Method for inhibiting scale deposition
Assignee: Noveon IP Holdings Corp
•
Filing: 1983-09-23
•
Granted: 1985-07-30
•
Expires: 2003-09-23
Abstract
Abstract Copolymers which are substantially completely soluble in water at the low concentration in which they are used to treat process water, include copolymers of acrylic acid ("AA") or methacrylic acid ("MAA") and salts thereof (together referred to herein as "(meth)acrylic acid", and for brevity as "(M)AA"), and a lower alkenyl carboxylate ("LAC") such as vinyl acetate or propionate, optionally together with a salt of a lower alkenyl sulfonate ("SLAS"). Typical copolymers are those of (M)AA and vinyl acetate ("VOAc") present in a molar ratio in the range from 95:5 to about 60:40; and those of (M)AA, VOAc and sodium vinyl sulfonate ("SVS") in a molar ratio in the range from 95:4.9:0.1 to about 50:25:25. If desired, the foregoing copolymers may be hydrolyzed for use as their hydrolyzates, or the copolymers may be at least partially hydrolyzed, prior to or, during use as for example when used in alkaline boiler water systems. The compositions are useful to inhibit the deposition of particulate matter in mud suspended in the process water, and also of scale due to salts dissolved in various process water streams, particularly in boiler water and cooling water. The compositions are therefore not only excellent dispersants but also exhibit unexpected threshold and sequestering effects. They are conventionally formed and have a relatively low molecular weight, preferably in the range from about 1000 to about 25,000. The molar ratio of the reactants is such that (M)AA is always present in a molar amount which is at least 50 mole percent relative to the remaining constituent(s) of the copolymer.
Inventors
- 👤 Zahid Amjad
- 👤 William F. Masler, III
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 13:38
CPC Classifications
A; A23; A23C; A23C9/00; A23C9/152; A23B; A23B70/00; A23B70/30; C; C02; C02F; C02F5/00; C02F5/08; C02F5/10; C02F5/12
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
206 words
A method of inhibiting the deposition of scale due particularly to calcium phosphate, zinc phosphate and magnesium phosphate formed in a system for treating process water, comprising, adding to said process water from 1 part per million (pp) to about 200 ppm of a water-soluble essentially non-crosslinked random copolymer, optionally after said copolymer is subjected to hydrolytic conditions, said copolymer having the structural formula ##STR8## wherein, R 1 represents H, or methyl; R 2 represents H, methyl or ethyl; X is selected from the group consisting of H, NH 4 , an alkali metal, an alkaline earth metal and zinc; n is either 0 or 1; X' is selected from NH 4 , an alkali metal, an alkaline earth metal and zinc; z is a number in the range from 0 to about 1.0; m is an integer in the range from about 3 to about 70; x is a number in the range from about 2.5 to about 15.0 times the amount of y present; the mole ratio of reactants used to form the copolymer contains at least 50 mole percent of acrylic or methacrylic acid relative to the remaining constitutents of the copolymer; and, x, y and z are present in relative heterogeneous order.
Claim 2
Independent Claim
206 words
A method of inhibiting the deposition of scale due particularly to calcium phosphate, zinc phosphate and magnesium phosphate formed in a system for treating process water, comprising, adding to said process water from 1 part per million (pp) to about 200 ppm of a water-soluble essentially non-crosslinked random copolymer, optionally after said copolymer is subjected to hydrolytic conditions, said copolymer having the structural formula ##STR8## wherein, R 1 represents H, or methyl; R 2 represents H, methyl or ethyl; X is selected from the group consisting of H, NH 4 , an alkali metal, an alkaline earth metal and zinc; n is either 0 or 1; X' is selected from NH 4 , an alkali metal, an alkaline earth metal and zinc; z is a number in the range from 0 to about 1.0; m is an integer in the range from about 3 to about 70; x is a number in the range from about 2.5 to about 15.0 times the amount of y present; the mole ratio of reactants used to form the copolymer contains at least 50 mole percent of acrylic or methacrylic acid relative to the remaining constitutents of the copolymer; and, x, y and z are present in relative heterogeneous order.
Claim 3
Dependent Claim
16 words
The method of claim 1 wherein said process water is used in a steam generating system.
Claim 4
Dependent Claim
17 words
The method of claim 1 wherein said process water is used in a recirculating cooling water system.
Claim 5
Dependent Claim
16 words
The method of claim 1 wherein said process water is used in a gas scrubbing system.
Claim 6
Dependent Claim
20 words
The method of claim 1 wherein said process water stream is a brine circulated in a process for desalinating water.
Claim 7
Dependent Claim
22 words
The method of claim 1 wherein said process water stream is circulated in a process for recovering crude petroleum including hydrocarbon gases.
Claim 8
Dependent Claim
24 words
The method of claim 1 wherein X represents NH 4 , Na or K; R 1 and R 2 each represents H; and z=0.
Claim 9
Dependent Claim
65 words
The method of claim 7 wherein said copolymer is subjected to hydrolytic conditions prior to, or during use in said process water, so as to form a copolymer having the formula ##STR9## wherein, R 1 and R 2 each represent H; X represents Na; x, y, m and n have the same connotation as that given; p is a number less than y; and, y'=y-p.
Claim 10
Dependent Claim
41 words
The method of claim 8 wherein said water contains from about 2 ppm to about 20 ppm of said copolymer, n=0; p is in the range from 0.01 to about 0.5 when y is in the range from 0.5 to 0.99.
Claim 11
Dependent Claim
40 words
The method of claim 1 wherein z is greater than 0 and is represented by z' in the range from 0.1 to 1.0 in a copolymer having the structural formula ##STR10## wherein, y'=y-p, and z' is specified for each y.
