Mortar
Assignee: Saint Gobain Abrasives Inc
•
Filing: 1984-01-30
•
Granted: 1985-08-06
•
Expires: 2004-01-30
Abstract
Abstract A mullite containing cementing mix particularly suited for silicon carbide containing shapes is shown that is adapted to be initially activated when mixed with water and set by air drying so that it can subsequently permanently set by firing the mortar in situ. The mullite component is first mixed in a raw batch with ball clay, a chemically active alumina, bentonite, sodium silicate and a borosilicate glass frit and then after this composition is mixed with water and air dried, the cement is fired in place to react certain of the constituents in the mix and sinter the mullite phase in a bonded relation with the surface of the shapes being cemented in place. A refractory furnace liner or the like may thus be fabricated for example wherein the silicon carbide containing shapes forming the liner are held in place with an inert strongly adhering cement having substantially the same thermal expansion properties as the shapes being bonded.
Inventors
- 👤 Cecil M. Jones
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 22:52
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/622; C04B35/626; C04B35/63; C04B35/6303; C04B35/6316; C04B35/01; C04B35/16; C04B35/18; C04B35/48; C04B35/481; C04B35/66; C04B2235/00; C04B2235/02; C04B2235/30; C04B2235/32; C04B2235/3217; C04B2235/34; C04B2235/3427; C04B2235/3463; C04B2235/38; C04B2235/3817; C04B2235/3826; C04B2235/3852; C04B2235/3873
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
114 words
A raw batch adapted to be mixed with water to form a mortar adapted to be dried and then fired in situ particularly for use with silicon carbide containing elements including silicon carbide shapes bonded with oxides, silicon nitride or silicon oxynitride comprising a mixture of from 70% to 90% by weight of a calcined refractory mullite grain containing 70% alumina, from 2% to 7% by weight of a ball clay, from 2% to 10% by weight of a finely ground chemically active alumina, from 1% to 4% by weight of a purified bentonite, from 0.5% to 1.5% by weight of sodium silicate, and from 5% to 15% by weight of a glass frit.
Claim 2
Dependent Claim
114 words
A raw batch adapted to be mixed with water to form a mortar adapted to be dried and then fired in situ particularly for use with silicon carbide containing elements including silicon carbide shapes bonded with oxides, silicon nitride or silicon oxynitride comprising a mixture of from 70% to 90% by weight of a calcined refractory mullite grain containing 70% alumina, from 2% to 7% by weight of a ball clay, from 2% to 10% by weight of a finely ground chemically active alumina, from 1% to 4% by weight of a purified bentonite, from 0.5% to 1.5% by weight of sodium silicate, and from 5% to 15% by weight of a glass frit.
Claim 3
Dependent Claim
82 words
A raw batch as in claim 1 wherein said calcined refractory grain is present in an amount of 77% by weight, said ball clay is present in an amount of 5% by weight, said chemically active alumina is present in an amount of 5% by weight, said bentonite is present in an amount of 2% by weight, said sodium silicate is present in an amount of 0.75% by weight, and said glass frit is present in an amount of 10% by weight.
Claim 4
Dependent Claim
100 words
A structure comprising silicon carbide containing elements cemented together, wherein the cement for bonding said elements is the reaction product formed by the in situ firing of a mixture of grains, said mixture including from 70% to 90% by weight of a calcined mullite refractory grain containing 70% alumina, from 2% to 7% by weight of a ball clay, from 2% to 10% by weight of a finely ground chemically active alumina, from 1% to 4% by weight of bentonite, from 0.5% to 1.5% by weight of sodium silicate, and from 5% to 15% by weight of a glass frit.
Claim 5
Dependent Claim
100 words
A structure comprising silicon carbide containing elements cemented together, wherein the cement for bonding said elements is the reaction product formed by the in situ firing of a mixture of grains, said mixture including from 70% to 90% by weight of a calcined mullite refractory grain containing 70% alumina, from 2% to 7% by weight of a ball clay, from 2% to 10% by weight of a finely ground chemically active alumina, from 1% to 4% by weight of bentonite, from 0.5% to 1.5% by weight of sodium silicate, and from 5% to 15% by weight of a glass frit.
Claim 6
Dependent Claim
56 words
A structure as in claim 3 wherein said mixture included 77% by weight of said refractory grain, 5% by weight of said ball clay, 5% by weight of said chemically active alumina, 2% by weight of said bentonite, 0.75% by weight of said sodium silicate, and 10% of said glass frit was present prior to firing.
Claim 7
Dependent Claim
116 words
A fabricated refractory apparatus formed of a plurality of interfitted silicon carbide containing shapes having oppositely disposed faces cemented together comprising a cement disposed between the faces of said interfitting silicon carbide containing shapes, said cement being the reaction product resulting from the in situ firing of a mixture containing from 70% to 90% by weight of a calcined mullite refractory grain containing 70% alumina, from 2% to 7% by weight of a ball clay, from 2% to 10% by weight of a finely ground chemically active alumina, from 1% to 4% by weight of bentonite, from 0.5% to 1.5% by weight of sodium silicate, and from 5% to 15% by weight of a glass frit.
Claim 8
Dependent Claim
116 words
A fabricated refractory apparatus formed of a plurality of interfitted silicon carbide containing shapes having oppositely disposed faces cemented together comprising a cement disposed between the faces of said interfitting silicon carbide containing shapes, said cement being the reaction product resulting from the in situ firing of a mixture containing from 70% to 90% by weight of a calcined mullite refractory grain containing 70% alumina, from 2% to 7% by weight of a ball clay, from 2% to 10% by weight of a finely ground chemically active alumina, from 1% to 4% by weight of bentonite, from 0.5% to 1.5% by weight of sodium silicate, and from 5% to 15% by weight of a glass frit.
Claim 9
Dependent Claim
38 words
A fabricated apparatus as in claim 5 wherein the cement between said faces has exposed edges that are insulated from exposure by reason of the borosilicate glass frit and mullite that form a seal on said exposed edges.
Claim 10
Dependent Claim
111 words
A raw batch adapted to be mixed with water to form a mortar adapted to be dried and then fired in situ particularly for use with silicon carbide containing elements including silicon carbide shapes bonded with oxides, silicon nitride or silicon oxynitride comprising a mixture of from 70% to 90% by weight of a calcined refractory zircon grain, from 2% to 7% by weight of a ball clay, from 2% to 10% by weight of a finely ground chemically active alumina, from 1% to 4% by weight of a purified bentonite, from 0.5 to 1.5% by weight of sodium silicate, and from 5% to 15% by weight of a glass frit.
Claim 11
Dependent Claim
111 words
A raw batch adapted to be mixed with water to form a mortar adapted to be dried and then fired in situ particularly for use with silicon carbide containing elements including silicon carbide shapes bonded with oxides, silicon nitride or silicon oxynitride comprising a mixture of from 70% to 90% by weight of a calcined refractory zircon grain, from 2% to 7% by weight of a ball clay, from 2% to 10% by weight of a finely ground chemically active alumina, from 1% to 4% by weight of a purified bentonite, from 0.5 to 1.5% by weight of sodium silicate, and from 5% to 15% by weight of a glass frit.
References Cited (Backward Citations)
US1442413A
Cited
US1081536A
Cited
US1251888A
Cited
US1893313A
Cited
US3197315A
Cited
US3303034A
Cited
US4090881A
Cited
US4244745A
Cited
US4222782A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-08-05 | 1989-02-04 | 1989-08-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-08-05 | 1993-02-04 | 1993-08-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-08-05 | 1997-02-04 | 1997-08-06 | $7700.00 | Window Closed / Lapsed |