said method comprising the steps of: first, defining spatially on said blank solely the respective spatial regions of said given spatial pattern that correspond solely with all said preselected certain one of cyan or yellow spatial regions and all said white spatial regions; second, dry etching solely said first defined spatial regions of said second stack to remove all but a portion of the bottom layer of said second stack only within said first-defined spatial regions of said second stack; third wet etching said portion of the bottom layer of said second stack with said given wet etchant to remove all of said portion of the bottom layer of said second stack only within said first defined spatial regions thereby to reveal the underlying top layer of said first stack without etching any of said top layer of said first stack; fourth, defining spatially solely those first defined revealed spatial regions of said top layer of said first stack that correspond solely to said white spatial regions, and fifth, dry etching said step-four defined spatial regions of said first stack to remove all of the layers of said first stack only within said second-defined spatial regions thereby to reveal the underlying substrate only within said second-defined spatial regions.
Claim 16
Dependent Claim
56 words
The method defined in claim 13, wherein said top layer of said first stack is composed of TiO 2 and said bottom layer of said second stack is composed of SiO 2 , and wherein the step of wet etching comprises wet etching said portion of said bottom layer of said second stack with buffered HF.
Claim 17
Dependent Claim
68 words
The method defined in claim 13, wherein said top layer of said first stack is composed of TiO 2 and the bottom layer of said second stack is composed of SnO 2 , and wherein said step of wet etching said portion of said bottom layer of said second stack with concentrated HCl to which a small amount of Zn is added to produce nascent H 2 .
Claim 18
Dependent Claim
48 words
The method defined in claim 13, wherein said step of dry etching solely said first defined spatial regions of said second stack comprises the step of removing all but a portion of the bottom layer of said second stack having a thickness of the order of 100 nanometers.
Claim 19
Independent Claim
221 words
A method for fabricating a multi-colored filter from a transmissive dielectric filter blank configuration comprising a plurality of dielectric stacks for use in fabricating a color-encoding filter therefrom, said blank configuration including: a first multilayer interference dielectric stack supporting an overlying second multilayer interference dielectric stack with the bottom layer of said second stack being directly in contact with the top layer of said first stack, said first stack by itself transmitting light of a first color spectrum and said second stack by itself transmitting light of a second color spectrum that partially overlaps said first color spectrum, whereby said first and second stacks together transmit light of a third color spectrum that corresponds only with the overlap of said first and second color spectra and wherein all layers of both said first and second stacks are dry etched by a given dry etching process; said method comprising the steps of: dry etching at least one selected region of said second stack to remove all but a portion of the bottom layer of said second stack only within said selected regions of said second stack; and at least optically effectively removing said portion of the bottom layer of said second stack only within said selected regions of said second stack without affecting any of said top layer of said first stack.
Claim 20
Independent Claim
221 words
A method for fabricating a multi-colored filter from a transmissive dielectric filter blank configuration comprising a plurality of dielectric stacks for use in fabricating a color-encoding filter therefrom, said blank configuration including: a first multilayer interference dielectric stack supporting an overlying second multilayer interference dielectric stack with the bottom layer of said second stack being directly in contact with the top layer of said first stack, said first stack by itself transmitting light of a first color spectrum and said second stack by itself transmitting light of a second color spectrum that partially overlaps said first color spectrum, whereby said first and second stacks together transmit light of a third color spectrum that corresponds only with the overlap of said first and second color spectra and wherein all layers of both said first and second stacks are dry etched by a given dry etching process; said method comprising the steps of: dry etching at least one selected region of said second stack to remove all but a portion of the bottom layer of said second stack only within said selected regions of said second stack; and at least optically effectively removing said portion of the bottom layer of said second stack only within said selected regions of said second stack without affecting any of said top layer of said first stack.
Claim 21
Dependent Claim
138 words
The method defined in claim 17, wherein said filter blank configuration includes a top layer of said first stack which is composed of a first material which is inert to a given wet etchant and a bottom layer of said second stack which is composed of a second material which is wet etched by said given wet etchant, and wherein said step of at least optically effectively removing comprises the step of: physically removing by wet etching said portion of the bottom layer of said second stack only within said selected regions of said second stack to remove all of said portion of the bottom layer only within said selected regions and thereby reveal the underlying top layer of said first stack only within said selected regions without affecting any of said top layer of said first stack.
Claim 22
Dependent Claim
94 words
The method defined in claim 17, wherein said filter blank configuration includes a bottom layer of said second stack exhibiting a given index-of-refraction, and wherein said step of at least optically effectively removing includes the step of: covering said portion of the bottom layer of said second stack only within said selected regins of the bottom layer of said second stack with a given transparent material that is in intimate contact with said portion of the bottom layer of said second stack, said given material exhibiting an index-of-refraction substantially equal to said given index-of-refraction.
References Cited (Backward Citations)
FR1206317A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-08-12 | 1989-02-11 | 1989-08-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-08-12 | 1993-02-11 | 1993-08-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-08-12 | 1997-02-11 | 1997-08-13 | $7700.00 | Window Closed / Lapsed |