Claim 12
Dependent Claim
16 words
The method of claim 10 wherein said process water is used in a steam generating system.
Claim 13
Dependent Claim
17 words
The method of claim 10 wherein said process water is used in a recirculating cooling water system.
Claim 14
Dependent Claim
16 words
The method of claim 10 wherein said process water is used in a gas scrubbing system.
Claim 15
Dependent Claim
22 words
The method of claim 10 wherein X represents NH 4 , Na or K; R 1 and R 2 each represents H.
Claim 16
Independent Claim
199 words
A method for inhibiting the deposition of scale due particularly to calcium phosphate formed in a system for pasteurizing milk, comprising, adding to said milk from 0.05 part per million (ppm) to about 10 ppm of a water-soluble essentially non-crosslinked random copolymer, optionally after said copolymer is subjected to hydrolytic conditions, said copolymer having the structural formula ##STR11## wherein, R 1 represents H, or methyl; R 2 represents H, methyl or ethyl; X is selected from the group consisting of H, NH 4 , an alkali metal, an alkali earth metal and zinc; n is either 0 or 1; X' is selected from NH 4 , an alkali metal, an alkaline earth metal and zinc; z is a number in the range from 0 to about 1.0; m is an integer in the range from about 3 to about 70; x is a number in the range from about 2.5 to about 15.0 times the amount of y present; the mole ratio of reactants used to form the copolymer contains at least 50 mole percent of acrylic or methacrylic acid relative to the remaining constitutents of the copolymer; and, x, y and z are present in relative heterogeneous order.
Claim 17
Independent Claim
199 words
A method for inhibiting the deposition of scale due particularly to calcium phosphate formed in a system for pasteurizing milk, comprising, adding to said milk from 0.05 part per million (ppm) to about 10 ppm of a water-soluble essentially non-crosslinked random copolymer, optionally after said copolymer is subjected to hydrolytic conditions, said copolymer having the structural formula ##STR11## wherein, R 1 represents H, or methyl; R 2 represents H, methyl or ethyl; X is selected from the group consisting of H, NH 4 , an alkali metal, an alkali earth metal and zinc; n is either 0 or 1; X' is selected from NH 4 , an alkali metal, an alkaline earth metal and zinc; z is a number in the range from 0 to about 1.0; m is an integer in the range from about 3 to about 70; x is a number in the range from about 2.5 to about 15.0 times the amount of y present; the mole ratio of reactants used to form the copolymer contains at least 50 mole percent of acrylic or methacrylic acid relative to the remaining constitutents of the copolymer; and, x, y and z are present in relative heterogeneous order.
Claim 18
Dependent Claim
40 words
The method of claim 15 wherein z is greater than 0 and is represented by z' in the range from 0.1 to 1.0 in a copolymer having the structural formula ##STR12## wherein, y'=y-p, and z' is specified for each y.
Claim 19
Independent Claim
207 words
A method for inhibiting the deposition of scale due particularly to calcium carbonate, calcium phosphate, calcium oxalate and magnesium silicate formed in a system for processing fruit juice, comprising, adding to said juice from 0.05 part per million (ppm) to about 10 ppm of a water-soluble essentially non-crosslinked random copolymer, optionally after said copolymer is subjected to hydrolytic conditions, said copolymer having the structural formula ##STR13## wherein, R 1 represents H, or methyl; R 2 represents H, methyl or ethyl; X is selected from the group consisting of H, NH 4 , an alkali metal, an alkaline earth metal and zinc; n is either 0 or 1; X' is selected from NH 4 , an alkali metal, an alkaline earth metal and zinc; z is a number in the range from 0 to about 1.0; m is an integer in the range from about 3 to about 70; x is a number in the range from about 2.5 to about 15.0 times the amount of y present; the mole ratio of reactants used to form the copolymer contains at least 50 mole percent of acrylic or methacrylic acid relative to the remaining constituents of the copolymer, and, x, y and z are present in relative heterogeneous order.
Claim 20
Independent Claim
207 words
A method for inhibiting the deposition of scale due particularly to calcium carbonate, calcium phosphate, calcium oxalate and magnesium silicate formed in a system for processing fruit juice, comprising, adding to said juice from 0.05 part per million (ppm) to about 10 ppm of a water-soluble essentially non-crosslinked random copolymer, optionally after said copolymer is subjected to hydrolytic conditions, said copolymer having the structural formula ##STR13## wherein, R 1 represents H, or methyl; R 2 represents H, methyl or ethyl; X is selected from the group consisting of H, NH 4 , an alkali metal, an alkaline earth metal and zinc; n is either 0 or 1; X' is selected from NH 4 , an alkali metal, an alkaline earth metal and zinc; z is a number in the range from 0 to about 1.0; m is an integer in the range from about 3 to about 70; x is a number in the range from about 2.5 to about 15.0 times the amount of y present; the mole ratio of reactants used to form the copolymer contains at least 50 mole percent of acrylic or methacrylic acid relative to the remaining constituents of the copolymer, and, x, y and z are present in relative heterogeneous order.
Claim 21
Dependent Claim
40 words
The method of claim 17 wherein z is greater than 0 and is represented by z' in the range from 0.1 to 1.0 in a copolymer having the structural formula ##STR14## wherein, y'=y-p, and z' is specified for each y.
References Cited (Backward Citations)
US2847308A
Cited
US3186849A
Cited
US3699048A
Cited
US3879288A
Cited
GB1414964A
Cited
US3856755A
Cited
DE2522637A1
Cited
US4029577A
Cited
US4389324A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-07-29 | 1989-01-28 | 1989-07-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-07-29 | 1993-01-28 | 1993-07-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-07-29 | 1997-01-28 | 1997-07-30 | $7700.00 | Window Closed / Lapsed |